CN103614100B - 一种阻燃型防水密封用热熔压敏胶及其制备方法 - Google Patents
一种阻燃型防水密封用热熔压敏胶及其制备方法 Download PDFInfo
- Publication number
- CN103614100B CN103614100B CN201310586418.0A CN201310586418A CN103614100B CN 103614100 B CN103614100 B CN 103614100B CN 201310586418 A CN201310586418 A CN 201310586418A CN 103614100 B CN103614100 B CN 103614100B
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardant
- polyisobutene
- sensitive adhesive
- waterproof sealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种阻燃型防水密封用热熔压敏胶，包括：丁基橡胶268、溴化丁基橡胶、聚异丁烯B50、聚异丁烯B12、辛基酚醛树酯、热塑性弹性体SBS、矿物油、十溴联苯醚、三氧化二锑、氢氧化铝、氧化锌、抗氧剂1010、炭黑。本发明通过配方体系入手，选择防水密封性非常好的树脂和橡胶体系，配合协同阻燃性能优异的阻燃剂，在保证产品防水密封性及粘接强度的同时，获得了高的阻燃性能的热熔型压敏胶。制得的压敏胶粘剂在-40～80℃温度范围内具有很高的粘接强度且具有优异的绝缘、防水、阻燃、密封性能，用该产品可生产防水密封胶带，电线电缆绝缘包缠、管道密封等。
Description
技术领域
本发明涉及胶黏剂领域，尤其涉及压敏胶粘剂领域。
背景技术
伴随着科学技术的不断发展，电子电器设备的功率不断加大，这些设备应用的场所也更加的广泛和苛刻。大功率电器的应用使得对电线电缆的要求越来越高，尤其是在电线电缆接头部位。如果接头部位密封性不好，防水性较差，那么就会存在非常大的风险，有可能会造成设备短路而破坏或者起火而引发火灾。所以应用到接头上的产品必须是要防水密封性好，而且阻燃等级越高越好。
发明内容
本发明通过配方体系入手，选择防水密封性非常好的树脂和橡胶体系，配合协同阻燃性能优异的阻燃剂，在保证产品防水密封性及粘接强度的同时，获得了高的阻燃性能的热熔型压敏胶。
本发明的技术方案是：一种阻燃型防水密封用热熔压敏胶，以重量份计包括：
丁基橡胶268 20-60
溴化丁基橡胶 20-70
聚异丁烯B50 10-50
聚异丁烯B12 50-200
辛基酚醛树酯 50-150
热塑性弹性体SBS 10-60
矿物油 10-50
十溴联苯醚 50-150
三氧化二锑 20-80
氢氧化铝 50-200
氧化锌 5-20
抗氧剂1010 1-5
炭黑 20-40
一种本发明所述的阻燃型防水密封用热熔压敏胶的制备方法，包括：捏合机升温至80-120℃后，将聚异丁烯B50、聚异丁烯B12、丁基橡胶268、溴化丁基橡胶、辛基酚醛树酯、热塑性弹性体SBS、抗氧剂1010、氧化锌加入到捏合机中，充分捏合1-3h后再依次加入矿物油、十溴联苯醚、三氧化二锑、氢氧化铝、炭黑，加入完成后温度保持120-150℃捏合1-3h后出料，冷却至室温后既得阻燃型热熔压敏胶。
本发明的有益效果是：该压敏胶粘剂在-40～80℃温度范围内具有很高的粘接强度且具有优异的绝缘、防水、阻燃、密封性能，用该产品可生产防水密封胶带，电线电缆绝缘包缠、管道密封等。
具体实施例
以下实施例中所用到的原料为:
丁基橡胶268，美国埃克森
溴化丁基橡胶，BIIR2222，美国埃克森
聚异丁烯B50，德国巴斯夫
聚异丁烯B12，德国巴斯夫
SBS，D4150，美国科腾
辛基酚醛树酯，HY-2045，山西化工研究所
氧化锌，唐山海港合缘锌业有限公司
抗氧剂1010，辽宁嘉凯精化有限公司
矿物油，淄博泰畅润滑油有限公司
十溴联苯醚，山东天一化学有限公司
三氧化二锑，益阳华昌锑业
氢氧化铝，常州市迎燕复合材料有限公司
实施例1
捏合机升温至90℃，将丁基268橡胶40份、溴化丁基橡胶20份、聚异丁烯B50 20份、聚异丁烯B12 100份、SBS 30份、辛基酚醛树酯100份、氧化锌10份、抗氧剂1010 2份加入到捏合机中，充分捏合1h后再依次加入矿物油10份、十溴联苯醚80份、三氧化二锑40份、氢氧化铝150份、炭黑30份，加入完成后温度保持130℃捏合2h后出料，冷却至室温后既得阻燃型热熔压敏胶。
实施例2
捏合机升温至90℃，将丁基268橡胶20份、溴化丁基橡胶60份、聚异丁烯B50 30份、聚异丁烯B12 120份、SBS 40份、辛基酚醛树酯70份、氧化锌15份、抗氧剂1010 3份加入到捏合机中，充分捏合2h后再依次加入矿物油20份、十溴联苯醚110份、三氧化二锑50份、氢氧化铝100份、炭黑30份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后既得阻燃型热熔压敏胶。
实施例3
捏合机升温至110℃，将丁基268橡胶50份、溴化丁基橡胶40份、聚异丁烯B50 50份、聚异丁烯B12 150份、SBS 50份、辛基酚醛树酯80份、氧化锌20份、抗氧剂1010 4份加入到捏合机中，充分捏合2h后再依次加入矿物油15份、十溴联苯醚150份、三氧化二锑60份、氢氧化铝120份、炭黑30份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后既得阻燃型热熔压敏胶。
