CN103641452B - 一种环境友好型陶瓷材料及其制备方法 - Google Patents

一种环境友好型陶瓷材料及其制备方法 Download PDF

Info

Publication number
CN103641452B
CN103641452B CN201310618496.4A CN201310618496A CN103641452B CN 103641452 B CN103641452 B CN 103641452B CN 201310618496 A CN201310618496 A CN 201310618496A CN 103641452 B CN103641452 B CN 103641452B
Authority
CN
China
Prior art keywords
parts
softening agent
environment
stupalith
ceramic material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310618496.4A
Other languages
English (en)
Other versions
CN103641452A (zh
Inventor
吴洁新
谢培东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Aolitai Ceramic Industrial Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310618496.4A priority Critical patent/CN103641452B/zh
Publication of CN103641452A publication Critical patent/CN103641452A/zh
Application granted granted Critical
Publication of CN103641452B publication Critical patent/CN103641452B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及陶瓷材料技术领域，更具体地，涉及一种环境友好型陶瓷材料及其制备方法，该环境友好型陶瓷材料，按重量百分比包括以下组分：工业废弃物45~76份、增塑剂16~20份、润滑剂0.5~3份、改性剂0.8~8份、硅藻土6~11份以及增强纤维1.2~6份。本发明环境友好型陶瓷材料充分利用工业废弃物作为原料，并添加适当份数的增塑剂、润滑剂、改性剂、硅藻土和增强纤维，得到的陶瓷材料无毒无害，资源可以重复利用的同时，得到的陶瓷材料环保，适于日用陶瓷或建筑用陶瓷等的应用。

Description

一种环境友好型陶瓷材料及其制备方法
技术领域
本发明涉及陶瓷材料技术领域，更具体地，涉及一种改进陶瓷材料及其制备方法。
背景技术
随着人们生活水平的不断提高，环境与健康的意识正在逐步增强，绿色材料及环保产品将日益被人们所关注。健康、长寿、舒适已经成为现代人追求的最高目标。抗菌、保健、环保制品应运而生，并获得迅速发展。而陶瓷制品无论作为日用陶瓷还是作为家居、装饰等建筑用陶瓷，都与人们的日常生活息息相关，所以人们对各类陶瓷制品的卫生保健功能也提出了更高的要求。
发明内容
本发明为克服上述现有技术所述的至少一种缺陷，提供一种利用工业废弃物制造的环境友好型陶瓷材料。
为解决上述技术问题，本发明采用的技术方案是：
提供一种环境友好型陶瓷材料，按重量百分比包括以下组分：工业废弃物45~76份、增塑剂16~20份、润滑剂0.5~3份、改性剂0.8~8份、硅藻土6~11份、增强纤维1.2~6份以及云母粉0.3~3份。
优选地，按重量百分比包括以下组分：工业废弃物61份、增塑剂18份、润滑剂2份、改性剂5份、硅藻土8份、增强纤维3份、云母粉1。
可选地，所述工业废料为废淤泥、废陶瓷碎片或焚烧灰渣。
可选地，所述改性剂为碳化硅或氧化硅。
可选地，所述增强纤维为羟乙基纤维素、陶瓷纤维或氧化铝纤维。
优选地，所述增塑剂为无毒性增塑剂。
本发明还提供一种如上述任一环境友好型陶瓷材料的制备方法，包括以下步骤：
S1.分别按重量份数球磨以下组分：工业废弃物45~76份、增塑剂16~20份、润滑剂0.5~3份、改性剂0.8~8份、硅藻土6~11份以及增强纤维1.2~6份；
S2.将上述组分混合搅拌后，添加云母粉0.3~3份并制成浆料；
S3.将所述浆料烧结成型。
其中，所述球磨时间为26~30小时，搅拌时间为10~20分钟；烧结时间为3~5小时，烧结温度为1100~1250℃。
与现有技术相比，本发明的有益效果是：
本发明环保陶瓷材料充分利用工业废弃物作为原料，并添加适当份数的增塑剂、润滑剂、改性剂、硅藻土和增强纤维，得到的陶瓷材料无毒无害，资源可以重复利用的同时，得到的陶瓷材料环保，适于日用陶瓷或建筑用陶瓷等的应用。
具体实施方式
下面结合具体实施方式对本发明作进一步的说明。
实施例1
选取废淤泥61份、无毒性增塑剂18份、润滑剂2份、碳化硅5份、硅藻土8份和羟乙基纤维素3份；破碎混合，球磨26小时并混合搅拌15分钟；添加云母粉1份继续混合搅拌并制成浆料；将浆料在1200℃的环境下烧结4小时。
制得的陶瓷材料成品经测试，无损坏现象，无味、无毒。
实施例2
选取废陶瓷碎片45份、无毒性增塑剂20份、润滑剂3份、碳化硅8份、硅藻土11份和羟乙基纤维素6份；破碎混合，球磨26小时并混合搅拌20分钟；添加云母粉0.3份，余量为稀土氧化物或其他不可避免的杂质继续混合搅拌并制成浆料；将浆料在1100℃的环境下烧结4小时。
制得的陶瓷材料成品经测试，无损坏现象，无味、无毒。
实施例3
选取废淤泥76份、增塑剂16份、润滑剂0.5份、碳化硅0.8份、硅藻土6份和陶瓷纤维1.2份；破碎混合，球磨30小时并混合搅拌10分钟；添加云母粉3份以及阻燃剂3份，余量为稀土氧化物或其他不可避免的杂质继续混合搅拌并制成浆料；将浆料在1100℃的环境下烧结3小时。
制得的陶瓷材料成品经测试，无损坏现象，无味、无毒。
显然，本发明的上述实施例仅仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明权利要求的保护范围之内。

Claims (5)

1.一种改进陶瓷材料，其特征在于，按重量份数包括以下组分：工业废弃物61份、增塑剂18份、润滑剂2份、改性剂5份、硅藻土8份、增强纤维3份、云母粉1份，所述工业废弃物为废淤泥、废陶瓷碎片或焚烧灰渣，所述增强纤维为羟乙基纤维素或陶瓷纤维。
2.根据权利要求1所述的改进陶瓷材料，其特征在于，所述增塑剂为无毒性增塑剂。
3.一种如权利要求1至2任一项所述改进陶瓷材料的制备方法，其特征在于，包括以下步骤：
分别按重量份数球磨以下组分：工业废弃物61份、增塑剂18份、润滑剂2份、改性剂5份、硅藻土8份、增强纤维3份；
将上述组分混合搅拌后，添加云母粉1份并制成浆料；
将所述浆料烧结成型。
4.根据权利要求3所述的制备方法，其特征在于，所述球磨时间为26~30小时，搅拌时间为10~20分钟。
5.根据权利要求4所述的制备方法，其特征在于，所述烧结时间为3~5小时，烧结温度为1100~1250℃。
CN201310618496.4A 2013-11-29 2013-11-29 一种环境友好型陶瓷材料及其制备方法 Active CN103641452B (zh)