CN103601432A - 基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料 - Google Patents
基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料 Download PDFInfo
- Publication number
- CN103601432A CN103601432A CN201310592381.2A CN201310592381A CN103601432A CN 103601432 A CN103601432 A CN 103601432A CN 201310592381 A CN201310592381 A CN 201310592381A CN 103601432 A CN103601432 A CN 103601432A
- Authority
- CN
- China
- Prior art keywords
- concrete waste
- crack
- waste material
- coal ash
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
.本发明涉及一种基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料,其包括蒸压粉煤灰加气混凝土废料,40~65份;水泥,35~60份;甲基纤维素,0.07~0.1份;胶粉,0.1~0.25份;抗裂纤维,0.03~0.1份;助剂,0.01~0.02份。本发明首次利用蒸压粉煤灰加气混凝土废料制备抹面抗裂砂浆干粉料,有效降低了砂浆干粉料成本,开发的产品能够作为墙体自保温原材料,就地为建筑配套使用,节约资源、变废为宝,能促进建筑节能工作的发展;并且干粉料制备方法简单,无二次污染,原料来源广泛,适于工业化生产。
Description
技术领域
本发明涉及建筑材料技术领域一种抹面抗裂砂浆干粉料,尤其涉及一种利用蒸压粉煤灰加气混凝土废料制备的低成本抹面抗裂砂浆干粉料。
背景技术
我国煤产量居世界首位,在煤炭的生产和加工过程中,排放大量的煤矸石;在煤炭、煤矸石的燃烧发电过程中会产生大量的粉煤灰,由此催生了蒸压粉煤灰加气混凝土。
蒸压粉煤灰加气混凝土是一种具有墙体自保温的新型建筑墙材,主要以水泥、石灰、石膏、铝粉以及粉煤灰为原料,经过原材料制备、配料浇注、静养发气、坯体切割、蒸压养护、成品贮存等工序制成。其原料的来源非常的广泛,并且有非常好的可加工能力、隔热、保温能力以及加工特性,可铇可锯。随着墙材革新工作的不断推进,蒸压粉煤灰加气混凝土砌块已逐渐在建筑工程中得到规模应用。
随着蒸压粉煤灰加气混凝土应用的广泛,在生产过程中,切割废料、搬运废料以及不合格品废料总量也日益增多,无处堆放、无地运出,给企业造成极大困扰,给环境带来污染。目前,除了利用蒸压粉煤灰加气混凝土废料制备膨胀水泥、加气混凝土废碎渣墙体、密实(或配筋)硅酸盐酸盐混凝土制品和密实硅酸盐瓦材产品以及硅酸盐水磨石制品、铺地及贴墙用各色面砖等,有人研究了利用其去除含磷废水中的磷的方法。
但是以上技术无法就地利用废料,并且废料利用率较低、废料利用技术不完善,会产生二次污染,所以其市场推广存在难度。如何妥善处理、有效利用蒸压粉煤灰加气混凝土废料并获得较高的社会效益、生态效益和经济效益是亟待解决的问题。
发明内容
本发明的目的是提供一种基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料,所得抹面抗裂砂浆干粉料可以直接应用于墙体自保温系统。
为达到上述发明目的,本发明采用的技术方案是:
一种基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料,以质量份计,包括以下组分:
蒸压粉煤灰加气混凝土废料 40~65份
水泥 35~60份
甲基纤维素 0.07~0.1份
胶粉 0.1~0.25份
抗裂纤维 0.03~0.1份
助剂 0.01~0.02份
其中,胶粉为乙烯/醋酸乙烯酯的共聚物;抗裂纤维为聚丙烯纤维;助剂为萘系减水剂。
本发明中胶粉为乙烯/醋酸乙烯酯的共聚物,为可再分散胶粉;甲基纤维素为建筑业用MC粉料;水泥为强度等级为42.5的硅酸盐水泥;蒸压粉煤灰加气混凝土废料为蒸压粉煤灰加气混凝土生产过程中的废品或建筑垃圾中产生的蒸压粉煤灰加气混凝土废料。
