CN108623901A - A kind of high strength glass fiber reinforced polypropylene compound material and preparation method thereof - Google Patents
A kind of high strength glass fiber reinforced polypropylene compound material and preparation method thereof Download PDFInfo
- Publication number
- CN108623901A CN108623901A CN201710186020.6A CN201710186020A CN108623901A CN 108623901 A CN108623901 A CN 108623901A CN 201710186020 A CN201710186020 A CN 201710186020A CN 108623901 A CN108623901 A CN 108623901A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- fiber reinforced
- high strength
- reinforced polypropylene
- compound material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high strength glass fiber reinforced polypropylene compound materials and preparation method thereof, are prepared by weight percentage by following components:Acrylic resin 47 84.2%, modified glass-fiber 10 40%, compatilizer 5 10%, stabilizer 0.4 1%, light stabilizer 0.1 1%, processing aid 0.3 1%;The wherein described modified glass-fiber is the glass fibre of area load nucleating agent, is 100 in mass ratio by glass fibre, alkali compounds and nucleating agent:0.3‑2:0.2 1 are mixed with.The present invention uses the surface-treated glass fiber of load nucleating agent as reinforcing filler, it is evenly dispersed in Pp System to can help to glass, and the bond strength of reinforcing glass fiber and polypropylene matrix, so as to provide the intensity of glass fiber reinforced polypropylene composite material significantly.
Description
Technical field
The present invention relates to a kind of technical field of modification of PP composite material more particularly to a kind of high strength glass fibers
Reinforced polypropylene material and preparation method thereof.
Background technology
Polypropylene material has in daily life and industrial and agricultural production and widely answers as one of five big general-purpose plastics
With, such as applied to appliance shell, washing machine drum, electric tool.But with industrialization development, how to reduce cost becomes very
More companies exploitation new products are done one's utmost the target pursued, therefore, before some commonly Engineering Plastics Parts at leisure by glass
Fiber reinforced polypropylene composite product is replaced.
Glass fibre is as reinforcing filler, since glass itself can transmit stress, institute when material is deformed by external force
There are much relations with the power of degree of scatter and the two binding force of the intensity and glass fibre of material in polypropylene matrix.
The present invention is using the surface-treated glass fiber of load nucleating agent as reinforcing filler, after the addition of nucleating agent makes melt blending
Composite modification material have higher crystallinity, evenly tiny crystallization local glass fibre can be promoted more uniformly to be distributed
It is embedded in non-crystalline areas, and the nucleating agent of fiberglass surfacing load can promote matrix polypropylene structure cell perpendicular to glass simultaneously
Side is grown up so that glass has higher bond strength with matrix, so that modified material has higher intensity, pole
The earth extends its application field.
Invention content
The object of the present invention is to provide a kind of high strength glass fiber reinforced polypropylene materials and preparation method thereof.
Technical scheme is as follows:
A kind of high strength glass fiber reinforced polypropylene compound material, prepared by weight percentage by following components and
At:
Acrylic resin 47-84.2%
Modified glass-fiber 10-40%
Compatilizer 5-10%
Stabilizer 0.4-1%
Light stabilizer 0.1-1%
Processing aid 0.3-1%;
The modified glass-fiber be area load nucleating agent glass fibre, by glass fibre, alkali compounds and
Nucleating agent is 100 in mass ratio:0.3-2:0.2-1 is mixed with.
Further scheme, the alkali compounds are calcium carbonate, magnesium hydroxide, aluminium hydroxide, zinc hydroxide, bicarbonate
At least one of sodium, sodium carbonate and potassium carbonate.
The nucleating agent is Sorbitol Nucleator;The compatilizer is maleic anhydride inoculated polypropylene.
The Sorbitol Nucleator is preferably two sub- (3,4- dimethyl) benzyl D-sorbites (DMDBS).
