CN103627208B - 一种复合活性黑色染料 - Google Patents
一种复合活性黑色染料 Download PDFInfo
- Publication number
- CN103627208B CN103627208B CN201310652639.3A CN201310652639A CN103627208B CN 103627208 B CN103627208 B CN 103627208B CN 201310652639 A CN201310652639 A CN 201310652639A CN 103627208 B CN103627208 B CN 103627208B
- Authority
- CN
- China
- Prior art keywords
- formula
- component
- black dye
- black
- reactive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种复合活性黑色染料,如下重量百分比的组份组成:60-80%如式(1)所示的组份A,5~10%如式(2)所示的组份B,5~10%如式(3)所示的组份C,5~10%如式(4)所示的组份D,5~10%如式(5)所示的组份E。该复合活性黑色染料采用五种组分进行混拼,提高了染料的乌黑度;同时该五种组分的亲水/亲油性、对纤维的直接性相似,上染和固色性能协调,匀染性好,并且得到的染料的各项牢度均优。
Description
技术领域
本发明属染料技术领域,具体涉及一种复合活性黑色染料。
背景技术
为了提高染料的耐洗牢度,人们一直在试图制造一种能与纤维共价结合的染料。1956年英国ICI公司首先生产了含二氯均三嗪活性基的棉用活性染料,此后,世界各国相继发展开发生产出各种类型的活性染料。目前,活性染料已发展成为用于纤维素纤维的染料中最重要的一类。
黑色染料一直是染料中用量最大的品种,直接耐日晒黑染料的色牢度较差,硫化黑虽然色牢度较好,但存在环保问题,所以其应用受到越来越多的限制,因此,中温型活性黑成了棉(粘)织物浸染黑色的首选,其应用范围越来越广。
目前市场上以活性黑5#为主的乙烯砜基型活性黑印花产品为主导,活性黑5#在最大吸收波长600nm处的吸收值偏低,实际上是一只灰度较高的藏青色染料,而非黑色染料,因此,以活性黑5#为主拼混黑色,必须按余色原理添加适量蓝色的余色-橙色,将蓝光适度地消除。普通活性黑通常是以高浓度的活性黑5#为主色(占60%~80%),活性橙做副色(占10%~20%),再添加少量活性黄或活性红做次色拼混而成。
活性橙82#反应性高、提升性好,与活性黑5#拼混容易获得乌黑度较好的黑色,且价格低廉,故被广泛用于活性黑的拼混。然而采用活性黑5#与活性橙82#混拼得到的黑色染料存在匀染性和重现性问题。这是由于活性橙82#一端为乙烯砜基,另一端为二氯均三嗪活性基,反应性高,适合30~40℃吸色、固色,提高染色温度上色迅猛,极易色花;同时耐热耐碱稳定性差,极易发生水解。
直接以活性橙82#与活性黑5#混拼得到的活性黑染料在60~65℃染色,会因为活性橙82#组分上色过快而产生布面色花;因不同染料水解程度不同,产生色光异变,重现性不佳;染料水解量多且亲和力较高,易洗性差,导致后整理时产生云状色斑和色牢度低下等问题。
随着生活水平的日益提高,人们对纺织产品的要求也越来越高,从而使用于纺织品染色的活性染料在各项性能上的要求日益苛刻,开发出各项性能均优的活性黑染料成为目前亟待解决的问题。
发明内容
本发明提供了一种复合活性黑色染料,该染料匀染性好,具有较高的乌黑度,同时具有较高的耐汗渍牢度和皂洗牢度。
一种复合活性黑色染料,由如下重量百分比的组份组成:
所述的组份A为式(1)所示化合物中的一种或多种:
式(1)中,R1和R2选自H、卤素、C1~C4烷基或者C1~C4烷氧基;
所述的组份B为式(2)所示化合物中的一种或多种:
式(2)中,R3选自H、卤素、C1~C4烷基或者C1~C4烷氧基;
所述的组份C为式(3)所示化合物中的一种或多种:
式(3)中,R4和R5选自H、C1~C4烷基、C1~C4烷氧基或SO3M,其中,M为H、Na或K;
所述的组份D为式(4)所示化合物中的一种或多种:
式(4)中,R6和R7选自H、C1~C4烷基、C1~C4烷氧基或SO3M,其中,M为H、Na或K;
所述的组份E为式(5)所示化合物中的一种或多种:
式(5)中,R8和R9选自H、卤素、C1~C4烷基或者C1~C4烷氧基。
本发明中,采用五种组分进行混拼,其中,组分A为主组分,其他四种组分用于弥补主组分的不足,提高了得到的复合染料的乌黑度;同时该五种组分的亲水/亲油性、对纤维的直接性相似,上染和固色性能协调,匀染性好,并且得到的染料的各项牢度均优。
