CN103569532A - Manufacture method for anti-counterfeiting ceramic wine bottles - Google Patents
Manufacture method for anti-counterfeiting ceramic wine bottles Download PDFInfo
- Publication number
- CN103569532A CN103569532A CN201210253883.8A CN201210253883A CN103569532A CN 103569532 A CN103569532 A CN 103569532A CN 201210253883 A CN201210253883 A CN 201210253883A CN 103569532 A CN103569532 A CN 103569532A
- Authority
- CN
- China
- Prior art keywords
- base substrate
- blank
- bottle
- mud
- carry out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A manufacture method for anti-counterfeiting ceramic wine bottles comprises preparation of blanks, wherein the blanks are composed of Guizhou soil, feldspar powder and Maji mud, and water is added in the blanks which are then subjected to ball milling in a ball mill; shaping, dual-layer bottlenecks are formed, and anti-counterfeiting wine bottle semi-finished products are manufactured; firing of the manufactured anti-counterfeiting wine bottle semi-finished products to be manufactured into finished products after natural cooing. Ingenious dual-layer bottleneck design is used, so that irreparable breakages can be produced at positions of the bottlenecks, and the anti-counterfeiting purpose that the wine bottles cannot be used repeatedly for wine filling and packaging is achieved.
Description
Technical field
The present invention relates to a kind of method for making of Anti-sham ceramic wine bottle.
Background technology
At present, famous brand of wine on market, the phenomenon that especially commodity such as white wine, foreign wine are imitated, palm off is more and more, tracing it to its cause, is exactly not adopt the false proof measure of actv., and the bottle of many famous brands of wine mostly adopts common bottle, open after use, bottle profile is excellent, after some unprincipled fellow reclaims used bottle, fill fake wine, Reseal, seeks exorbitant profit afterwards, leads consumers in general into a trap, urgent need is a kind of at present both can normally open use, can reach false proof bottle again.
Summary of the invention
The invention provides a kind of method for making of Anti-sham ceramic wine bottle, make the product after burning till there is double-layer mouth structure, its ectomesoderm mouth is two independent semiellipse ring bodies, two semiellipse ring bodies are connected into the oval ring-type of hollow by lining cement, when opening bottle, the fracture of this skin mouth meeting unrepairable, plays the not reproducible utilization of bottle, fills with the false proof object that wine encapsulates with this.
The present invention realizes like this, a kind of method for making of Anti-sham ceramic wine bottle, the preparation of blank: the source of blank and consist of (mass parts): adopt 5～10 parts of Guizhou clays, 70～90 parts of feldspar powders, 10～20 parts of clues mud, above-mentioned blank is added to 15～20 parts of water, in ball grinding mill, carry out ball milling 48 hours; When glaze fineness reaches 280 mesh sieves, carry out deironing, press filt and pugging, and add Water-Electrolyteization slurry, then carried out 180 mesh sieves, vacuum defoamation;
Moulding: get above-mentioned blank mud and the plaster mold preparing, carry out high-pressure slip-casting, after the demoulding, at 60～100 ℃, be dried 6～8 hours, carry out repaired biscuit after dry, bottle base substrate;
Bottle double welt moulding: get the above-mentioned blank mud preparing and bottleneck plaster mold and outer mouthful plaster mold, carry out high-pressure slip-casting, after the demoulding, at 60～100 ℃, be dried 6～8 hours, after dry, repair a die, bottleneck and outer mouthful of base substrate, bottleneck base substrate is connect to slurry mud by Leix powder not and bond to bottle base substrate port, a described outer mouthful base substrate is two independent semiellipse ring bodies, two semiellipse ring bodies connect the oval ring-type of the bonding one-tenth hollow of slurry mud by Leix powder not, a skin mouthful base substrate is socketed on to bottleneck base substrate peripheral, and with Leix powder not, connect slurry mud and bond to bottle base substrate end, so far false-proof wine bottle half-blank,
Fire: the above-mentioned false-proof wine bottle half-blank preparing high temperature at 1100～1300 ℃ is burnt till, and firing time is 6～8 hours, last naturally cooling after, finished product.