实施例4
捏合机升温至110℃，将丁基268橡胶30份、溴化丁基橡胶70份、聚异丁烯B50 10份、聚异丁烯B12 160份、SBS 60份、辛基酚醛树酯120份、氧化锌20份、抗氧剂1010 5份加入到捏合机中，充分捏合2h后再依次加入矿物油30份、十溴联苯醚100份、三氧化二锑70份、氢氧化铝160份、炭黑40份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后既得阻燃型热熔压敏胶。
实施例5
捏合机升温至120℃，将丁基268橡胶60份、溴化丁基橡胶50份、聚异丁烯B50 40份、聚异丁烯B12 180份、SBS 20份、辛基酚醛树酯90份、氧化锌5份、抗氧剂1010 3份加入到捏合机中，充分捏合3h后再依次加入矿物油50份、十溴联苯醚120份、三氧化二锑80份、氢氧化铝180份、炭黑40份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后既得阻燃型热熔压敏胶。
通过下面的试验测试本发明制备的阻燃型热熔压敏胶的性能。
试验实施例1
剥离强度依据GB/T 2792-1988进行测试。
试验实施例2
拉伸剪切强度依据GB/T 7124-2008进行测试。
试验实施例3
水汽透过率依据GB 1037-1988进行测试。
试验实施例4
阻燃性依据UL94垂直燃烧试验进行测试。
测试结果如下：
从上表的实验结果可以看出，本发明制备的阻燃型热熔压敏胶，初粘性高，粘接强度大，水汽透过率低，阻燃性能良好。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (2)
1.一种阻燃型防水密封用热熔压敏胶，以重量份计包括：
丁基橡胶268 20-60
溴化丁基橡胶 20-70
聚异丁烯B50 10-50
聚异丁烯B12 50-200
辛基酚醛树脂 50-150
热塑性弹性体SBS 10-60
矿物油 10-50
十溴联苯醚 50-150
三氧化二锑 20-80
氢氧化铝 50-200
氧化锌 5-20
抗氧剂1010 1-5
炭黑 20-40。
2.如权利要求1所述的阻燃型防水密封用热熔压敏胶的制备方法，包括：捏合机升温至80-120℃后，将聚异丁烯B50、聚异丁烯B12、丁基橡胶268、溴化丁基橡胶、辛基酚醛树脂、热塑性弹性体SBS、抗氧剂1010、氧化锌加入到捏合机中，充分捏合1-3h后再依次加入矿物油、十溴联苯醚、三氧化二锑、氢氧化铝、炭黑，加入完成后温度保持120-150℃捏合1-3h后出料，冷却至室温后即得阻燃型防水密封用热熔压敏胶。
3.根据权利要求2所述的制备方法，其特征在于，包括：捏合机升温至90℃，将丁基橡胶268 40份、溴化丁基橡胶20份、聚异丁烯B50 20份、聚异丁烯B12 100份、SBS 30份、辛基酚醛树脂100份、氧化锌10份、抗氧剂1010 2份加入到捏合机中，充分捏合1h后再依次加入矿物油10份、十溴联苯醚80份、三氧化二锑40份、氢氧化铝150份、炭黑30份，加入完成后温度保持130℃捏合2h后出料，冷却至室温后即得阻燃型防水密封用热熔压敏胶。
4.根据权利要求2所述的制备方法，其特征在于，包括：捏合机升温至90℃，将丁基橡胶268 20份、溴化丁基橡胶60份、聚异丁烯B50 30份、聚异丁烯B12 120份、SBS 40份、辛基酚醛树脂70份、氧化锌15份、抗氧剂1010 3份加入到捏合机中，充分捏合2h后再依次加入矿物油20份、十溴联苯醚110份、三氧化二锑50份、氢氧化铝100份、炭黑30份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后即得阻燃型防水密封用热熔压敏胶。
5.根据权利要求2所述的制备方法，其特征在于，包括：捏合机升温至110℃，将丁基橡胶268 50份、溴化丁基橡胶40份、聚异丁烯B50 50份、聚异丁烯B12 150份、SBS 50份、辛基酚醛树脂80份、氧化锌20份、抗氧剂1010 4份加入到捏合机中，充分捏合2h后再依次加入矿物油15份、十溴联苯醚150份、三氧化二锑60份、氢氧化铝120份、炭黑30份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后即得阻燃型防水密封用热熔压敏胶。
6.根据权利要求2所述的制备方法，其特征在于，包括：捏合机升温至110℃，将丁基橡胶268 30份、溴化丁基橡胶70份、聚异丁烯B50 10份、聚异丁烯B12 160份、SBS 60份、辛基酚醛树脂120份、氧化锌20份、抗氧剂1010 5份加入到捏合机中，充分捏合2h后再依次加入矿物油30份、十溴联苯醚100份、三氧化二锑70份、氢氧化铝160份、炭黑40份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后即得阻燃型防水密封用热熔压敏胶。
7.根据权利要求2所述的制备方法，其特征在于，包括：捏合机升温至120℃，将丁基橡胶268 60份、溴化丁基橡胶50份、聚异丁烯B50 40份、聚异丁烯B12 180份、SBS 20份、辛基酚醛树脂90份、氧化锌5份、抗氧剂1010 3份加入到捏合机中，充分捏合3h后再依次加入矿物油50份、十溴联苯醚120份、三氧化二锑80份、氢氧化铝180份、炭黑40份，加入完成后温度保持140℃捏合3h后出料，冷却至室温后即得阻燃型防水密封用热熔压敏胶。