The stabilizer is selected from phenolic thermostabilizers, amine heat stabilizer, phosphite ester type thermal stabilizing agent, half Hinered phenols
At least one of heat stabilizer, calixarene kind heat stabilizer and dilauryl thiodipropionate heat stabilizer;The light is stablized
Agent is UV light stabilizing agent.
The UV light stabilizing agent is preferably septichen phenyl ester, three nitrogen of 2- (2- hydroxy-5-methyl bases phenyl) benzo
Azoles, 2,4-DihydroxyBenzophenone, ESCALOL 567,2-hydroxy-4-n-octoxybenzophenone, 2- (2-
Two tertiary phenyl of hydroxyl -3,5-) at least one of -5- chlorinations benzotriazole and single benzoic acid resorcinol.
The processing aid is low molecule esters processing aid, metal soap processing aid, the compound esters processing of stearic acid
At least one of auxiliary agent and amides processing aid.
Another goal of the invention of the present invention is to provide a kind of above-mentioned high strength glass fiber reinforced polypropylene compound material
Preparation method, first by glass fibre, alkali compounds and nucleating agent in mass ratio be 100:0.3-2:0.2-1 is put into high mixer
In, it is heated to 40-80 DEG C and is stirred for the 5-30 minutes modified glass-fibers to get area load nucleating agent;Then by polypropylene
Resin, compatilizer, stabilizer, light stabilizer, processing aid are added in mixing apparatus are uniformly mixed according to the ratio;Finally incite somebody to action
The mixture arrived is added from twin-screw extrusion owner's spout, and modified glass-fiber is added from double screw extruder side spout
Enter, through melting mixing, is granulated to obtain composite material.
Further scheme, the melting temperature are 200-270 DEG C.
The present invention is blended double-screw extruding pelletizing technique using conventional melt and prepares composite material, and method of modifying is simply easy
Row is suitble to scale of mass production;
The present invention is using the modified glass-fiber of load nucleating agent as reinforcing filler, since the addition of nucleating agent to melt
Melting the composite modification material after being blended has higher crystallinity, and evenly tiny crystallization local can promote glass fibre more equal
It is distributed evenly and is embedded in non-crystalline areas, make the crystal region uniformity of polypropylene matrix;And modified glass-fiber surface may be used also
Matrix polypropylene structure cell is promoted to be grown up perpendicular to glass side so that glass has higher bond strength with matrix, from
And make modified material that there is higher intensity, greatly extend its application field.
Specific implementation mode
Embodiment 1:
It is simple glass fiber by mass ratio:Magnesium hydroxide:Two sub- (3,4- dimethyl) benzyl D-sorbite=100:1:
0.5 ratio weighs up, and is put into high mixer, is heated to 60 DEG C, and the modification up to area load nucleating agent in 15 minutes is mixed
Glass fibre.
By acrylic resin 71.3%, compatilizer grafted maleic anhydride 7%, hindered phenol stabilizer 1,010 0.2%, phosphorous
Acid esters type thermal stabilizing agent PEP-36 0.2%, light stabilizer 2- (2- hydroxy-5-methyl bases phenyl) benzotriazole 0.7%, processing
Auxiliary agent low molecule esters-zinc stearate 0.6% are added in mixing apparatus and are uniformly mixed, by mixture from double screw extruder
Main spout is added, and glass fibre 20% made from above-mentioned modification is added from double screw extruder side spout, then will obtain
Mixture and glass fibre melting mixing is carried out by double screw extruder, melt temperature scope is 200-220 DEG C, and is passed through
It is granulated processing method and obtains the high strength glass fiber reinforced polypropylene compound material.
Comparative example 1:
By acrylic resin 71.3%, compatilizer grafted maleic anhydride 7%, hindered phenol stabilizer 1,010 0.2%, phosphorous
Acid esters type thermal stabilizing agent PEP-36 0.2%, light stabilizer 2- (2- hydroxy-5-methyl bases phenyl) benzotriazole 0.7%, processing
Auxiliary agent low molecule esters-zinc stearate 0.6% are added in mixing apparatus and are uniformly mixed, by mixture from double screw extruder
Main spout is added, and simple glass fiber 20% is added from double screw extruder side spout, then by obtained mixture and
Glass fibre carries out melting mixing by double screw extruder, and melt temperature scope is 200-220 DEG C, and by being granulated processing side
Formula obtains the high strength glass fiber reinforced polypropylene compound material.