The invention has the beneficial effects as follows:
1, simple in structure, be beneficial to suitability for industrialized production;
2, by the outer layer body of bonding setting, by expansion damage, reach disposable and utilize false proofly, cost is low;
3, can be generalized on other bottles or container and apply.
The specific embodiment
In order to make object of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, the present invention is further elaborated.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
A kind of method for making of Anti-sham ceramic wine bottle, the preparation of blank: the source of blank and consist of (mass parts): adopt 5～10 parts of Guizhou clays, 70～90 parts of feldspar powders, 10～20 parts of clues mud, above-mentioned blank is added to 15～20 parts of water etc., in ball grinding mill, carry out ball milling 48 hours; When glaze fineness reaches 180 mesh sieves, carry out deironing, press filt and pugging, and add Water-Electrolyteization slurry, then carried out 180 mesh sieves, vacuum defoamation;
Moulding: get above-mentioned blank mud and the plaster mold preparing, carry out high-pressure slip-casting, after extrusion forming, the demoulding, at 60～100 ℃, be dried 6～8 hours, repair a die after dry, bottle base substrate;
Bottle double welt moulding: get the above-mentioned blank mud preparing and bottleneck plaster mold and outer mouthful plaster mold, carry out high-pressure slip-casting, after the demoulding, at 60～100 ℃, be dried 6～8 hours, after dry, repair a die, bottleneck and outer mouthful of base substrate, bottleneck base substrate is connect to slurry mud by Leix powder not and bond to bottle base substrate port, a described outer mouthful base substrate is two independent semiellipse ring bodies, two semiellipse ring bodies connect the oval ring-type of the bonding one-tenth hollow of slurry mud by Leix powder not, a skin mouthful base substrate is socketed on to bottleneck base substrate peripheral, and with Leix powder not, connect slurry mud and bond to bottle base substrate end, so far false-proof wine bottle half-blank,
Fire: the above-mentioned false-proof wine bottle half-blank preparing high temperature at 1100～1300 ℃ is burnt till, and firing time is 6～8 hours, last naturally cooling after, finished product.
When reality is used, this bottle can configure a bottle cap, and bottle cap place arranges opening device, makes outer mouthful can, in the fracture of abutting edge unrepairable, with this, play the not reproducible utilization of bottle, fill with the false proof object that wine encapsulates.
These are only preferred embodiment of the present invention, not in order to limit the present invention, all any modifications of doing within the spirit and principles in the present invention, be equal to and replace and improvement etc., within all should being included in protection scope of the present invention.
Claims (1)
1. the method for making of an Anti-sham ceramic wine bottle, it is characterized in that: the preparation of blank: the source of blank and consist of (mass parts): adopt 5～10 parts of Guizhou clays, 70～90 parts of feldspar powders, 10～20 parts of clues mud, above-mentioned blank is added to 15～20 parts of water, in ball grinding mill, carry out ball milling 48 hours; When glaze fineness reaches 280 mesh sieves, carry out deironing, press filt and pugging, and add Water-Electrolyteization slurry, then carried out 180 mesh sieves, vacuum defoamation;
Moulding: get above-mentioned blank mud and the plaster mold preparing, carry out high-pressure slip-casting, extrusion forming, after the demoulding, at 60～100 ℃, be dried 6～8 hours, carry out repaired biscuit after dry, bottle base substrate;
Bottle double welt moulding: get the above-mentioned blank mud preparing and bottleneck plaster mold and outer mouthful plaster mold, carry out high-pressure slip-casting, after the demoulding, at 60～100 ℃, be dried 6～8 hours, after dry, carry out repaired biscuit, bottleneck and outer mouthful of base substrate, bottleneck base substrate is connect to slurry mud by Leix powder not and bond to bottle base substrate port, a described outer mouthful base substrate is two independent semiellipse ring bodies, two semiellipse ring bodies connect the oval ring-type of the bonding one-tenth hollow of slurry mud by Leix powder not, a skin mouthful base substrate is socketed on to bottleneck base substrate peripheral, and with Leix powder not, connect slurry mud and bond to bottle base substrate end, so far false-proof wine bottle half-blank,
Fire: the above-mentioned false-proof wine bottle half-blank preparing high temperature at 1100～1300 ℃ is burnt till, and firing time is 6～8 hours, last naturally cooling after, finished product.