CN103627294A - Heavy anti-corrosion paint made of epoxy resin and basalt scales - Google Patents
Heavy anti-corrosion paint made of epoxy resin and basalt scales Download PDFInfo
- Publication number
- CN103627294A CN103627294A CN201210302809.0A CN201210302809A CN103627294A CN 103627294 A CN103627294 A CN 103627294A CN 201210302809 A CN201210302809 A CN 201210302809A CN 103627294 A CN103627294 A CN 103627294A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight parts
- component
- basalt
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heavy anti-corrosion paint made of epoxy resin and basalt scales. The paint comprises a component A and a component B, and is characterized in that: the component A comprises the following components in parts by weight: 20 to 40 parts of epoxy resin, 25 to 38 parts of dibutyl phthalate, 15 to 35 parts of dispersant, 20 to 40 parts of antifoaming agent, 20 to 39 parts of levelling agent, 10 to 25 parts of pigment zinc phosphate, and 12 to 78 parts of basalt scales; and the component B comprises the following components in parts by weight: 20 to 40 parts of polyamide and 25 to 40 parts of solvent. Basalt scales are adopted as the filling material, because of the labyrinth effect of the basalt scales, penetration of corrosive mediums is effectively prevented, the penetration rate is reduced by 8 to 9 times, and the paint has the advantages of high adhesive force, corrosion resistance, good penetration resistant property, low coating contracting rate, small thermo-expanding coefficient, low curing residual stress, wear resistance, simpleness for construction, and easy repairing.
Description
Technical field
The present invention relates to a kind of protective system, particularly a kind of heavy anticorrosion epoxy basalt flake anticorrosive paint.
Background technology
Protective system is widely used in the fields such as petrochemical complex, metallurgy, chemical fibre, traffic, electric power, building, special extensive especially in the application of various offshore engineering equipments, naval vessels, oil platform, port and pier steel construction etc.
Existing heavy-duty coating, anti-medium osmosis and wear resisting property are poor, and work-ing life is short, during use, generally all needs to use glass reinforced plastic or rubber lining,, execution conditions are comparatively complicated, inefficiency, maintenance difficult.
Generally all contain volatile solvent, these volatile solvents can insulting health.In the situation that ventilation is all right, the accumulation of this volatile solvent is less, and human health is had to certain infringement, and under the construction environment of improper ventilation, this infringement is just more outstanding.
Summary of the invention
The object of the present invention is to provide a kind of novel heavy corrosion-proof ring epoxy resins basalt flake paint.
The technical scheme that this your name takes is:
A kind of heavy corrosion-proof ring epoxy resins basalt flake paint, comprise first, second two components, it is characterized in that: first component comprises epoxy resin 20 ~ 40 weight parts, dibutyl phthalate 25 ~ 38 weight parts, dispersion agent 15 ~ 35 weight parts, defoamer 20 ~ 40 weight parts, flow agent 20 ~ 39 weight parts, pigment zinc phosphate 10 ~ 25 weight parts, basalt scale 12 ~ 78 weight parts, and component B comprises: polymeric amide 20 ~ 40 weight parts, solvent 25 ~ 40 weight parts.A heavy corrosion-proof ring epoxy resins basalt flake paint, is characterized in that: solvent is mixed solvent, by propyl carbinol: dimethylbenzene volume ratio=15 ~ 20:7 forms.
During use, first, second two components mix in the ratio of 3 ~ 7:0.9.
It is stopping composition that the present invention adopts basalt scale, utilize its labyrinth effect, effectively stop the infiltration of corrosive medium, its infiltration rate reduces by 8-9 times, has the plurality of advantages such as adhesion strength is high, anti-corrosion, permeability resistance is good, the shrinking percentage of filming is low, thermal expansivity is little, curing unrelieved stress is low, wear-resistant, easy construction, easy repairing.
Embodiment
Embodiment 1
First component:
Epoxy resin 40 weight parts, dibutyl phthalate 30 weight parts, dispersion agent 29 weight parts, defoamer 38 weight parts, flow agent 32 weight parts, pigment zinc phosphate 19 weight parts, basalt scale 50 weight parts;
Second component:
Polymeric amide 28 weight parts, solvent 32 weight parts.
Wherein solvent is mixed solvent, consists of propyl carbinol: dimethylbenzene volume ratio=17:7.
During use, first, component B is mixed in the ratio of 5:1.
Embodiment 2
First component:
Epoxy resin 25 weight parts, dibutyl phthalate 35 weight parts, dispersion agent 20 weight parts, defoamer 35 weight parts, flow agent 23 weight parts, pigment zinc phosphate 22 weight parts, basalt scale 65 weight parts;
Second component:
Kymene 0 weight part, solvent 35 weight parts.
Wherein solvent is mixed solvent, consists of propyl carbinol: dimethylbenzene volume ratio=18:7.
During use, first, component B is mixed in the ratio of 6:1.
The performance perameter that detects above each embodiment by ordinary method, result is as follows:
It is stopping composition that the present invention adopts basalt scale, utilize its labyrinth effect, effectively stop the infiltration of corrosive medium, its infiltration rate reduces by 8-9 times, has the plurality of advantages such as adhesion strength is high, anti-corrosion, permeability resistance is good, the shrinking percentage of filming is low, thermal expansivity is little, curing unrelieved stress is low, wear-resistant, easy construction, easy repairing.
Claims (2)
1. one kind weighs corrosion-proof ring epoxy resins basalt flake paint, comprise first, second two components, it is characterized in that: first component comprises epoxy resin 20 ~ 40 weight parts, dibutyl phthalate 25 ~ 38 weight parts, dispersion agent 15 ~ 35 weight parts, defoamer 20 ~ 40 weight parts, flow agent 20 ~ 39 weight parts, pigment zinc phosphate 10 ~ 25 weight parts, basalt scale 12 ~ 78 weight parts, and component B comprises: polymeric amide 20 ~ 40 weight parts, solvent 25 ~ 40 weight parts.
2. a kind of heavy corrosion-proof ring epoxy resins basalt flake paint according to claim 1, is characterized in that: solvent is mixed solvent, by propyl carbinol: dimethylbenzene volume ratio=15 ~ 20:7 forms.