CN103555136A - 一种环氧浸渍漆及其制备方法 - Google Patents

一种环氧浸渍漆及其制备方法 Download PDF

Info

Publication number
CN103555136A
CN103555136A CN201310510097.6A CN201310510097A CN103555136A CN 103555136 A CN103555136 A CN 103555136A CN 201310510097 A CN201310510097 A CN 201310510097A CN 103555136 A CN103555136 A CN 103555136A
Authority
CN
China
Prior art keywords
parts
epoxy
silane
stirring reaction
morpholine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310510097.6A
Other languages
English (en)
Inventor
徐文利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Venfi Electric Technology Group Co Ltd
Original Assignee
Anhui Venfi Electric Technology Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Venfi Electric Technology Group Co Ltd filed Critical Anhui Venfi Electric Technology Group Co Ltd
Priority to CN201310510097.6A priority Critical patent/CN103555136A/zh
Publication of CN103555136A publication Critical patent/CN103555136A/zh
Pending legal-status Critical Current

Abstract

一种环氧浸渍漆及其制备方法，其特征在于由下列重量份的原料制成：环氧树脂（E-51）32-35、2-氨基-2-甲基-1-丙醇5-7、吗啉1-2、聚异丁烯4-6、间苯二甲胺2-3、顺丁烯二酸酐6-8、对苯醌1-2、甲基三氯硅烷3-5、丙烯腈2-3、脂肪醇聚氧乙烯醚磷酸酯1-2、乙烯基三(β-甲氧基乙氧基)硅烷3-5、过氧化甲乙酮1-2、二甲苯32-35、成膜剂4-5。本发明浸渍漆能耐高温、高湿，电绝缘性能好，机械强度高，改善了导热性，可长期工作200℃，短期220℃，满足了设计要求。