作为优选,所述的复合活性黑色染料由如下重量百分比的组份组成:
综合考虑原料的成本和染料的各项牢度,所述的组分A选自式(1-1)~式(1-3)中的至少一种:
作为优选,所述的组分B选自式(2-1)~式(2-3)中的至少一种:
作为优选,所述的组分C选自式(3-1)~式(3-4)中的至少一种:
作为优选,所述的组分D选自式(4-1)~式(4-4)中的至少一种:
作为优选,所述的组分E选自式(5-1)~式(5-3)中的至少一种:
作为更进一步的优选,组分A为式(1-1)所示的化合物,组分B为式(2-1)所示的化合物,组分C为式(3-1)所示的化合物,组分D为式(4-1)所示的化合物,组分E为式(5-1)所示的化合物;此时,得到的复合活性黑色染料的乌黑度和匀染性最好。
本发明中的复合活性黑色染料在制备时通常需要加入活性染料常用的助剂来提高染料的分散性能,助剂的加入量通常为产品总重量的3~5%,助剂可采用市售产品,作为优选,所述助剂为分散剂MF或扩散剂NNO。
本发明的复合活性黑色染料可用常规方法制备,如按所需比例机械地混合染料组份A~E及助剂,或以本领域熟知的方式进行拼混,其中染料组份可以以粉状、粒颗状、合成水溶液形式存在;助剂可以以粉状、溶液的形式存在。染料组份A~E可采用市售产品,也可以采用本领域熟知的方法进行制备。
同现有技术相比,本发明的有益效果体现在:本发明的复合活性黑色染料非常适用于纤维素织物的轧染和印花,具有较高的乌黑度、优良的色牢度、好的匀染性、易水洗性和经济性,以及对纤维素纤维良好的选择性。
具体实施方式
下面结合实施例和比例对本发明作进一步说明。但本发明的保护范围不限于此。
实施例1~15
根据表1中数据所示,将染料组份A、染料组份B、染料组份C、染料组份D、染料组份E、及助剂使用拼混设备混合均匀,或者液体浆料直接混合均匀。
表1
将上述实施例制得的活性染料采用标准的活性染料进行染色测试,得其相应的性能数据,见表2。其中所用相关标准为:
GB/T2374-2007染料染色测定的一般条件规定;
GB/T2387-2006反应染料色光和强度的测定;
GB/T3920-1997纺织品色牢度试验耐摩擦色牢度(eqv ISO105-X12:1993);
GB/T3921.4-1997纺织品色牢度试验耐洗色牢度(eqv ISO105-C04:1989);
GB/T3922-1995纺织品耐汗渍色牢度试验方法(eqv ISO105-E04:1994);
表2
通过表2的检测数据分析,本发明得到的复合黑染料完全可以按照不同染色色相来调整配比,从Integ值数据分析,由于配比的变化得到的结果也有所波动,但不影响产品使用效果;其中,通过同时加入组分D、组分C和组分E会提高耐摩牢度、耐汗渍和皂洗牢度,当组分A为式(1-1)所示的化合物,组分B为式(2-1)所示的化合物,组分C为式(3-1)所示的化合物,组分D为式(4-1)所示的化合物,组分E为式(5-1)所示的化合物;此时,得到的复合活性黑色染料的各项牢度更加卓越。
Claims (7)
1.一种复合活性黑染料,其特征在于,由如下重量百分比的组份组成:
余量为助剂;
所述的组份A选自式(1-1)~式(1-3)中的至少一种::
所述的组份B为式(2)所示化合物中的一种或多种:
式(2)中,R3选自H、卤素、C1~C4烷基或者C1~C4烷氧基;
所述的组份C为式(3)所示化合物中的一种或多种:
式(3)中,R4和R5选自H、C1~C4烷基、C1~C4烷氧基或SO3M,其中,M为H、Na或K;
所述的组份D为式(4)所示化合物中的一种或多种:
式(4)中,R6和R7选自H、C1~C4烷基、C1~C4烷氧基或SO3M,其中,M为H、Na或K;
所述的组份E为式(5)所示化合物中的一种或多种:
式(5)中,R8和R9选自H、卤素、C1~C4烷基或者C1~C4烷氧基。
2.根据权利要求1所述的复合活性黑染料,其特征在于,由如下重量百分比的组份组成:
余量为助剂。
3.根据权利要求1所述的复合活性黑染料,其特征在于,所述的组分B选自式(2-1)~式(2-3)中的至少一种:
4.根据权利要求1所述的复合活性黑染料,其特征在于,所述的组分C选自式(3-1)~式(3-4)中的至少一种:
5.根据权利要求1所述的复合活性黑染料,其特征在于,所述的组分C选自式(4-1)~式(4-4)中的至少一种:
6.根据权利要求1所述的复合活性黑染料,其特征在于,所述的组分C选自式(5-1)~式(5-3)中的至少一种:
7.根据权利要求1~6任一项所述的复合活性黑染料,其特征在于,所述助剂为分散剂MF或扩散剂NNO。