CN103602786B - 一种狭缝式透气砖的制备方法 - Google Patents

一种狭缝式透气砖的制备方法 Download PDF

Info

Publication number
CN103602786B
CN103602786B CN201310580577.XA CN201310580577A CN103602786B CN 103602786 B CN103602786 B CN 103602786B CN 201310580577 A CN201310580577 A CN 201310580577A CN 103602786 B CN103602786 B CN 103602786B
Authority
CN
China
Prior art keywords
gas permeable
permeable brick
green compact
slit
demoulding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310580577.XA
Other languages
English (en)
Other versions
CN103602786A (zh
Inventor
郜桥刚
邵淑英
彭小品
张伟
李纪伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HENAN HAIGEER HIGH TEMPERATURE MATERIAL CO Ltd
Original Assignee
HENAN HAIGEER HIGH TEMPERATURE MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HENAN HAIGEER HIGH TEMPERATURE MATERIAL CO Ltd filed Critical HENAN HAIGEER HIGH TEMPERATURE MATERIAL CO Ltd
Priority to CN201310580577.XA priority Critical patent/CN103602786B/zh
Publication of CN103602786A publication Critical patent/CN103602786A/zh
Application granted granted Critical
Publication of CN103602786B publication Critical patent/CN103602786B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种狭缝式透气砖的制备方法，涉及钢包精炼用透气砖的制备方法，包括将透气砖浇注料在浇注模具内浇注成形，并制成透气砖生坯的步骤，将透气砖生坯经养护和脱模的步骤、将脱模后的透气砖生坯烘干和高温烧制，并最终制成成品的步骤，所述浇注模具内根据要制备的透气砖的狭缝结构固定有可烧失的狭缝填充物，在将透气砖浇注料浇注成形制成透气砖生坯之前，先在所述的狭缝填充物的表面均匀涂抹润滑剂；在将透气砖生坯经养护和脱模之后，先将狭缝填充物从透气砖生坯内抽出，然后再进行将透气砖生坯经烘干和高温烧制的步骤。本发明制备的狭缝式透气砖在其它同等制备条件下可提高透气砖的透气量10%左右，降低了透气砖成品因透气不足而带来的废品率。

Description

一种狭缝式透气砖的制备方法
技术领域
本发明涉及钢包精炼用透气砖的制备方法，具体为一种狭缝式透气砖的制备方法。
背景技术
透气砖是钢水精炼中钢包底吹氩必需的功能性元件。根据透气原理，透气砖的主要种类为狭缝式透气砖，成品狭缝式透气砖内部有狭缝通道，用于向钢包内吹入氩气。狭缝式透气砖是由浇注料浇注成形，并经高温烧成而得。制作浇注模具时，为了形成透气砖内部的狭缝通道，通常在模具内根据狭缝结构布置并固定一定厚度的可烧失的狭缝填充物，浇注成型后，砖坯经养护、脱模和烘干后，再在高温窑内经高温烧制而得成品。高温烧制过程中，狭缝填充物被烧掉，从而留下透气的狭缝通道。但是，高温烧制后狭缝填充物会有残留，使狭缝通道阻碍，造成透气砖透气量不足的问题，在成品砖的透气率检测中，常常由于透气量不足而产生废品。
发明内容
本发明的目的就是提供一种狭缝式透气砖的制备方法，解决现有的狭缝式透气砖制备过程中由于狭缝填充物烧后的残留造成了透气砖透气量不足的问题。
为了实现上述目的，本发明的技术方案为：一种狭缝式透气砖的制备方法，包括将透气砖浇注料在浇注模具内浇注成形，并制成透气砖生坯的步骤，将透气砖生坯经养护和脱模的步骤、将脱模后的透气砖生坯烘干和高温烧制，并最终制成透气砖成品的步骤，所述浇注模具内根据要制备的透气砖的狭缝结构固定有可烧失的狭缝填充物，在将透气砖浇注料浇注成形制成透气砖生坯之前，先在所述的狭缝填充物的表面均匀涂抹润滑剂；在将透气砖生坯经养护和脱模之后，先将狭缝填充物从透气砖生坯内抽出，然后再进行将透气砖生坯经烘干和高温烧制的步骤。
所述的润滑剂为机油。
有益效果：本发明在狭缝式透气砖的制备过程中，通过在狭缝填充物表面涂抹润滑剂使得透气砖的狭缝填充物可以抽出而不破坏透气砖生坯的结构，然后在接下来的烘干和高温烧制环节中，可以避免狭缝填充物烧后残余造成的成品透气砖透气量不足的问题。本发明方法制备的狭缝式透气砖在其它同等制备条件下可平均提高透气砖的透气量10%左右，降低了透气砖成品因透气不足而带来的废品率。
具体实施方式
一种狭缝式透气砖的制备方法，包括将透气砖浇注料在浇注模具内浇注成形，并制成透气砖生坯的步骤，将透气砖生坯经养护和脱模的步骤、将脱模后的透气砖生坯烘干和高温烧制，并最终制成透气砖成品的步骤，所述浇注模具内根据要制备的透气砖的狭缝结构固定有可烧失的狭缝填充物，在将透气砖浇注料浇注成形制成透气砖生坯之前，先在所述的狭缝填充物的表面均匀涂抹机油；在将透气砖生坯经养护和脱模之后，先将狭缝填充物从透气砖生坯内抽出，然后再进行将透气砖生坯经烘干和高温烧制的步骤。
狭缝填充物表面所涂抹的机油主要起润滑作用，以便于将狭缝填充物从透气砖生坯内抽出时不破坏透气砖生坯的结构。

Claims (2)

1.一种狭缝式透气砖的制备方法，包括将透气砖浇注料在浇注模具内浇注成形，并制成透气砖生坯的步骤，将透气砖生坯经养护和脱模的步骤、将脱模后的透气砖生坯烘干和高温烧制，并最终制成透气砖成品的步骤，所述浇注模具内根据要制备的透气砖的狭缝结构固定有可烧失的狭缝填充物，其特征在于：在将透气砖浇注料浇注成形制成透气砖生坯之前，先在所述的狭缝填充物的表面均匀涂抹润滑剂；在将透气砖生坯经养护和脱模之后，先将狭缝填充物从透气砖生坯内抽出以形成狭缝，然后再进行将透气砖生坯经烘干和高温烧制的步骤。
2.如权利要求1所述的一种狭缝式透气砖的制备方法，其特征在于：所述的润滑剂为机油。
CN201310580577.XA 2013-11-19 2013-11-19 一种狭缝式透气砖的制备方法 Expired - Fee Related CN103602786B (zh)