CN103589058A - Reinforced polypropylene composite material and preparation method thereof - Google Patents
Reinforced polypropylene composite material and preparation method thereof Download PDFInfo
- Publication number
- CN103589058A CN103589058A CN201310504517.XA CN201310504517A CN103589058A CN 103589058 A CN103589058 A CN 103589058A CN 201310504517 A CN201310504517 A CN 201310504517A CN 103589058 A CN103589058 A CN 103589058A
- Authority
- CN
- China
- Prior art keywords
- reinforced polypropylene
- compound material
- polypropylene
- reinforced
- polypropylene compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a reinforced polypropylene composite material and a preparation method thereof. The reinforced polypropylene composite material comprises 54-64 parts of PP (propene polymer) resin, 4-6 parts of polypropylene grafting maleic anhydride, 29-32 parts of glass fiber chopped strand, 3-5 parts of a flexibilizer, 0.2-1 part of an antioxidant, 0.5-1 part of a lubricant, 0.2-0.5 part of a floating fiber resisting agent, and 0.1-0.2 part of di(3,4 dimethyl) dibenzaldehyde sosrbitol. The reinforced polypropylene composite material prepared by the method holds high rigidity of glass fiber materials and reduces floating glass fibers, the impact strength and flowing property of the material are improved, and the reinforced polypropylene composite material can substitute for the existing materials of roller washing machines, and meets the requirements of high capacity, high load, high rotation speed and ultrathin sheet of modern washing machines.
Description
Technical field
The present invention relates to technical field of macromolecules, be specifically related to a kind of reinforced polypropylene compound material and preparation method thereof.
Background technology
Roller washing machine becomes requisite in modern society already, and the steel ladle of roller washing machine is mainly to make as fiber glass reinforced polypropylene, talc powder filled polypropylene with modified plastics, and contemporary roller washing machine is characterized as axle with ultra-thin and large capacity, two of high rotating speeds especially, so require its modified plastics resin will possess the features such as intensity is large, toughness is high, easy-formation, product any surface finish.
Polypropylene (PP) is a kind of crystal formation thermoplastic resin of high comprehensive performance, has the features such as nontoxic, tasteless, density is little; Its intensity, rigidity, hardness and thermotolerance are all better than low pressure polyethylene, can be about 100 ℃ uses; There is good electrical property and high-frequency insulation simultaneously and be not subject to humidity effect, but under cold condition, can become fragile, not wear-resisting, easily aging.Polypropylene is suitable for making common mechanical part, corrosion-resistant part and insulating part.The organic solvents such as common acid, alkali work hardly to it, can be used for tableware.But common PP intensity and toughness all do not reach roller washing machine water containing barrel and in high rotating speed, large capacity, full load situation, act on the requirement of the power on axis, so must just can make polypropylene reach its requirement through modification.
Fiber glass reinforced polypropylene is on the basis of original pure PP, adds glass fibre and other auxiliary agent, thereby improves the use range of material.General, most glass fiber reinforced materials is multiplex on the structural parts of product, it is a kind of Structural Engineering material, there is high strength, high rigidity, the features such as low contraction, when glass fiber content reaches certain limit, even can partly substitute iron and steel, but aspect toughness but relatively polypropylene reduce a lot, under high rotating speed high load condition, be easy to produce phenomenon of rupture and cause danger.And polypropylene is after being used glass to strengthen, it is apparent loses original glossiness and becomes coarse; It is can become very obvious that glass lines is greater than 15% at glass fiber content, and the glass fiber material that the major part that different household laundry machine cylinder steel ladle is used strengthens for 20%-30% left and right glass.
summary of the invention
For overcoming the deficiencies in the prior art, the invention discloses reinforced polypropylene compound material of a kind of high strength, high tenacity, low floating fibre and preparation method thereof.
The reinforced polypropylene compound material that the inventive method makes, by polyacrylic modification, has improved toughness and rigidity that original glass strengthens PP, and floating fine phenomenon also greatly reduces.
Technical scheme of the present invention is: a kind of reinforced polypropylene compound material, consists of by weight following raw materials according:
PP resin 54-64 part
Polypropylene grafted maleic anhydride (PP-g-MAH) 4-6 part
Glass fibre 29-32 part
Toughner 3-5 part
Oxidation inhibitor 0.2-1 part
Lubricant 0.5-1 part
The fine agent 0.2-0.5 of anti-floating part
Two (3,4 dimethyl two benzals) Sorbitol Powder 0.1-0.2 part
Further, described polypropylene is at least one in isotatic polypropylene, syndiotactic polypropylene, Atactic Polypropelene.
