CN103641293A - Preparation technology of toughened glass - Google Patents
Preparation technology of toughened glass Download PDFInfo
- Publication number
- CN103641293A CN103641293A CN201310609132.XA CN201310609132A CN103641293A CN 103641293 A CN103641293 A CN 103641293A CN 201310609132 A CN201310609132 A CN 201310609132A CN 103641293 A CN103641293 A CN 103641293A
- Authority
- CN
- China
- Prior art keywords
- glass
- temperature
- mass parts
- parts
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation technology of toughened glass. The preparation technology comprises the following steps: (1) polishing, cleaning and drying glass; (2) pre-heating the dried glass for 4 to 5 hours at a temperature of 300 to 310 DEG C; (3) adding following components in parts by weight into a toughening treatment tank: 3 to 5 parts of barium oxide, 10 to 15 parts of potassium silicate, 11 to 12 parts of silicon dioxide, 15 to 20 parts of potassium permanganate, and 300 parts of sylvite; (4) putting the pre-heated glass into the toughening treatment tank, allowing the glass to stand still for 13 to 14 hours, controlling the temperature in a range of 480 to 490 DEG C; (5) putting the toughened glass into a heat dissipation furnace with a temperature of 300 to 310 DEG C, taking out the glass when the temperature decreases to 40 DEG C, then putting the glass into hot water with a temperature of 80 DEG C, and allowing the glass to stand still for 2 to 3 hours so as to obtain the finished product. The preparation technology of toughened glass can reduce the toughening time, and thickens the surface compressive stress layer.
Description
Technical field
The present invention relates to the preparation technology of toughened glass.
Background technology
The preparation technology of current toughened glass, the tempering time is long, and makes bearing stress layer thinner.
Summary of the invention
The object of the present invention is to provide a kind of preparation technology of toughened glass, it reduces the tempering time, and makes the thickening of bearing stress layer.
For achieving the above object, technical scheme of the present invention is the preparation technology of a kind of toughened glass of design, comprises the steps:
1) by glass polishing, cleaning, dry;
2) by dried glass at 300-310 ℃ of preheating 4-5 hour;
3) 3-5 mass parts barium oxide, 10-15 mass parts potassium silicate, 11-12 mass parts silicon-dioxide, 15-20 mass parts potassium permanganate, 300 mass parts sylvite are joined in tempering treatment trough;
4) glass of preheating is put into the standing 13-14 hour of tempering treatment trough, solution temperature is controlled at 480-490 ℃;
5) glass after tempering being put into temperature is the heat radiation stove of 300-310 ℃, when temperature is down to 40 ℃, glass is taken out and put into 80 ℃ of standing 2-3 hour of hot water, takes out.
Advantage of the present invention and beneficial effect are: a kind of preparation technology of toughened glass is provided, and it reduces the tempering time, and make the thickening of bearing stress layer.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A preparation technology for toughened glass, comprises the steps:
1) by glass polishing, cleaning, dry;
2) by dried glass 300 ℃ of preheatings 4 hours;
3) 3 mass parts barium oxide, 10 mass parts potassium silicates, 11 mass parts silicon-dioxide, 15 mass parts potassium permanganate, 300 mass parts sylvite are joined in tempering treatment trough;
4) glass of preheating is put into tempering treatment trough standing 13 hours, solution temperature is controlled at 480 ℃;
5) glass after tempering being put into temperature is the heat radiation stove of 300 ℃, when temperature is down to 40 ℃, glass is taken out and put into 80 ℃ of hot water standing 2 hours, takes out.
Embodiment 2
A preparation technology for toughened glass, comprises the steps:
1) by glass polishing, cleaning, dry;
2) by dried glass 310 ℃ of preheatings 5 hours;
3) 5 mass parts barium oxide, 15 mass parts potassium silicates, 12 mass parts silicon-dioxide, 20 mass parts potassium permanganate, 300 mass parts sylvite are joined in tempering treatment trough;
4) glass of preheating is put into tempering treatment trough standing 14 hours, solution temperature is controlled at 490 ℃;
5) glass after tempering being put into temperature is the heat radiation stove of 310 ℃, when temperature is down to 40 ℃, glass is taken out and put into 80 ℃ of hot water standing 3 hours, takes out.
Embodiment 3
A preparation technology for toughened glass, comprises the steps:
1) by glass polishing, cleaning, dry;
2) by dried glass 308 ℃ of preheatings 4.5 hours;
3) 4 mass parts barium oxide, 12 mass parts potassium silicates, 11.5 mass parts silicon-dioxide, 18 mass parts potassium permanganate, 300 mass parts sylvite are joined in tempering treatment trough;
4) glass of preheating is put into tempering treatment trough standing 13.5 hours, solution temperature is controlled at 485 ℃;
5) glass after tempering being put into temperature is the heat radiation stove of 305 ℃, when temperature is down to 40 ℃, glass is taken out and put into 80 ℃ of standing 2-3 hour of hot water, takes out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the preparation technology of toughened glass, is characterized in that, comprises the steps:
1) by glass polishing, cleaning, dry;
2) by dried glass at 300-310 ℃ of preheating 4-5 hour;
3) 3-5 mass parts barium oxide, 10-15 mass parts potassium silicate, 11-12 mass parts silicon-dioxide, 15-20 mass parts potassium permanganate, 300 mass parts sylvite are joined in tempering treatment trough;
4) glass of preheating is put into the standing 13-14 hour of tempering treatment trough, solution temperature is controlled at 480-490 ℃;
5) glass after tempering being put into temperature is the heat radiation stove of 300-310 ℃, when temperature is down to 40 ℃, glass is taken out and put into 80 ℃ of standing 2-3 hour of hot water, takes out.