Embodiment 2:
It is simple glass fiber by mass ratio:Alkali compounds (aluminium hydroxide:Zinc hydroxide=1:1):Two Asias (3,4- bis-
Methyl) benzyl D-sorbite (DMDBS)=100:0.3:0.2 ratio weighs up, and is put into high mixer, is heated to 40 DEG C, mixing
Stir 5 minutes modified glass-fibers up to area load nucleating agent.
By weight percentage, by acrylic resin 84.2%, compatilizer grafted maleic anhydride 5%, half hindered phenol antioxygen
Agent AO-80 0.4%, light stabilizer 2,4-DihydroxyBenzophenone 0.05%, ESCALOL 567 0.05%,
(grease amide, trimerization glycerol monosterate and calcium stearate are according to weight ratio 1 for processing aid:1:1 carry out mixing compounding and
At) 0.3% addition mixing apparatus in uniformly mixed, by mixture from twin-screw extrusion owner's spout be added, will be above-mentioned
Modified glass fibre 10% obtained is added from double screw extruder side spout, then obtained mixture and glass fibre are led to
Cross double screw extruder and carry out melting mixing, melt temperature scope is 200-250 DEG C, and by be granulated processing method obtain it is described
High strength glass fiber reinforced polypropylene compound material.
Comparative example 2
By weight percentage, by acrylic resin 84.2%, compatilizer grafted maleic anhydride 5%, half hindered phenol antioxygen
Agent AO-80 0.4%, light stabilizer 2,4-DihydroxyBenzophenone 0.05%, ESCALOL 567 0.05%,
(grease amide, trimerization glycerol monosterate and calcium stearate are according to weight ratio 1 for processing aid:1:1 carry out mixing compounding and
At) 0.3% addition mixing apparatus in uniformly mixed, by mixture from twin-screw extrusion owner's spout be added, will be common
Glass fibre 10% is added from double screw extruder side spout, then obtained mixture and glass fibre is squeezed by twin-screw
Go out machine and carry out melting mixing, melt temperature scope is 200-250 DEG C, and obtains the high-strength glass by being granulated processing method
Glass fiber reinforced polypropylene composite material.
Embodiment 3:
It is simple glass fiber by mass ratio:Sodium bicarbonate:Two sub- (3,4- dimethyl) benzyl D-sorbites (DMDBS)=
100:2:1 ratio weighs up, and is put into high mixer, is heated to 80 DEG C, is mixed 30 minutes up to area load nucleating agent
Modified glass-fiber.
By weight percentage, by acrylic resin 47%, compatilizer grafted maleic anhydride 10%, heat stabilizer is (by cup
Aromatic hydrocarbons type thermal stabilizing agent and dilauryl thiodipropionate=1:1) 1%, light stabilizer is (by 2- hydroxyl -4- n-octyloxy hexichol
Ketone, 2- (two tertiary phenyl of 2- hydroxyls -3,5-) -5- chlorinations benzotriazole and single benzoic acid resorcinol=1:1:1% 1) plus
Work auxiliary agent is (by sorbitan monostearate, glyceryl monostearate and magnesium stearate according to weight ratio 1:1:1 is mixed
Compounding) 1% addition mixing apparatus in uniformly mixed, by mixture from twin-screw extrusion owner's spout be added, will be above-mentioned
Modified glass fibre 40% obtained is added from double screw extruder side spout, then obtained mixture and glass fibre are led to
Cross double screw extruder and carry out melting mixing, melt temperature scope is 240-270 DEG C, and by be granulated processing method obtain it is described
High strength glass fiber reinforced polypropylene compound material.