Further, described toughner is a kind of in ethylene-octene copolymer, terpolymer EP rubber/propylene-alpha olefin multipolymer, propylene-alpha olefin multipolymer, styrene-ethylene-propylene-styrene segmented copolymer.
Further, described glass fibre is fiberglas chopped strand, and its diameter is between 10-14 μ m, length is 3.0-4.5mm.
Further, the percentage of grafting of described polypropylene grafted maleic anhydride is 1.5-2.0%.
Further, described oxidation inhibitor is at least one in Hinered phenols, monothioester class, phosphorous acid ester type thermal stabilizing agent.
Further, described Hinered phenols is four [β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester (antioxidant 1010), monothioester class is thio-2 acid 2 stearyl ester (oxidation inhibitor DSTP), phosphorous acid esters are tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester (irgasfos 168).
Further, described lubricant is selected from least one in polyethylene wax, stearate, ethylene bis stearamide, grafting ethylene bis stearamide.
In the present invention, anti-glass emergence on the surface agent is named again in the fine agent of anti-floating, is to be white or micro-yellow particle or Powdered.On the basis of ethylene bis-fatty acid amides (EBS), to introduce polar group to form lower molecular weight BAB type multipolymer.Can buy in the market.
Another object of the present invention is to provide the preparation method of above-mentioned reinforced polypropylene compound material, comprises the following steps:
(1) by proportioning, take polypropylene, polypropylene grafted maleic anhydride, toughner, oxidation inhibitor, lubricant, fine agent, two (3, the 4 dimethyl two benzals) Sorbitol Powder of anti-floating, add together the mixing machine high speed that is connected with nitrogen protection to mix 2-10 minute;
(2), under nitrogen protection, (1) mixture is dropped into melting in parallel double-screw extruder, then add glass fibre from the side spout of forcing machine, through extruding, granulation makes reinforced polypropylene compound material; Wherein the barrel zone temperature of forcing machine is 205-220 ℃, and screw speed is 400-600r/min, and vacuum tightness is-0.04~0.1MPa.
Reinforced polypropylene compound material of the present invention has following beneficial effect with respect to prior art:
1, the reinforced polypropylene compound material that the present invention makes is to adopt general PP base material, toughner, lubricant and oxidation inhibitor to make, and its starting material are easy to get and can be directly used in suitability for industrialized production; And available waste or used plastics source PP utilizes problem to solve the reclaiming of waste or used plastics source PP
2, because glass fibre and coupling agent polypropylene grafted maleic anhydride carry out surface treatment, the fine polar group of agent of anti-floating produces very strong magnetism with the long-chain end of coupling agent by Fan get Hua, and this magnetism is enough to make two phase interfaces disappearances, and forms a phase; In addition, solvation segment and the matrix resin of the fine agent of anti-floating have certain intermiscibility, and the fine agent of anti-floating has played phase solvent effect.Like this, between glass fibre, acrylic resin, form cross-linking set, improved the bond state of glass and acrylic resin, impelled glass to the toughening effect between acrylic resin, and reduced the glass exposing widely.
3, during reinforced polypropylene compound material common die injection moulding of the present invention, just can obtain brighter and cleaner than common Reinforced Polypropylene outward appearance, the product of low floating fibre.
4, according to the examination criteria reinforced polypropylene compound material notched Izod impact strength of the industry, be greater than 15KJ/m
2, modulus in flexure is greater than 5500Mpa, shows that the shock strength of this material is high, has good flowing property simultaneously, the rigidity of material and toughness have realized well balanced; Make reinforced polypropylene compound material of the present invention have high rigidity, high tenacity, high temperature tolerance, thereby it is thinner to meet contemporary washing machine, rotating speed is higher, the more feature of function.
5, in the present invention, increased polypropylene nucleater two (3,4 dimethyl two benzals) Sorbitol Powder, has improved the physical and mechanical properties such as the transparency, surface luster, tensile strength, rigidity, heat-drawn wire, shock resistance, creep resistance of polypropylene composite material goods.
Embodiment
For better understanding the present invention, below in conjunction with embodiment, the invention will be further described, and following examples are only that the present invention will be described but not it is limited.
The glass fibre adopting in embodiment is below short glass fiber precursor, and its diameter is between 10-14 μ m, length is 3.0-4.5mm.
