CN106590356A - Basalt flake anticorrosion paint - Google Patents

Basalt flake anticorrosion paint Download PDF

Info

Publication number
CN106590356A
CN106590356A CN201610984026.3A CN201610984026A CN106590356A CN 106590356 A CN106590356 A CN 106590356A CN 201610984026 A CN201610984026 A CN 201610984026A CN 106590356 A CN106590356 A CN 106590356A
Authority
CN
China
Prior art keywords
parts
basalt
component
agent
anticorrosive paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610984026.3A
Other languages
Chinese (zh)
Inventor
钱立兵
程丽萍
谈亚蓓
李宁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Meng Gu Filamentary Material Science And Technology Ltd
Original Assignee
Anhui Meng Gu Filamentary Material Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Meng Gu Filamentary Material Science And Technology Ltd filed Critical Anhui Meng Gu Filamentary Material Science And Technology Ltd
Priority to CN201610984026.3A priority Critical patent/CN106590356A/en
Publication of CN106590356A publication Critical patent/CN106590356A/en
Pending legal-status Critical Current

Abstract

The invention discloses a basalt flake anticorrosion paint, and belongs to the field of anticorrosion paints. The paint comprises a component A and a component B; wherein the component A comprises the following raw materials in parts by weight: 30 to 80 parts of vinyl resin, 15 to 40 parts of basalt flake, 10 to 45 parts of filling material, 5 to 30 parts of pigment, 1 to 6 parts of auxiliary agent, and 0.3 to 4 parts of solvent; and the component B comprises the following raw materials in parts by weight: 0.3 to 2 parts of promoter, and 0.5 to 5 parts of curing agent. The invention aims to solve the problems of glass flake paints such as low mechanical strength, bad weatherability, bad performance on resisting acid corrosion, and the like. The prepared anticorrosion paint has the advantages of good mechanical properties, good performance on resisting acid and alkali, good weatherability, and long service life. Moreover, compared with transparent glass flakes, dark basalt flakes also have a good UV resistant performance, and the damage of UV rays to the coating is reduced therefore. The paint can be applied to desulfurization and denitration apparatuses and the anticorrosion performance is excellent.