Comparative example 3
By weight percentage, by acrylic resin 47%, compatilizer grafted maleic anhydride 10%, heat stabilizer is (by cup
Aromatic hydrocarbons type thermal stabilizing agent and dilauryl thiodipropionate=1:1) 1%, light stabilizer is (by 2- hydroxyl -4- n-octyloxy hexichol
Ketone, 2- (two tertiary phenyl of 2- hydroxyls -3,5-) -5- chlorinations benzotriazole and single benzoic acid resorcinol=1:1:1% 1) plus
Work auxiliary agent is (by sorbitan monostearate, glyceryl monostearate and magnesium stearate according to weight ratio 1:1:1 is mixed
Compounding) 1% addition mixing apparatus in uniformly mixed, by mixture from twin-screw extrusion owner's spout be added, will be common
Glass fibre 40% is added from double screw extruder side spout, then obtained mixture and glass fibre is squeezed by twin-screw
Go out machine and carry out melting mixing, melt temperature scope is 240-270 DEG C, and obtains the high-strength glass by being granulated processing method
Glass fiber reinforced polypropylene composite material.
Embodiment 4:
It is simple glass fiber by mass ratio:Alkali compounds (compares sodium carbonate by quality:Potassium carbonate=1:1 compounding):Two
Sub- (3,4- dimethyl) benzyl D-sorbite (DMDBS)=100:1.5:0.6 ratio weighs up, and is put into high mixer, is heated to
70 DEG C, 15 minutes modified glass-fibers up to area load nucleating agent are mixed.
By weight percentage, by acrylic resin 61.2%, compatilizer grafted maleic anhydride 7%, heat stabilizer is (by cup
Aromatic hydrocarbons type thermal stabilizing agent and dilauryl thiodipropionate=1:1) 0.7%, light stabilizer is (by 2- hydroxyl -4- n-octyloxies two
Benzophenone, 2- (two tertiary phenyl of 2- hydroxyls -3,5-) -5- chlorinations benzotriazole and single benzoic acid resorcinol=1:1:1)
0.6%, processing aid is (by sorbitan monostearate, glyceryl monostearate and magnesium stearate according to weight ratio 1:1:1
Carry out mixing compounding) 0.5% addition mixing apparatus in uniformly mixed, mixture is added from twin-screw extrusion owner's spout
Enter, glass fibre 30% made from above-mentioned modification be added from double screw extruder side spout, then by obtained mixture and
Glass fibre carries out melting mixing by double screw extruder, and melt temperature scope is 220-250 DEG C, and by being granulated processing side
Formula obtains the high strength glass fiber reinforced polypropylene compound material.
Comparative example 4
By weight percentage, by acrylic resin 61.2%, compatilizer grafted maleic anhydride 7%, heat stabilizer is (by cup
Aromatic hydrocarbons type thermal stabilizing agent and dilauryl thiodipropionate=1:1) 0.7%, light stabilizer is (by 2- hydroxyl -4- n-octyloxies two
Benzophenone, 2- (two tertiary phenyl of 2- hydroxyls -3,5-) -5- chlorinations benzotriazole and single benzoic acid resorcinol=1:1:1)
0.6%, processing aid is (by sorbitan monostearate, glyceryl monostearate and magnesium stearate according to weight ratio 1:1:1
Carry out mixing compounding) 0.5% addition mixing apparatus in uniformly mixed, mixture is added from twin-screw extrusion owner's spout
Enter, simple glass fiber 30% is added from double screw extruder side spout, then obtained mixture and glass fibre are led to
Cross double screw extruder and carry out melting mixing, melt temperature scope is 220-250 DEG C, and by be granulated processing method obtain it is described
High strength glass fiber reinforced polypropylene compound material.
PP composite material obtained by above-described embodiment 1-4 and comparative example 1-4 is molded into batten respectively, is then pressed
Its mechanical strength is tested respectively according to the testing standard of the industry, shown in table 1 specific as follows:
Table 1
From upper table 1 as it can be seen that high strength glass fiber reinforced polypropylene compound material phase obtained by 1-4 of the embodiment of the present invention
Than in traditional fiber glass reinforced polypropylene material, hence it is evident that have higher intensity and impact property.
