CN103613850B - A kind of Filament for vermin-proof plastic woven bag - Google Patents
A kind of Filament for vermin-proof plastic woven bag Download PDFInfo
- Publication number
- CN103613850B CN103613850B CN201310617633.2A CN201310617633A CN103613850B CN 103613850 B CN103613850 B CN 103613850B CN 201310617633 A CN201310617633 A CN 201310617633A CN 103613850 B CN103613850 B CN 103613850B
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- filament
- vermin
- ferrocene
- woven bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of Filament for vermin-proof plastic woven bag, it is characterized in that, be made up by operations such as batching, melting, filtration, extruding membrane, water-cooled, sub-wire, wire drawing, rollings of the raw material of following weight part: polypropylene 100, metallocene linear-low density polyethylene 4-6, pyrethroid 0.2-0.4, Mono-n-butyltin 0.4-0.6, acrylate 3.2-3.6, chlorinatedpolyethylene 2-4, ferrocene 1-1.5, methyl ethyl diketone selenium 0.1-0.2, auxiliary agent 3-3.5; The present invention adds auxiliary agent, can be effectively anti-aging, anti-Exposure to Sunlight, and rationally, cost is low for formula, and the Polywoven Bag made can effective anti-insect bite, adds work-ing life and the use range of packing bag, is applicable to long-distance transport and article and preserves and use.
Description
Technical field
The present invention relates to chemical technology field, particularly a kind of Filament for vermin-proof plastic woven bag.
Background technology
Polywoven Bag is divided into Polypropylene Bag, polyethylene bag by main raw formation; Bag at the bottom of seam end bag, tape edge is divided into by method of sewing.Be widely used in a kind of wrapping material of the article such as fertilizer, Chemicals at present.Its main production utilizes plastic raw materials to be flat filament through extrusion film, cutting, unilateral stretching, through obtaining product through knitting device, is commonly referred to as woven bag.The packing bag of the polypropylene flat-filament establishment that conventional art is produced, weathering resistance is poor, easily occur hardening at north of china in winter, embrittlement, demoulding, peeling, the problem such as fracture, in south because summer temperature is high, illumination strong, ultraviolet penetration power is strong, easily cause that woven bag is aging, the problem such as burn into poor toughness, intensity low work-ing life is short, not only wasted resource but also contaminate environment.
Summary of the invention
The object of this invention is to provide a kind of Filament for vermin-proof plastic woven bag.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of Filament for vermin-proof plastic woven bag, is made up by operations such as batching, melting, filtration, extruding membrane, water-cooled, sub-wire, wire drawing, rollings of the raw material of following weight part: polypropylene 100, metallocene linear-low density polyethylene 4-6, pyrethroid 0.2-0.4, Mono-n-butyltin 0.4-0.6, acrylate 3.2-3.6, chlorinatedpolyethylene 2-4, ferrocene 1-1.5, methyl ethyl diketone selenium 0.1-0.2, auxiliary agent 3-3.5;
Described auxiliary agent is made up of the raw material of following weight part: clay 20-24, alum 5-6, altax 2-3, linking agent TAC2-3, antioxidant 1010 1-2, Tremoliteor Tremoliteasbestos 3-4, ferrocene 2-3, morpholine 1-2,1,6 hexanediyl ester 5-7, phthalic ester 35-40, Tenox PG 3-4, green tea powder 1-2, coix seed oil 2-3, vanadium diboride 2-3, l-Epicatechol 1-2; Clay, Tremoliteor Tremoliteasbestos are sent in calcining furnace and calcine 2-3 hour at 720-740 DEG C by preparation method, then, take out, send in the hydrochloric acid soln of 10-15% and soak 2-3 hour, filter, obtain filter residue, clean, dry, grind to form 400-600 order powder with clear water; Gained powder mixes with other remaining component, is heated to 60-70 DEG C, stirring reaction 40-50 minute, and cooling, grinds to form slurry, to obtain final product.
Excellent effect of the present invention is: the present invention adds auxiliary agent, can be effectively anti-aging, anti-Exposure to Sunlight, rationally, cost is low for formula, and the Polywoven Bag made can effective anti-insect bite, add work-ing life and the use range of packing bag, be applicable to long-distance transport and article preservation use.
Embodiment
Below by specific examples, the present invention is described in detail.
A kind of Filament for vermin-proof plastic woven bag, is made up by operations such as batching, melting, filtration, extruding membrane, water-cooled, sub-wire, wire drawing, rollings of the raw material of following weight part (kilogram): polypropylene 100, metallocene linear-low density polyethylene 4, pyrethroid 0.2, Mono-n-butyltin 0.4, acrylate 3.2, chlorinatedpolyethylene 2, ferrocene 1, methyl ethyl diketone selenium 0.1, auxiliary agent 3;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): described auxiliary agent is made up of the raw material of following weight part (kilogram): clay 20, alum 5, altax 3, linking agent TAC2, antioxidant 1010 1, Tremoliteor Tremoliteasbestos 3, ferrocene 2, morpholine 1,1,6 hexanediyl ester 5, phthalic ester 35, Tenox PG 3, green tea powder 1, coix seed oil 2, vanadium diboride 3, l-Epicatechol 1; Clay, Tremoliteor Tremoliteasbestos are sent in calcining furnace and calcine 2-3 hour at 720-740 DEG C by preparation method, then, take out, send in the hydrochloric acid soln of 10-15% and soak 2-3 hour, filter, obtain filter residue, clean, dry, grind to form 400-600 order powder with clear water; Gained powder mixes with other remaining component, is heated to 60-70 DEG C, stirring reaction 40-50 minute, and cooling, grinds to form slurry, to obtain final product.
After tested, the radial pull-off force of the flat filament that the present invention produces and broadwise pull-off force are all greater than 790N/50mm, substantially increase the tensile strength of flat filament, have stopped the fracture of wire problem in braiding process.
Claims (1)
1. a Filament for vermin-proof plastic woven bag, it is characterized in that, be made up by operations such as batching, melting, filtration, extruding membrane, water-cooled, sub-wire, wire drawing, rollings of the raw material of following weight part: polypropylene 100, metallocene linear-low density polyethylene 4-6, pyrethroid 0.2-0.4, Mono-n-butyltin 0.4-0.6, acrylate 3.2-3.6, chlorinatedpolyethylene 2-4, ferrocene 1-1.5, methyl ethyl diketone selenium 0.1-0.2, auxiliary agent 3-3.5;
Described auxiliary agent is made up of the raw material of following weight part: clay 20-24, alum 5-6, altax 2-3, linking agent TAC2-3, antioxidant 1010 1-2, Tremoliteor Tremoliteasbestos 3-4, ferrocene 2-3, morpholine 1-2,1,6 hexanediyl ester 5-7, phthalic ester 35-40, Tenox PG 3-4, green tea powder 1-2, coix seed oil 2-3, vanadium diboride 2-3, l-Epicatechol 1-2; Clay, Tremoliteor Tremoliteasbestos are sent in calcining furnace and calcine 2-3 hour at 720-740 DEG C by preparation method, then, take out, send in the hydrochloric acid soln of 10-15% and soak 2-3 hour, filter, obtain filter residue, clean, dry, grind to form 400-600 order powder with clear water; Gained powder mixes with other remaining component, is heated to 60-70 DEG C, stirring reaction 40-50 minute, and cooling, grinds to form slurry, to obtain final product.