Description

A kind of basalt flake anticorrosive paint
Technical field
The present invention relates to a kind of anticorrosive paint, and in particular to a kind of basalt flake anticorrosive paint.
Background technology
Sulfur dioxide (SO in coal-fired flue-gas2), nitrogen oxides (NOx) be China's air major pollutants.Flue gas takes off Sulfur, denitration are current more effective means.Contain SO in coal-fired plant flue gas2、NOx, the composition such as HCl, HF, desulphurization system washes Contain H in paint liquid2SO4, HCl, HF etc., and containing 20% or so solid content.Desulfuration absorbing tower inlet temperature is up to 110-120 ℃.Therefore, wet desulfurization system requires extremely strict to the resistance to candle of material, wear-resisting, heatproof.
At present the conventional anticorrosive paint of desulfuring and denitrifying apparatus is flake anticorrosive paint, and described flake anticorrosive paint mostly is glass Glass scale resin coating.But the heat conductivity of glass is low, it is unfavorable for the raising of coating heat resistance.Due to glass flake fragility Greatly, mechanical strength is not high, there are problems that easily aging, easy, and during life-time service, glass-flake coating holds Easily there is the phenomenon of anticorrosion failure.
The content of the invention
According to problems of the prior art, the present invention provides a kind of basalt flake anticorrosive paint, it is intended to solve glass Glass flake paint mechanical strength is low, weatherability is poor, the problem that acid corrosion-resistant performance is low.
In order to solve the above problems, the present invention is employed the following technical solutions：
A kind of basalt flake anticorrosive paint, comprising two kinds of components of first, second, described first component includes following parts by weight Raw material：30～80 parts of vinylite, 15～40 parts of basalt scale, 10～45 parts of filler, 5～30 parts of pigment, auxiliary agent 1～ 6 parts, 0.3～4 part of solvent；Raw material of the described component B comprising following parts by weight：0.3～2 part of accelerator, firming agent 0.5 ～5 parts.
Preferably, the fineness degree of described basalt scale is 20～400 mesh, and thickness is 2～6 μm.
Preferably, described vinylite is epoxy novolac type vinyl ester resin.
Preferably, described filler be Pulvis Talci, silica flour, blanc fixe, in attapulgite one or two with On mixture.
Preferably, described pigment is titanium dioxide or zinc phosphate.
Mixture of the preferred described auxiliary agent for dispersant, defoamer and levelling agent；Described solvent is styrene；Institute The accelerator stated is cobalt octoate；Described firming agent is methyl ethyl ketone peroxide.
Preferably, described first component is prepared in the following order：Under agitation, add in vinyl ester resin and fill out Material, pigment, auxiliary agent, solvent are uniformly mixed, and add basalt scale, are uniformly mixed, first is obtained after ground dispersion Component.
The beneficial effects of the present invention is：
1) present invention substitutes traditional glass flake using basalt scale, and the basalt scale is by melting the Black Warrior A kind of lepidiod material obtained from rock and ore, is free of contamination pure ecological product；Basalt scale can improve polymeric material The antiseptic property of material simultaneously improves its wearability, and monolayer average thickness is that 500 μm of coating has 150～200 layers of scale, can cambium layer Anti-corrosion layer penetrance is reduced to original 1/10～1/15 by shape curved structure, can also improve mechanical performance, the heat of coating Deformation temperature, dielectric properties, reduce thermal expansion and contraction.Also there is very strong resistance to acids and bases and good weatherability simultaneously, make The antiseptic property for obtaining basalt flake paint is very prominent, and service life is greatly prolonged, and has obvious in similar flake paint Advantage.Compared with transparent glass flake, dark basalt scale has good anti-ultraviolet property, preferably can shield Cover destruction of the solar UV to paint film.The coating is applicable to desulfuring and denitrifying apparatus, and Corrosion Protection is excellent.
2) present invention using in Pulvis Talci, silica flour, blanc fixe and attapulgite one or more Mixture makees filler；Pulvis Talci can improve its thermoelasticity and crack resistance in heat-resisting paint；Silica flour can strengthen coating Anti-uv-ray, and with good insulating properties, to improving paint, the storage stability of coating and reducing production cost effect It is significantly；The volumetric concentration of blanc fixe scalable pigment, improves the adhesive force of paint film；Attapulgite can be risen to coating To good reinforcing effect.
3) present invention adopts titanium dioxide or zinc phosphate to make pigment, ferrum white lead as opacifying property pigment, with excellent impermeable Bright property and covering power, while with superior weather resistance, heat stability and chemical stability；Zinc phosphate is a kind of environment friend Good, non-poisonous antirust pigment, in various coating systems, the compatibility is fine, and under the high temperature conditions, can produce more stable And not volatile zinc pyrophosphate, due to its it is environmentally friendly, efficient the characteristics of, alternative leaded, chromium pigment.
4) cobalt octoate and methyl ethyl ketone peroxide are included in component B of the present invention, the cobalt octoate and methyl ethyl ketone peroxide can be Construction temperature is to be solidified resin crosslinks under -10～40 DEG C of middle cryogenic conditions.
5) make solvent from styrene in first component of the present invention, can both reduce the viscosity of vinyl ester resin, can promote again Enter the solidification and crosslinking of resin.
6) present invention adopt the higher vinyl ester resin with good mechanical properties of heat distortion temperature for raw material, made coating Heat resistance is good, mechanical performance is high, and with good adhesive force.
Specific embodiment
With reference to embodiments, the technical scheme in the present invention is clearly and completely described.Based in the present invention Embodiment, the every other embodiment obtained under the premise of creative work is not made by those of ordinary skill in the art, all Belong to the scope of protection of the invention.
Embodiment 1
A kind of basalt flake anticorrosive paint, comprising two kinds of components of first, second, described first component includes following parts by weight Raw material：70 parts of vinyl ester resin (epoxy novolac type vinyl ester resin), 30 parts of basalt scale, filler (Pulvis Talci) 30 Part, 30 parts of pigment (titanium dioxide), 3 parts of auxiliary agent, 2 parts of solvent (styrene)；Original of the described component B comprising following parts by weight Material：0.5 part of accelerator (cobalt octoate), 3 parts of firming agent (methyl ethyl ketone peroxide).
It is 1 by weight that described auxiliary agent is dispersant, defoamer and levelling agent:1:1 mixture.
Described first component is prepared in the following order：Under agitation, filler, face are added in vinyl ester resin Material, auxiliary agent, solvent are uniformly mixed, and add basalt scale, are uniformly mixed, first component is obtained after ground dispersion.
Described component B is will to be obtained after accelerator and firming agent mixing and stirring.
During construction, by the first and second two kinds of component mix homogeneously.
Embodiment 2
A kind of basalt flake anticorrosive paint, comprising two kinds of components of first, second, described first component includes following parts by weight Raw material：30 parts of vinyl ester resin (epoxy novolac type vinyl ester resin), 20 parts of basalt scale, filler (silica flour) 10 Part, 20 parts of pigment (zinc phosphate), 2 parts of auxiliary agent, 1.5 parts of solvent (styrene)；Described component B includes following parts by weight Raw material：1 part of accelerator (cobalt octoate), 1.5 parts of firming agent (methyl ethyl ketone peroxide).
It is 1 by weight that described auxiliary agent is dispersant, defoamer and levelling agent:1:1 mixture.
Described first component is prepared in the following order：Under agitation, filler, face are added in vinyl ester resin Material, auxiliary agent, solvent are uniformly mixed, and add basalt scale, are uniformly mixed, first component is obtained after ground dispersion.
Described component B is will to be obtained after accelerator and firming agent mixing and stirring.
During construction, by first and second liang of component mix homogeneously.
Embodiment 3
A kind of basalt flake anticorrosive paint, comprising two kinds of components of first, second, described first component includes following parts by weight Raw material：75 parts of vinyl ester resin (epoxy novolac type vinyl ester resin), 40 parts of basalt scale, filler (sulfate precipitate Barium) 10 parts, 10 parts of pigment (titanium dioxide), 4 parts of auxiliary agent, 4 parts of solvent (styrene)；Described component B includes following parts by weight Raw material：0.3 part of accelerator (cobalt octoate), 5 parts of firming agent (being methyl ethyl ketone peroxide).
It is 1 by weight that described auxiliary agent is dispersant, defoamer and levelling agent:1:1 mixture.
Described first component is prepared in the following order：Under agitation, filler, face are added in vinyl ester resin Material, auxiliary agent, solvent are uniformly mixed, and add basalt scale, are uniformly mixed, first component is obtained after ground dispersion.
Described component B is will to be obtained after accelerator and firming agent mixing and stirring.
During construction, by first and second liang of component mix homogeneously.
Obtained in embodiment 1, the Specifeca tion speeification of basalt flake anticorrosive paint is shown in Table 1.
Table 1
Adhesive force 1～2 grade
Impact resistance 120kg.cm
Hardness ≥0.6
Maximum operation (service) temperature 180℃
Acid resistance (80%H2SO4) 100d is unchanged
Alkali resistance (60%NaOH) 100d is unchanged
Resistance to water 120d is unchanged
Oil resistivity 120d is unchanged
As seen from the above table, the basalt flake anticorrosive paint in the present invention not only has excellent acid-proof alkaline, and With extremely strong impact resistance, so as to be effectively improved the adhesion property of gained paint film after the coating of this coating, also significantly carry The antiseptic property and weatherability of this coating are risen.