This hair can be understood and applied the above description of the embodiments is intended to facilitate those skilled in the art
It is bright.Person skilled in the art obviously easily can make various modifications to these embodiments, and described herein
General Principle is applied in other embodiment without having to go through creative labor.Therefore, the present invention is not limited to implementations here
Example, those skilled in the art's announcement according to the present invention, improvement and modification made without departing from the scope of the present invention all should be
Within protection scope of the present invention.
Claims (9)
1. a kind of high strength glass fiber reinforced polypropylene compound material, it is characterised in that:By weight percentage by following components
It is prepared:
Acrylic resin 47-84.2%
Modified glass-fiber 10-40%
Compatilizer 5-10%
Stabilizer 0.4-1%
Light stabilizer 0.1-1%
Processing aid 0.3-1%;
The modified glass-fiber is the glass fibre of area load nucleating agent, by glass fibre, alkali compounds and nucleation
Agent is 100 in mass ratio:0.3-2:0.2-1 is mixed with.
2. a kind of high strength glass fiber reinforced polypropylene compound material according to claim 1, it is characterised in that:It is described
Alkali compounds be calcium carbonate, magnesium hydroxide, aluminium hydroxide, zinc hydroxide, sodium bicarbonate, sodium carbonate and potassium carbonate at least
It is a kind of.
3. a kind of high strength glass fiber reinforced polypropylene compound material according to claim 1, it is characterised in that:It is described
Nucleating agent is Sorbitol Nucleator;The compatilizer is maleic anhydride inoculated polypropylene.
4. a kind of high strength glass fiber reinforced polypropylene compound material according to claim 3, it is characterised in that:It is described
Sorbitol Nucleator is preferably two Asias(3,4- dimethyl)Benzyl D-sorbite.
5. a kind of high strength glass fiber reinforced polypropylene compound material according to claim 1, it is characterised in that:It is described
Stabilizer is selected from phenolic thermostabilizers, amine heat stabilizer, phosphite ester type thermal stabilizing agent, half Hinered phenols heat stabilizer, cup
At least one of aromatic hydrocarbons type thermal stabilizing agent and dilauryl thiodipropionate heat stabilizer;The light stabilizer is that ultraviolet light is steady
Determine agent.
6. a kind of high strength glass fiber reinforced polypropylene compound material according to claim 5, it is characterised in that:It is described
UV light stabilizing agent is preferably septichen phenyl ester, 2- (2- hydroxy-5-methyl bases phenyl) benzotriazole, 2,4- dihydroxy
Benzophenone, ESCALOL 567,2-hydroxy-4-n-octoxybenzophenone, 2- (two uncles of 2- hydroxyls -3,5-
Phenyl) at least one of -5- chlorinations benzotriazole and single benzoic acid resorcinol.
7. a kind of high strength glass fiber reinforced polypropylene compound material according to claim 1, it is characterised in that:It is described
Processing aid is low molecule esters processing aid, metal soap processing aid, the compound esters processing aid of stearic acid and amides
At least one of processing aid.
8. a kind of preparation method of high strength glass fiber reinforced polypropylene compound material as described in claim 1, feature
It is:It is first 100 in mass ratio by glass fibre, alkali compounds and nucleating agent:0.3-2:0.2-1 is put into high mixer, is added
Heat is to being stirred for the 5-30 minutes modified glass-fibers to get area load nucleating agent after 40-80 DEG C;Then by polypropylene tree
Fat, compatilizer, stabilizer, light stabilizer, processing aid are added in mixing apparatus are uniformly mixed according to the ratio;It will finally obtain
Mixture from twin-screw extrusion owner's spout be added, by modified glass-fiber from double screw extruder side spout be added,
Through melting mixing, it is granulated to obtain composite material.
9. preparation method according to claim 8, it is characterised in that:The melting temperature is 200-270 DEG C.