CN103641450A - 一种陶瓷材料及其制备方法 - Google Patents

一种陶瓷材料及其制备方法 Download PDF

Info

Publication number
CN103641450A
CN103641450A CN201310618483.7A CN201310618483A CN103641450A CN 103641450 A CN103641450 A CN 103641450A CN 201310618483 A CN201310618483 A CN 201310618483A CN 103641450 A CN103641450 A CN 103641450A
Authority
CN
China
Prior art keywords
parts
stupalith
softening agent
properties
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310618483.7A
Other languages
English (en)
Inventor
唐海秋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310618483.7A priority Critical patent/CN103641450A/zh
Publication of CN103641450A publication Critical patent/CN103641450A/zh
Pending legal-status Critical Current

Abstract

本发明涉及陶瓷材料技术领域，更具体地，涉及一种陶瓷材料及其制备方法，该陶瓷材料，按重量百分比包括以下组分：工业废弃物45~76份、增塑剂16~20份、润滑剂0.5~3份、改性剂0.8~8份、硅藻土6~11份以及增强纤维1.2~6份。本发明陶瓷材料充分利用工业废弃物作为原料，并添加适当份数的增塑剂、润滑剂、改性剂、硅藻土和增强纤维，得到的陶瓷材料无毒无害，资源可以重复利用的同时，得到的陶瓷材料环保，适于日用陶瓷或建筑用陶瓷等的应用。

Description

一种陶瓷材料及其制备方法
技术领域
 本发明涉及陶瓷材料技术领域，更具体地，涉及一种陶瓷材料及其制备方法。
背景技术
随着国内外对污泥处理思路的转变，现已逐步统一到污泥干化焚烧的技术思路上来。对于污泥焚烧后形成的固体废弃物，焚烧灰渣应该如何进行处置，一直处于争论的状态。同时，对各种大中小型热电厂产生的粉煤灰的出路一直没有得到有效的解决。各类陶瓷工厂的废碎料片，砖瓦厂的肥料随意堆弃权，倾倒对环境造成严重破坏。
发明内容
本发明为克服上述现有技术所述的至少一种缺陷，提供一种利用工业废弃物制造的陶瓷材料。
为解决上述技术问题，本发明采用的技术方案是：
提供一种陶瓷材料，按重量百分比包括以下组分：工业废弃物45~76份、增塑剂8~11份、润滑剂0.5~3份、改性剂6~7份、硅藻土12~13份、增强纤维11~15份、云母粉0.3~1份、阻燃剂1~1.5份。
按重量百分比包括以下组分：工业废弃物61份、增塑剂9份、润滑剂2份、改性剂6.5份、硅藻土12份、增强纤维11份、云母粉1份以及阻燃剂1份。
所述工业废料为废淤泥、废陶瓷碎片或焚烧灰渣。
所述改性剂为碳化硅或氧化硅。
所述增强纤维为羟乙基纤维素、陶瓷纤维或氧化铝纤维。
所述增塑剂为无毒性增塑剂。
本发明还提供一种陶瓷材料的制备方法，其包括以下步骤：
分别按重量份数球磨以下组分：工业废弃物45~76份、增塑剂8~11份、润滑剂0.5~3份、改性剂6~7份、硅藻土12~13份以及增强纤维11~15份；
将上述组分混合搅拌后，添加云母粉0.3~3份和阻燃剂1~1.5份并制成浆料；
将所述浆料烧结成型。
所述球磨时间为20~24小时，搅拌时间为10~20分钟。
所述烧结时间为5~6小时，烧结温度为1000~1150℃。
与现有技术相比，本发明的有益效果是：
本发明陶瓷材料充分利用工业废弃物作为原料，并添加适当份数的增塑剂、润滑剂、改性剂、硅藻土和增强纤维，得到的陶瓷材料无毒无害，资源可以重复利用的同时，得到的陶瓷材料环保，适于日用陶瓷或建筑用陶瓷等的应用。
具体实施方式
下面结合具体实施方式对本发明作进一步的说明。
实施例1
选取废淤泥61份、无毒性增塑剂11份、润滑剂2份、碳化硅6份、硅藻土12份和羟乙基纤维素11份；破碎混合，球磨22小时并混合搅拌15分钟；添加云母粉1份以及阻燃剂1.5份继续混合搅拌并制成浆料；将浆料在1100℃的环境下烧结5.5小时。
制得的陶瓷材料成品经测试，无损坏现象，无味、无毒。
实施例2
选取废陶瓷碎片45份、无毒性增塑剂10份、润滑剂3份、碳化硅7份、硅藻土13份和羟乙基纤维素15份；破碎混合，球磨24小时并混合搅拌20分钟；添加云母粉0.3份以及阻燃剂1.5份，余量为稀土氧化物或其他不可避免的杂质继续混合搅拌并制成浆料；将浆料在1100℃的环境下烧结5小时。
制得的陶瓷材料成品经测试，无损坏现象，无味、无毒。
显然，本发明的上述实施例仅仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明权利要求的保护范围之内。

Claims (9)

1.一种陶瓷材料，其特征在于，按重量百分比包括以下组分：工业废弃物45~76份、增塑剂8~11份、润滑剂0.5~3份、改性剂6~7份、硅藻土12~13份、增强纤维11~15份、云母粉0.3~1份、阻燃剂1~1.5份。
2.根据权利要求1所述的陶瓷材料，其特征在于，按重量百分比包括以下组分：工业废弃物61份、增塑剂9份、润滑剂2份、改性剂6.5份、硅藻土12份、增强纤维11份、云母粉1份以及阻燃剂1份。
3.根据权利要求1至2任一项所述的陶瓷材料，其特征在于，所述工业废料为废淤泥、废陶瓷碎片或焚烧灰渣。
4.根据权利要求1至2任一项所述的陶瓷材料，其特征在于，所述改性剂为碳化硅或氧化硅。
5.根据权利要求1至3任一项所述的陶瓷材料，其特征在于，所述增强纤维为羟乙基纤维素、陶瓷纤维或氧化铝纤维。
6.根据权利要求1至3任一项所述的陶瓷材料，其特征在于，所述增塑剂为无毒性增塑剂。
7.一种如权利要求1至6任一项所述陶瓷材料的制备方法，其特征在于，包括以下步骤：
分别按重量份数球磨以下组分：工业废弃物45~76份、增塑剂8~11份、润滑剂0.5~3份、改性剂6~7份、硅藻土12~13份以及增强纤维11~15份；
将上述组分混合搅拌后，添加云母粉0.3~3份和阻燃剂1~1.5份并制成浆料；
将所述浆料烧结成型。
8.根据权利要求7所述的制备方法，其特征在于，所述球磨时间为20~24小时，搅拌时间为10~20分钟。
9.根据权利要求7所述的制备方法，其特征在于，所述烧结时间为5~6小时，烧结温度为1000~1150℃。
CN201310618483.7A 2013-11-29 2013-11-29 一种陶瓷材料及其制备方法 Pending CN103641450A (zh)