本发明还公开了上述基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料的制备方法,具体为先将蒸压粉煤灰加气混凝土废料粉磨为蒸压粉煤灰加气混凝土废料粉料备用;然后按照各组分的比例,将蒸压粉煤灰加气混凝土废料粉料、水泥、甲基纤维素、胶粉、抗裂纤维以及助剂依次加入粉体混合机中混合均匀,即制备得到所述的基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料。
上述技术方案中,粉磨设备为球磨机,粉磨过程包括破碎、研磨,筛分;所得蒸压粉煤灰加气混凝土废料粉料的粒径为60~120目。
由于上述技术方案运用,本发明与现有技术相比具有下列优点:
1.本发明首次利用蒸压粉煤灰加气混凝土废料制备抹面抗裂砂浆,有效降低了砂浆成本,开发的产品能够作为墙体自保温原材料就地为建筑配套使用,节约资源、变废为宝,能促进建筑节能工作的发展;
2.本发明公开的制备方法简单,无二次污染,原料来源广泛,适于工业化生产。
具体实施方式
下面结合实施例对本发明做进一步描述。
根据不同要求,本领域技术人员可以选用下列组分以及质量份的原料制备基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料:蒸压粉煤灰加气混凝土废料,40~65份;水泥,35~60份;甲基纤维素,0.07~0.1份;胶粉,0.1~0.25份;抗裂纤维,0.03~0.1份;助剂,0.01~0.02份。胶粉为乙烯/醋酸乙烯酯的共聚物可再分散胶粉;抗裂纤维为聚丙烯纤维;助剂为萘系减水剂。
下面通过具体实施例给予详述:
表1 各实施例中原料的质量,单位Kg
序号 | 蒸压粉煤灰加气混凝土废料 | PO.42.5水泥 | 甲基纤维素 | 胶粉 | 抗裂纤维 | 助剂 |
实施例1 | 40 | 60 | 0.1 | 0.1 | 0.03 | 0.02 |
实施例2 | 60 | 40 | 0.07 | 0.25 | 0.1 | 0.01 |
实施例3 | 65 | 35 | 0.09 | 0.2 | 0.06 | 0.015 |
具体制备方法为:先将蒸压粉煤灰加气混凝土废料破碎、研磨,筛分成蒸压粉煤灰加气混凝土废料粉料(实施例1、实施例2、实施例3中,蒸压粉煤灰加气混凝土废料粉料的粒径分别为60目、80目以及120目);然后按照上述各组分的比例称重,将蒸压粉煤灰加气混凝土废料粉料、水泥、甲基纤维素、胶粉、抗裂纤维以及助剂依次放入粉体混合机中混合均匀,即制备得到所述的基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料。
上述方法制作基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料时,只需一台研磨机和一套粉体混合设备就能生产出性能优于同类产品质量的建筑新材料。使用时,将干粉料产品运送至施工现场,按一定比例的水搅拌成为浆料,即可施工使用。
Claims (5)
1.一种基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料,其特征在于,以质量份计,包括以下组分:
蒸压粉煤灰加气混凝土废料 40~65份
水泥 35~60份
甲基纤维素 0.07~0.1份
胶粉 0.1~0.25份
抗裂纤维 0.03~0.1份
助剂 0.01~0.02份
其中,胶粉为乙烯/醋酸乙烯酯的共聚物;抗裂纤维为聚丙烯纤维;助剂为萘系减水剂。
2.根据权利要求1所述的抹面抗裂砂浆干粉料,其特征在于:所述水泥为强度等级为42.5硅酸盐水泥。
3.一种权利要求1所述抹面抗裂砂浆干粉料的制备方法,其特征在于,包括以下步骤:首先将蒸压粉煤灰加气混凝土废料粉磨为蒸压粉煤灰加气混凝土废料粉料;然后按照各组分的比例,将蒸压粉煤灰加气混凝土废料粉料、水泥、甲基纤维素、胶粉、抗裂纤维以及助剂依次加入粉体混合机中混合均匀,即制备得到所述的基于蒸压粉煤灰加气混凝土废料的抹面抗裂砂浆干粉料。
4.根据权利要求3所述抹面抗裂砂浆干粉料的制备方法,其特征在于:所述蒸压粉煤灰加气混凝土废料粉料的粒径为60~120目。
5.根据权利要求3所述抹面抗裂砂浆干粉料的制备方法,其特征在于:用于蒸压粉煤灰加气混凝土废料粉磨的设备为球磨机。