Description

一种环氧浸渍漆及其制备方法
技术领域
本发明属于绝缘材料领域，涉及一种浸渍漆，尤其是一种环氧浸渍漆及其制备方法。
背景技术
电机、变压器、导线等生产普遍采用压力浸渍工艺。将工件预烘去潮后冷却，置于真空环境中，排除内部的空气和挥发物，依靠真空中漆液重力、施加一定压力的作用，使漆液迅速渗透并充满绝缘结构内层。该工艺可获得连续致密、无针孔的漆膜。
现有的浸渍漆是由环氧树脂作为主体树脂、酸酐为固化剂。但是该体系固化产物的耐温等级和韧性不足，需要对环氧酸酐浸渍漆体系进行改性，是浸渍漆体系固化物同时满足耐温等级和机械性能的要求。
发明内容
本发明的目的是提供一种环氧浸渍漆及其制备方法。
本发明的技术方案如下：
一种环氧浸渍漆，其特征在于由下列重量份的原料制成：环氧树脂（E-51）32-35、2- 氨基-2- 甲基-1- 丙醇5-7、吗啉1-2、聚异丁烯4-6、间苯二甲胺2-3、顺丁烯二酸酐6-8、对苯醌1-2、甲基三氯硅烷3-5、丙烯腈2-3、脂肪醇聚氧乙烯醚磷酸酯1-2、乙烯基三(β-甲氧基乙氧基)硅烷3-5、过氧化甲乙酮1-2、二甲苯32-35、成膜剂4-5。
所述的成膜剂由下列重量份的原料制成：苯基三乙氧基硅烷1-2、苯胺甲基三乙氧基硅烷1-2、二茂铁2-3、氮化铝1-2、纳米凹凸棒土1-2、环氧大豆油4-5、吗啉1-2、聚异丁烯3-4；
制备方法是：将各物料混合，加热至105-110℃，搅拌反应2-3小时，研磨去渣得到。
所述的环氧浸渍漆的制备方法，其特征在于包括以下步骤：将吗啉、聚异丁烯、顺丁烯二酸酐、对苯醌、甲基三氯硅烷、丙烯腈、脂肪醇聚氧乙烯醚磷酸酯、二甲苯混合，加入过氧化甲乙酮搅拌反应2-3小时，加热至120-130℃，加入乙烯基三(β-甲氧基乙氧基)硅烷，搅拌反应40-50分钟，再加入其它剩余成分，搅拌反应2-3小时，即得。
本发明浸渍漆能耐高温、高湿，电绝缘性能好，机械强度高，改善了导热性，可长期工作200℃，短期220℃，满足了设计要求。
具体实施方式
一种环氧浸渍漆，由下列重量份的原料（公斤）制成：
环氧树脂（E-51）35、2- 氨基-2- 甲基-1- 丙醇7、吗啉2、聚异丁烯6、间苯二甲胺3、顺丁烯二酸酐8、对苯醌2、甲基三氯硅烷5、丙烯腈3、脂肪醇聚氧乙烯醚磷酸酯2、乙烯基三(β-甲氧基乙氧基)硅烷5、过氧化甲乙酮2、二甲苯35、成膜剂5。
所述的成膜剂由下列重量份的原料制成：苯基三乙氧基硅烷2、苯胺甲基三乙氧基硅烷2、二茂铁2、氮化铝1、纳米凹凸棒土2、环氧大豆油5、吗啉1、聚异丁烯4；
制备方法是：将各物料混合，加热至105-110℃，搅拌反应2-3小时，研磨去渣得到。
环氧浸渍漆的制备方法，包括以下步骤：将吗啉、聚异丁烯、顺丁烯二酸酐、对苯醌、甲基三氯硅烷、丙烯腈、脂肪醇聚氧乙烯醚磷酸酯、二甲苯混合，加入过氧化甲乙酮搅拌反应2-3小时，加热至120-130℃，加入乙烯基三(β-甲氧基乙氧基)硅烷，搅拌反应40-50分钟，再加入其它剩余成分，搅拌反应2-3小时，即得。
固化工艺：在110~150℃下烘制3-5 小时；
其固化后粘结强度大于25N，耐热等级为H 级，体积电阻率不低于1×1014Ω·m，表面电阻不低于1×1014Ω，浸水后体积电阻率不低于1×1012Ω·m，表面电阻不低于1×1012Ω。本发明浸渍漆能耐高温、高湿，电绝缘性能好，机械强度高，改善了导热性，可长期工作200℃，短期220℃，满足了设计要求。

Claims (2)

1.一种环氧浸渍漆，其特征在于由下列重量份的原料制成：环氧树脂（E-51）32-35、2- 氨基-2- 甲基-1- 丙醇5-7、吗啉1-2、聚异丁烯4-6、间苯二甲胺2-3、顺丁烯二酸酐6-8、对苯醌1-2、甲基三氯硅烷3-5、丙烯腈2-3、脂肪醇聚氧乙烯醚磷酸酯1-2、乙烯基三(β-甲氧基乙氧基)硅烷3-5、过氧化甲乙酮1-2、二甲苯32-35、成膜剂4-5；
所述的成膜剂由下列重量份的原料制成：苯基三乙氧基硅烷1-2、苯胺甲基三乙氧基硅烷1-2、二茂铁2-3、氮化铝1-2、纳米凹凸棒土1-2、环氧大豆油4-5、吗啉1-2、聚异丁烯3-4；制备方法是：将各物料混合，加热至105-110℃，搅拌反应2-3小时，研磨去渣得到。
2.根据权利要求1所述的环氧浸渍漆的制备方法，其特征在于包括以下步骤：将吗啉、聚异丁烯、顺丁烯二酸酐、对苯醌、甲基三氯硅烷、丙烯腈、脂肪醇聚氧乙烯醚磷酸酯、二甲苯混合，加入过氧化甲乙酮搅拌反应2-3小时，加热至120-130℃，加入乙烯基三(β-甲氧基乙氧基)硅烷，搅拌反应40-50分钟，再加入其它剩余成分，搅拌反应2-3小时，即得。
CN201310510097.6A 2013-10-25 2013-10-25 一种环氧浸渍漆及其制备方法 Pending CN103555136A (zh)