CN103640786A - 一种耐高温的复合包装材料 - Google Patents
一种耐高温的复合包装材料 Download PDFInfo
- Publication number
- CN103640786A CN103640786A CN201310614527.9A CN201310614527A CN103640786A CN 103640786 A CN103640786 A CN 103640786A CN 201310614527 A CN201310614527 A CN 201310614527A CN 103640786 A CN103640786 A CN 103640786A
- Authority
- CN
- China
- Prior art keywords
- microns
- thickness
- package material
- film
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温的复合包装材料,耐高温的复合包装材料为四层,第一层为厚度60微米~130微米的低密度聚乙烯薄膜、第二层为厚度70微米~100微米的聚甲醛树脂薄膜、第三层为厚度80微米~110微米聚异丁烯薄膜、第四层为厚度90微米~140微米的聚甲基丙烯薄膜。复合包装材料具有良好的耐高温性能,在90℃下水中蒸煮50min~70min无破损现象。
Description
技术领域
本发明涉及一种复合包装材料,特别是涉及一种耐高温的复合包装材料。
背景技术
包装材料应用范围较广,可以用于包装食品、化工产品、器械等。包装材料的性能对包装材料的使用空间有较大的影响,如果包装材料的性能较差,在使用中容易发生破损等现象。通过将不同材料进行复合,获得的复合包装材料可以具备良好的性能。耐高温性能也是考察包装材料性能的一个重要指标。耐高温性能较差,会降低包装的耐高温效果,影响产品的使用。
发明内容
要解决的技术问题:常规的复合包装材料耐高温效果差的问题。
技术方案:本发明公开了一种耐高温的复合包装材料,耐高温的复合包装材料为四层,第一层为厚度60微米~130微米的低密度聚乙烯薄膜、第二层为厚度70微米~100微米的聚甲醛树脂薄膜、第三层为厚度80微米~110微米的聚异丁烯薄膜、第四层为厚度90微米~140微米的聚甲基丙烯薄膜。复合的包装材料通过多台挤出机共同挤压复合的方式来得到耐高温的复合的包装材料。
复合包装材料中低密度聚乙烯薄膜的厚度优选为60微米。
复合包装材料中聚甲醛树脂薄膜的厚度优选为100微米。
复合包装材料中聚异丁烯薄膜的厚度优选为110微米。
复合包装材料中聚甲基丙烯薄膜的厚度优选为140微米。
有益效果:得到的耐高温复合包装材料具有良好的耐高温效果,在90℃下水中蒸煮50min~70min无破损现象。可以大量使用在物品的包装用途中。
附图说明
图1为耐高温的复合包装材料的示意图,1为低密度聚乙烯薄膜、2为聚甲醛树脂薄膜、3为聚异丁烯薄膜、4为聚甲基丙烯薄膜。
具体实施方式
实施例1
一种耐高温的复合包装材料,耐高温的复合包装材料为四层,第一层为厚度60微米的低密度聚乙烯薄膜1、第二层为厚度70微米的聚甲醛树脂薄膜2、第三层为厚度110微米的聚异丁烯薄膜3、第四层为厚度90微米的聚甲基丙烯薄膜4。复合的包装材料通过多台挤出机共同挤压复合的方式来得到耐高温的复合的包装材料。
实施例2
一种耐高温的复合包装材料,耐高温的复合包装材料为四层,第一层为厚度100微米的低密度聚乙烯薄膜1、第二层为厚度80微米的聚甲醛树脂薄膜2、第三层为厚度100微米的聚异丁烯薄膜3、第四层为厚度120微米的聚甲基丙烯薄膜4。复合的包装材料通过多台挤出机共同挤压复合的方式来得到耐高温的复合的包装材料。
实施例3
一种耐高温的复合包装材料,耐高温的复合包装材料为四层,第一层为厚度130微米的低密度聚乙烯薄膜1、第二层为厚度100微米的聚甲醛树脂薄膜2、第三层为厚度80微米的聚异丁烯薄膜3、第四层为厚度140微米的聚甲基丙烯薄膜4。复合的包装材料通过多台挤出机共同挤压复合的方式来得到耐高温的复合的包装材料。
测定了实施例1、实施例2、实施例3的耐高温效果,将实施例1、实施例2、实施例3在90℃下水中蒸煮50min、60min、70min。蒸煮结束后,实施例1、实施例2、实施例3的复合包装材料均未发生变化。具备了良好的耐高温的效果,可以用于产品的包装用途中。
Claims (5)
1.一种耐高温的复合包装材料,其特征在于耐高温的复合包装材料为四层,第一层为厚度60微米~130微米的低密度聚乙烯薄膜(1)、第二层为厚度70微米~100微米的聚甲醛树脂薄膜(2)、第三层为厚度80微米~110微米聚异丁烯薄膜(3)、第四层为厚度90微米~140微米的聚甲基丙烯薄膜(4)。
2.根据权利要求1所述的一种耐高温的复合包装材料,其特征在于复合包装材料中低密度聚乙烯薄膜(1)的厚度为60微米。
3.根据权利要求1所述的一种耐高温的复合包装材料,其特征在于复合包装材料中聚甲醛树脂薄膜(2)的厚度为100微米。
4.根据权利要求1所述的一种耐高温的复合包装材料,其特征在于复合包装材料中聚异丁烯薄膜(3)的厚度为110微米。
5.根据权利要求1所述的一种耐高温的复合包装材料,其特征在于复合包装材料中聚甲基丙烯薄膜(4)的厚度为140微米。