CN102910806A - Preparation process of toughened glass - Google Patents
Preparation process of toughened glass Download PDFInfo
- Publication number
- CN102910806A CN102910806A CN201110225920XA CN201110225920A CN102910806A CN 102910806 A CN102910806 A CN 102910806A CN 201110225920X A CN201110225920X A CN 201110225920XA CN 201110225920 A CN201110225920 A CN 201110225920A CN 102910806 A CN102910806 A CN 102910806A
- Authority
- CN
- China
- Prior art keywords
- glass
- sylvite
- catalyzer
- toughened glass
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation process of a toughened glass. The formula of a catalyst adopted by the process comprises the following materials in percentage by weight: 12-14 % of barium oxide, 50-60 % of potassium silicate, 12-14 % of silicon dioxide and 14-20 % of potassium hypermanganate. Through the adding of the catalyst, the toughening time can be reduced, a surface pressure layer of the toughened glass is thickened and the toughening strength is enhanced.
Description
[technical field]
The invention belongs to the glass preparation field, be specifically related to the preparation technology of toughened glass.
[technical background]
The mode of glass tempering has physical toughened and chemical tempering at present, and chemically toughened glass intensity and physical toughened glass approach, Heat stability is good, treatment temp is low, and product is not yielding, and its product is not subjected to the restriction of thickness and geometrical shape, use equipment is simple, and product is easily realized.But with physical toughened glassy phase ratio, the chemically toughened glass production cycle long (reach tens of hours swap time), efficient is low and production cost is high.
The principle of chemical enhancement method is: the surface composition that changes glass according to the mechanism of ion diffusion, at a certain temperature glass is immersed in the high-temperature molten salt, mutual exchange occurs because of diffusion in the alkalimetal ion in the glass and the alkalimetal ion in the fused salt, produce " jammed " phenomenon, make glass surface produce stress under compression, thereby improve the intensity of glass.But the bearing stress layer that ion exchange method produces is thinner, and the effects on surface microdefect is very responsive, and very little surface tear just is enough to make strength of glass to reduce.Ba
2+Diameter less than K
+, more be conducive to entering of ion, the surface pressure layer is thickened.
Purpose of the present invention is exactly in order to overcome the shortcomings such as long and bearing stress layer of tempering time that above-mentioned prior art exists is thinner, a kind of new catalyst and preparation technology to be provided.
[summary of the invention]
The object of the invention is, a kind of preparation method of new toughened glass is provided.
The present invention adopts following technical scheme to realize:
A kind of catalyzer: it is characterized in that being (weight ratio):
Barium oxide: 12-14%
Potassium silicate: 50-60%
Silicon-dioxide: 12-14%
Potassium permanganate: 14-20%
The preparation technology of toughened glass: 1. with glass cutting, sliver, polishing, put into pallet 4 cleanings, drying; 2. with the glass 3 of drying at 150-260 ℃ of preheating 30-90min; 3. configure catalyzer, it is joined in the sylvite 1 of tempering treatment trough 2, the adding weight of catalyzer is the 0.1-6% of sylvite; 4. the glass of preheating is put into the sylvite bath 1 that 3. configures and left standstill 4-10h, solution temperature is controlled at 350-450 ℃; 5. the glass behind the tempering is put into temperature and be 150-260 ℃ heat radiation stove, when temperature is down to 60 ℃, glass is taken out then put into 70 ℃ of hot water, 10-20min takes out and gets final product.
[description of drawings]
Fig. 1 is tempering schematic diagram of the present invention.
[embodiment]
The present invention will be further described below in conjunction with specific embodiment.Need to prove, following embodiment only is used for explanation the present invention, is not limited to practical range of the present invention.
1 couple of the present invention is described in further detail below in conjunction with accompanying drawing.
A kind of catalyzer: it is characterized in that being (weight ratio):
Barium oxide: 12-14%
Potassium silicate: 50-60%
Silicon-dioxide: 12-14%
Potassium permanganate: 14-20%
The preparation technology of toughened glass: 1. with glass cutting, sliver, polishing, put into pallet 4 cleanings, drying; 2. with the glass 3 of drying at 150-260 ℃ of preheating 30-90min; 3. configure catalyzer, it is joined in the sylvite 1 of tempering treatment trough 2, the adding weight of catalyzer is the 0.1-6% of sylvite; 4. the glass of preheating is put into the sylvite bath 1 that 3. configures and left standstill 4-10h, solution temperature is controlled at 350-450 ℃; 5. the glass behind the tempering is put into temperature and be 150-260 ℃ heat radiation stove, when temperature is down to 60 ℃, glass is taken out then put into 70 ℃ of hot water, 10-20min takes out and gets final product.
Claims (2)
1. catalyzer: it is characterized in that being (weight ratio):
Barium oxide: 12-14%
Potassium silicate: 50-60%
Silicon-dioxide: 12-14%
Potassium permanganate: 14-20%.
2. the preparation technology of toughened glass is characterized in that: 1. with glass cutting, sliver, polishing, put into pallet 4 cleanings, drying; 2. with the glass 3 of drying at 150-260 ℃ of preheating 30-90min; 3. according to configuring catalyzer in the claim 1, it is joined in the sylvite 1 of tempering treatment trough 2, the adding weight of catalyzer is the 0.1-6% of sylvite; 4. the glass of preheating is put into the sylvite 1 that 3. configures and left standstill 4-10h, solution temperature is controlled at 350-450 ℃; 5. the glass behind the tempering is put into temperature and be 150-260 ℃ heat radiation stove, when temperature is down to 60 ℃, glass is taken out then put into 70 ℃ of hot water, 10-20min takes out and gets final product.