Embodiment mono-:
Reinforced polycarbonate matrix material in the present embodiment consists of by weight following raw materials according:
Isotactic homo-polypropylene 64
Glass fibre 32
Propylene-alpha olefin multipolymer 3
PP-g-MAH 5
The fine agent 0.5 of anti-floating
Lubricant calcium stearate 0.3
Lubricant polyethylene wax 0.2
Antioxidant 1010 1
Two (3,4 dimethyl two benzals) Sorbitol Powder 0.1
Concrete preparation method comprises the following steps:
(1) by 64 parts of isotactic homo-polypropylene, 3 parts of propylene-alpha olefin multipolymers, 5 parts of polypropylene grafted maleic anhydrides (PP-g-MAH), 1 part of antioxidant 1010,0.2 part of lubricant polyethylene wax, 0.3 part of lubricant calcium stearate, the fine agent of 0.5 anti-floating, 0.1 part of two (3,4 dimethyl two benzals) Sorbitol Powder adds the mixing machine high speed that is connected with nitrogen protection to mix 10 minutes;
(2) under nitrogen protection, (1) mixture is dropped into melting in parallel double-screw extruder, then add 32 parts, glass fibre from the side spout of forcing machine, through extruding, granulation, make reinforced polypropylene compound material; Wherein each barrel zone temperature of forcing machine is 205-220 ℃, and screw speed is 400r/min, and vacuum tightness is-0.04MPa to make the reinforced polypropylene compound material of high tenacity, high rigidity, low floating fibre.
Embodiment bis-:
Reinforced polycarbonate matrix material in the present embodiment consists of by weight following raw materials according:
Isotactic homo-polypropylene 44
Atactic copolymerized polypropene 10
Glass fibre 30
Ethylene-octene copolymer 4
PP-g-MAH 4
The fine agent 0.2 of anti-floating
Lubricant calcium stearate 0.3
Lubricant ethylene bis stearamide 0.4
Antioxidant 1010 0.3
Irgasfos 168 0.2
Two (3,4 dimethyl two benzals) Sorbitol Powder 0.1
Concrete preparation method comprises the following steps:
(1) by 44 parts of isotactic homo-polypropylene, 10 parts of atactic copolymerized polypropenes, 4 parts of ethylene-octene copolymers, 4 parts of polypropylene grafted maleic anhydrides, 0.3 part of antioxidant 1010,0.2 part of irgasfos 168,0.4 part of lubricant ethylene bis stearamide, 0.3 part of lubricant calcium stearate, the fine agent of 0.2 anti-floating, 0.1 part of two (3,4 dimethyl two benzals) Sorbitol Powder adds the mixing machine high speed that is connected with nitrogen protection to mix 6 minutes;
(2) under nitrogen protection, (1) mixture is dropped into melting in parallel double-screw extruder, then add 30 parts, glass fibre from the side spout of forcing machine, through extruding, granulation, make reinforced polypropylene compound material; Wherein the barrel zone temperature of forcing machine is 205-220 ℃, and screw speed is 500r/min, and vacuum tightness is-0.01MPa to make the reinforced polypropylene compound material of high tenacity, high rigidity, low floating fibre.
Embodiment tri-:
Reinforced polycarbonate matrix material in the present embodiment consists of by weight following raw materials according:
Isotactic homo-polypropylene 30
Atactic copolymerized polypropene 30
Glass fibre 29
Terpolymer EP rubber/propylene-alpha olefin multipolymer 5
PP-g-MAH 6
The fine agent 0.4 of anti-floating
Lubricant calcium stearate 0.5
Lubricant polyethylene wax 0.5
Antioxidant 1010 0.1
Irgasfos 168 0.1
Two (3,4 dimethyl two benzals) Sorbitol Powder 0.2
Concrete preparation method comprises the following steps:
(1) by 30 parts of isotactic homo-polypropylene, 30 parts of atactic copolymerized polypropenes, 5 parts of terpolymer EP rubber/propylene-alpha olefin multipolymers, 6 parts of polypropylene grafted maleic anhydrides, 0.1 part of antioxidant 1010,0.1 part of irgasfos 168,0.5 part of lubricant polyethylene wax, 0.5 part of lubricant calcium stearate, the fine agent of 0.4 anti-floating, 0.1 part of two (3,4 dimethyl two benzals) Sorbitol Powder adds the mixing machine high speed that is connected with nitrogen protection to mix 2 minutes;
(2) under nitrogen protection, (1) mixture is dropped into melting in parallel double-screw extruder, then add 29 parts, glass fibre from the side spout of forcing machine, through extruding, granulation, make reinforced polypropylene compound material; Wherein the barrel zone temperature of forcing machine is 205-220 ℃, and screw speed is 600r/min, and melt pressure is 1.5MPa, and vacuum tightness is 0.1MPa, makes the reinforced polypropylene compound material of high tenacity, high rigidity, low floating fibre.