Claims (10)

1. a kind of basalt flake anticorrosive paint, it is characterised in that：Comprising two kinds of components of first, second, described first component comprising with The raw material of lower parts by weight：30～80 parts of vinylite, 15～40 parts of basalt scale, 10～45 parts of filler, pigment 5～30 Part, 1～6 part of auxiliary agent, 0.3～4 part of solvent；Raw material of the described component B comprising following parts by weight：0.3～2 part of accelerator, 0.5～5 part of firming agent.
2. a kind of basalt flake anticorrosive paint according to claim 1, it is characterised in that described first component comprising with The raw material of lower parts by weight：70 parts of vinyl ester resin, 30 parts of basalt scale, 30 parts of filler, 30 parts of pigment, 3 parts of auxiliary agent are molten 2 parts of agent；Raw material of the described component B comprising following parts by weight：0.5 part of accelerator, 3 parts of firming agent.
3. a kind of basalt flake anticorrosive paint according to claim 1, it is characterised in that described first component comprising with The raw material of lower parts by weight：30 parts of vinyl ester resin, 20 parts of basalt scale, 10 parts of filler, 20 parts of pigment, 2 parts of auxiliary agent are molten 1.5 parts of agent；Raw material of the described component B comprising following parts by weight：1 part of accelerator, 1.5 parts of firming agent.
4. a kind of basalt flake anticorrosive paint according to claim 1, it is characterised in that described first component comprising with The raw material of lower parts by weight：75 parts of vinyl ester resin, 40 parts of basalt scale, 10 parts of filler, 10 parts of pigment, 4 parts of auxiliary agent are molten 4 parts of agent；Raw material of the described component B comprising following parts by weight：0.3 part of accelerator, 5 parts of firming agent.
5. a kind of basalt flake anticorrosive paint according to any one of Claims 1 to 4, it is characterised in that：Described is profound The fineness degree of military rock scale is 20～400 mesh, and thickness is 2～6 μm.
6. a kind of basalt flake anticorrosive paint according to any one of Claims 1 to 4, it is characterised in that：Described second Ene based resins are epoxy novolac type vinyl ester resin.
7. a kind of basalt flake anticorrosive paint according to any one of Claims 1 to 4, it is characterised in that：Described fills out Expect for one or more the mixture in Pulvis Talci, silica flour, blanc fixe, attapulgite.
8. a kind of basalt flake anticorrosive paint according to any one of Claims 1 to 4, it is characterised in that：Described face Expect for titanium dioxide or zinc phosphate.
9. a kind of basalt flake anticorrosive paint according to any one of Claims 1 to 4, it is characterised in that：Described helps Mixture of the agent for dispersant, defoamer and levelling agent；Described solvent is styrene；Described accelerator is cobalt octoate；Institute The firming agent stated is methyl ethyl ketone peroxide.
10. a kind of basalt flake anticorrosive paint according to any one of Claims 1 to 4, it is characterised in that described first Component is prepared in the following order：Under agitation, in vinyl ester resin filler, pigment, auxiliary agent, solvent is added to stir Mix homogeneously, adds basalt scale, is uniformly mixed, first component is obtained after ground dispersion.
CN201610984026.3A 2016-11-09 2016-11-09 Basalt flake anticorrosion paint Pending CN106590356A (en)