CN106916979A - A kind of preparation method of metal foil - Google Patents
A kind of preparation method of metal foil Download PDFInfo
- Publication number
- CN106916979A CN106916979A CN201710249055.XA CN201710249055A CN106916979A CN 106916979 A CN106916979 A CN 106916979A CN 201710249055 A CN201710249055 A CN 201710249055A CN 106916979 A CN106916979 A CN 106916979A
- Authority
- CN
- China
- Prior art keywords
- metal foil
- preparation
- metal
- vacuum
- metal material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to provide a kind of preparation method of metal foil, including S01, by the washing of metal material base base substrate, drying；S02, metal material base base substrate is thermally formed slurries in being put into reduction furnace, be warmed up to 600 DEG C~1200 DEG C；S03, the slurries are poured into mould in vacuum or helium atmosphere in hot forming, and anneal 2 hours；S04, metal foil is taken out from container and pickling, then dried in the shade under vacuum normal temperature；S05, the joint face to metal foil cut into after frosted treatment the list structure of 150 300mm.Of the present invention is a kind of preparation method of metal foil, makes metal freezing more uniform by making metal material and can improve in vacuum or helium atmosphere, while reducing the production cost of metal material, is increased economic efficiency, and improves product quality.
Description
Technical field
The present invention relates to a kind of preparation method of metal foil.
Background technology
In actual life, metal material is generally all made up of 100% metal ingredient, the product that this metalloid material is made
It has been commercially available and has been widely applied and promotes.But but it is highly susceptible to the influence of extraneous factor and corrosion occurs, and
The use demand of people is often unable to reach in some specific environment, such as in summer metal material due to being influenceed by weather,
Often decrease, and the metal foil often skewness in process of setting, so as to trigger the hair of various fortuitous events
It is raw.Therefore it provides a kind of preparation method of metal foil turns into those skilled in the art's problem demanding prompt solution.
The content of the invention
Regarding to the issue above, the main object of the present invention is to provide and a kind of solidifies the uniform, metal foil of low production cost
Preparation method.
The present invention is achieved by the following technical solutions：A kind of preparation method of metal foil is provided, including：
S01, by metal material base base substrate washing, drying；
S02, metal material base base substrate is thermally formed slurries in being put into reduction furnace, be warmed up to 600 DEG C~1200 DEG C；
S03, the slurries are poured into mould in vacuum or helium atmosphere in hot forming, and anneal 2 hours；
S04, metal foil is taken out from container and pickling, then dried in the shade under vacuum normal temperature；
S05, the joint face to metal foil cut into after frosted treatment the list structure of 150-300mm.
Preferably, the time for heating the metal material matrix is 1h~1.5h.
Preferably, the temperature in the slurries being poured into mould in vacuum or helium atmosphere is 800 DEG C~1000
℃。
Preferably, the pressure in the slurries being poured into mould in vacuum or helium atmosphere is 1MPa~10MPa.
Preferably, in S03, hot formed product thickness is 0.8~20mm.
Preferably, in S05, the product thickness after frosted treatment is 0.8~10mm.
Preferably, in S04, the metal foil carries out pickling using HF.
Preferably, pickling time is 15~30min.
Of the present invention is a kind of preparation method of metal foil, by make metal material in vacuum or helium atmosphere can
Make metal freezing more uniform to improve, while reducing the production cost of metal material, increase economic efficiency, improve product product
Matter.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, those skilled in the art can be by this specification institute
The content of exposure understands other advantages of the invention and effect easily.The present invention can also be by specific implementations different in addition
Mode is embodied or practiced, and the various details in this specification can also be based on different viewpoints and application, without departing from this
Various modifications or alterations are carried out under the spirit of invention.
Embodiment one
The present invention is achieved by the following technical solutions：A kind of preparation method of metal foil is provided, including：
S01, by metal material base base substrate washing, drying.
S02, metal material base base substrate is thermally formed slurries in being put into reduction furnace, be warmed up to 600 DEG C, heat metal material
The time for expecting matrix is 1h.
S03, the slurries are poured into the mould that temperature is 800 DEG C in vacuum or helium atmosphere in hot forming, heat into
The product thickness of shape is 0.8mm, and is annealed 2 hours, and the pressure during slurries are poured into mould in vacuum or helium atmosphere is
1MPa。
S04, metal foil is taken out from container and HF pickling, then dried in the shade under vacuum normal temperature, pickling time is
15min。
S05, the joint face to metal foil cut into after frosted treatment the list structure of 150mm, after frosted treatment
Product thickness is 0.8mm.
Embodiment two
The present invention is achieved by the following technical solutions：A kind of preparation method of metal foil is provided, including：
S01, by metal material base base substrate washing, drying.
S02, metal material base base substrate is thermally formed slurries in being put into reduction furnace, be warmed up to 1200 DEG C, heat metal
The time of material matrix is 1.5h.
S03, the slurries are poured into the mould that temperature is 1000 DEG C in vacuum or helium atmosphere in hot forming, heat into
The product thickness of shape is 20mm, and is annealed 2 hours, the pressure during the slurries are poured into mould in vacuum or helium atmosphere
It is 10MPa.
S04, metal foil is taken out from container and HF pickling, then dried in the shade under vacuum normal temperature, pickling time is
30min。
S05, the joint face to metal foil cut into after frosted treatment the list structure of 300mm, after frosted treatment
Product thickness is 10mm.
In sum, of the present invention is a kind of preparation method of metal foil, is made by vacuum or helium atmosphere
Metal material can be improved makes metal freezing more uniform, while reducing the production cost of metal material, increases economic efficiency, and carries
High product quality.
Described above has shown and described some preferred embodiments of the invention, but as previously described, it should be understood that the present invention
Be not limited to form disclosed herein, be not to be taken as the exclusion to other embodiment, and can be used for various other combinations,
Modification and environment, and can be in invention contemplated scope described herein, by above-mentioned teaching or the technology or knowledge of association area
It is modified.And the change and change that those skilled in the art are carried out do not depart from the spirit and scope of the present invention, then all should be in this hair
In the protection domain of bright appended claims.
Claims (8)
1. a kind of preparation method of metal foil, it is characterised in that including：
S01, by metal material base base substrate washing, drying；
S02, metal material base base substrate is thermally formed slurries in being put into reduction furnace, be warmed up to 600 DEG C~1200 DEG C；
S03, the slurries are poured into mould in vacuum or helium atmosphere in hot forming, and anneal 2 hours；
S04, metal foil is taken out from container and pickling, then dried in the shade under vacuum normal temperature；
S05, the joint face to metal foil cut into after frosted treatment the list structure of 150-300mm.
2. the preparation method of metal foil as claimed in claim 1, it is characterised in that the time of the heating metal material matrix
It is 1h~1.5h.
3. the preparation method of metal foil as claimed in claim 1, it is characterised in that by the slurry in vacuum or helium atmosphere
The temperature that liquid pours into mould is 800 DEG C~1000 DEG C.
4. the preparation method of metal foil as claimed in claim 1, it is characterised in that by the slurry in vacuum or helium atmosphere
The pressure that liquid pours into mould is 1MPa~10MPa.
5. the preparation method of metal foil as claimed in claim 1, it is characterised in that in S03, hot formed product thickness is
0.8~20mm.
6. the preparation method of metal foil as claimed in claim 1, it is characterised in that in S05, the product after frosted treatment is thick
It is 0.8~10mm to spend.
7. the preparation method of metal foil as claimed in claim 1, it is characterised in that in S04, the metal foil is entered using HF
Row pickling.
8. the preparation method of metal foil as claimed in claim 7, it is characterised in that pickling time is 15~30min.