CN103555032A - 一种抗腐蚀涂料用纳米级碳酸钙的制备方法 - Google Patents

一种抗腐蚀涂料用纳米级碳酸钙的制备方法 Download PDF

Info

Publication number
CN103555032A
CN103555032A CN201310443508.4A CN201310443508A CN103555032A CN 103555032 A CN103555032 A CN 103555032A CN 201310443508 A CN201310443508 A CN 201310443508A CN 103555032 A CN103555032 A CN 103555032A
Authority
CN
China
Prior art keywords
calcium carbonate
parts
add
preparation
corrosive paints
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310443508.4A
Other languages
English (en)
Other versions
CN103555032B (zh
Inventor
王明竹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd
Original Assignee
ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd filed Critical ANHUI SHENGJIA COLOR PRINTING PACKING Co Ltd
Priority to CN201310443508.4A priority Critical patent/CN103555032B/zh
Publication of CN103555032A publication Critical patent/CN103555032A/zh
Application granted granted Critical
Publication of CN103555032B publication Critical patent/CN103555032B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗腐蚀涂料用纳米级碳酸钙的制备方法，制备方法包括以下步骤：（1）将100-120份轻质碳酸钙加入适量水，研磨成纳米浆料，于40-50℃下加入1-2份硅烷偶联剂KH580，搅拌30-50分钟后，再加入0.3-0.5份抗氧剂1076，1-2份抗氧剂BHT，搅拌10-20分钟后，过滤，干燥，磨粉；（2）将0.1-0.2份钼酸铵、1-2份甲基丙烯酸异丁酯，5-7份松香树脂，10-15份溶剂混匀，得改性液备用；（3）将步骤（1）所得粉体加入高速搅拌机中，保持温度在70-80℃，加入改性液，搅拌20-30分钟后，干燥，研磨成纳米粉末即得。

Description

一种抗腐蚀涂料用纳米级碳酸钙的制备方法
技术领域
本发明涉及涂料领域，确切地说是一种抗腐蚀涂料用纳米级碳酸钙的制备方法。
背景技术
现有的应用于涂料上面的碳酸钙功能单一，使用配置麻烦。
发明内容
本发明的目的。
上述目的通过以下方案实现：
    一种抗腐蚀涂料用纳米级碳酸钙的制备方法，其特征在于：制备方法包括以下步骤：
（1）将100-120份轻质碳酸钙加入适量水，研磨成纳米浆料，于40-50℃下加入1-2份硅烷偶联剂KH580，搅拌30-50分钟后，再加入0.3-0.5份抗氧剂1076，1-2份抗氧剂BHT，搅拌10-20分钟后，过滤，干燥，磨粉；
（2）将0.1-0.2份钼酸铵、1-2份甲基丙烯酸异丁酯，5-7份松香树脂，10-15份溶剂混匀，得改性液备用；
（3）将步骤（1）所得粉体加入高速搅拌机中，保持温度在70-80℃，加入改性液，搅拌20-30分钟后，干燥，研磨成纳米粉末即得。
    所述的一种抗腐蚀涂料用纳米级碳酸钙的制备方法，其特征在于：所述的溶剂指的是丙醇。
本发明的有益效果为：本发明经过处理后，表面具有很好的亲油疏水性，同时松香树脂具有形成包膜的作用，因此添加本发明的涂料具有防腐蚀的作用。
具体实施方式
 一种抗腐蚀涂料用纳米级碳酸钙的制备方法，制备方法包括以下步骤：
（1）将120份（kg)轻质碳酸钙加入适量水，研磨成纳米浆料，于45℃下加入1份硅烷偶联剂KH580，搅拌50分钟后，再加入0.5份抗氧剂1076，1.3份抗氧剂BHT，搅拌15分钟后，过滤，干燥，磨粉；
（2）将0.1份钼酸铵、2份甲基丙烯酸异丁酯，7份松香树脂，15份溶剂混匀，得改性液备用；
（3）将步骤（1）所得粉体加入高速搅拌机中，保持温度在80℃，加入改性液，搅拌30分钟后，干燥，研磨成纳米粉末即得。
添加本实施例所制得的涂料，耐盐雾实验结果为22天，耐盐水实验结果为29天，显著高于未添加本实施例的对比涂料的耐盐雾实验结果10天，耐盐水实验结果14天。

Claims (2)

1.一种抗腐蚀涂料用纳米级碳酸钙的制备方法，其特征在于：制备方法包括以下步骤：
（1）将100-120份轻质碳酸钙加入适量水，研磨成纳米浆料，于40-50℃下加入1-2份硅烷偶联剂KH580，搅拌30-50分钟后，再加入0.3-0.5份抗氧剂1076，1-2份抗氧剂BHT，搅拌10-20分钟后，过滤，干燥，磨粉；
（2）将0.1-0.2份钼酸铵、1-2份甲基丙烯酸异丁酯，5-7份松香树脂，10-15份溶剂混匀，得改性液备用；
（3）将步骤（1）所得粉体加入高速搅拌机中，保持温度在70-80℃，加入改性液，搅拌20-30分钟后，干燥，研磨成纳米粉末即得。
2.根据权利要求1所述的一种抗腐蚀涂料用纳米级碳酸钙的制备方法，其特征在于：所述的溶剂指的是丙醇。
CN201310443508.4A 2013-09-26 2013-09-26 一种抗腐蚀涂料用纳米级碳酸钙的制备方法 Expired - Fee Related CN103555032B (zh)