The main physical index of reinforced polypropylene compound material that above-described embodiment 1-3 is made is strong according to its tensile strength of correlation detection standard testing, elongation at break, flexural strength, modulus in flexure, socle girder notch shock, density and shrinking percentage, its examination criteria and detected result as shown in Table 1:
Table 1: the main physical index of reinforced polycarbonate matrix material of embodiment 1-4
The high rigidity that as can be seen from Table 1 prepared by the present invention, high tenacity, low floating fiber reinforced polypropylene composite material be take polypropylene copolymer as base material is under nitrogen protection; by reaction, extrude; the matrix material rigidity and the toughness that make have realized well balanced; modulus is greater than 5500MPa, and notched Izod impact strength is greater than 15 KJ/m
2, molding shrinkage is 0.4-0.7%, density < 1.14g/cm
3there is the fine performance of good anti-floating, can substitute existing roller washing machine material, meet the large capacity of contemporary washing machine, high capacity, high rotating speed and ultra-thin requirement.
As added the functional agents such as ultraviolet absorbers, photostabilizer, static inhibitor, tinting material of the present invention in preparing component, make matrix material there is individual features and protected by the present invention.
The above-mentioned description to embodiment is can understand and apply the invention for ease of those skilled in the art.Person skilled in the art obviously can easily make various modifications to these embodiment, and General Principle described herein is applied in other embodiment and needn't passes through performing creative labour.Therefore, the invention is not restricted to the embodiment here, those skilled in the art are according to announcement of the present invention, and not departing from the improvement that category of the present invention makes and revise all should be within protection scope of the present invention.
Claims (9)
1. a reinforced polypropylene compound material, is characterized in that: following raw materials according, consist of by weight:
Polypropylene 54-64 part
Polypropylene grafted maleic anhydride 4-6 part
Glass fibre 29-32 part
Toughner 3-5 part
Oxidation inhibitor 0.2-1 part
Lubricant 0.5-1 part
The fine agent 0.2-0.5 of anti-floating part
Two (3,4 dimethyl two benzals) Sorbitol Powder 0.1-0.2 part.
2. reinforced polypropylene compound material according to claim 1, is characterized in that: described polypropylene is at least one in isotatic polypropylene, syndiotactic polypropylene, Atactic Polypropelene.
3. according to the reinforced polypropylene compound material described in claim 1, it is characterized in that: described toughner is a kind of in ethylene-octene copolymer, terpolymer EP rubber/propylene-alpha olefin multipolymer, propylene-alpha olefin multipolymer, styrene-ethylene-propylene-styrene segmented copolymer.
4. reinforced polypropylene compound material according to claim 1, is characterized in that: described glass fibre is fiberglas chopped strand, and its diameter is between 10-14 μ m, length is 3.0-4.5mm.
5. reinforced polypropylene compound material according to claim 1, is characterized in that: the percentage of grafting of described polypropylene grafted maleic anhydride is 1.5-2.0%.
6. reinforced polypropylene compound material according to claim 1, is characterized in that: described oxidation inhibitor is at least one in Hinered phenols, monothioester class, phosphorous acid ester type thermal stabilizing agent.
7. reinforced polypropylene compound material according to claim 6, it is characterized in that: described Hinered phenols is four [β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester, monothioester class is thio-2 acid 2 stearyl ester, phosphorous acid esters are tricresyl phosphite (2,4-di-tert-butyl-phenyl) ester.
8. reinforced polypropylene compound material according to claim 1, is characterized in that: described lubricant is selected from least one in polyethylene wax, stearate, ethylene bis stearamide, grafting ethylene bis stearamide.
9. a method of preparing reinforced polypropylene compound material as claimed in claim 1, is characterized in that: comprise the following steps:
(1) by proportioning, take polypropylene, polypropylene grafted maleic anhydride, toughner, oxidation inhibitor, lubricant, fine agent, two (3, the 4 dimethyl two benzals) Sorbitol Powder of anti-floating, add together the mixing machine high speed that is connected with nitrogen protection to mix 2-10 minute;
(2), under nitrogen protection, (1) mixture is dropped into melting in parallel double-screw extruder, then add glass fibre from the side spout of forcing machine, through extruding, granulation makes reinforced polypropylene compound material; Wherein the barrel zone temperature of forcing machine is 205-220 ℃, and screw speed is 400-600r/min, and vacuum tightness is-0.04~0.1MPa.