CN103554885A - 一种耐磨聚碳酸酯水杯壳体材料及其制备方法 - Google Patents
一种耐磨聚碳酸酯水杯壳体材料及其制备方法 Download PDFInfo
- Publication number
- CN103554885A CN103554885A CN201310510397.4A CN201310510397A CN103554885A CN 103554885 A CN103554885 A CN 103554885A CN 201310510397 A CN201310510397 A CN 201310510397A CN 103554885 A CN103554885 A CN 103554885A
- Authority
- CN
- China
- Prior art keywords
- parts
- polycarbonate
- antioxidant
- wear
- screw extruder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐磨聚碳酸酯水杯壳体材料，其特征在于，由下列重量份的原料制成：聚碳酸酯500-520、聚四氟乙烯24-28、抗氧剂10101-2、月桂酸钙3-4、硬脂酸2-3、氧化聚乙烯蜡10-12、钛白粉12-15、抗氧剂565 0.9-1.1、柠檬酸三丁酯4-5、聚异丁烯3-4、助剂10-12；本发明耐磨聚碳酸酯材料具有较好的耐磨性，摩擦系数低，强度高，抗冲击性好，使用温度范围广，成型收缩率低，成型稳定，表面光洁度好，成本低，适合大面积推广。
Description
技术领域
本发明涉及塑料领域，特别是一种耐磨聚碳酸酯水杯壳体材料及其制备方法。
背景技术
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，由于聚碳酸酯结构上的特殊性，现已成为五大工程塑料中增长速度最快的通用工程塑料。由于聚碳酸酯制品具有质量轻，抗冲击和透明性好，用热水和腐蚀性溶液洗涤处理时不变形且保持透明的优点，一些领域PC瓶已完全取代玻璃瓶。据预测，随着人们对饮用水质量重视程度的不断提高，聚碳酸酯在这方面的用量增长速度将保持在10%以上，因此研发一种聚碳酸酯材料的水杯壳体是大势所趋。
发明内容
本发明的目的是提供一种耐磨聚碳酸酯水杯壳体材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种耐磨聚碳酸酯水杯壳体材料，由下列重量份的原料制成：聚碳酸酯500-520、聚四氟乙烯24-28、抗氧剂1010 1-2、月桂酸钙3-4、硬脂酸2-3、氧化聚乙烯蜡10-12、钛白粉12-15、抗氧剂565 0.9-1.1、柠檬酸三丁酯4-5、聚异丁烯3-4、助剂10-12；
所述助剂由下列重量份的原料制成：硅藻土40-45、丙烯酸二甲基氨基乙酯4-5、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石4-5、3-氨丙基三甲氧基硅烷2-3、交联剂TAC1-2、葡萄糖酸锌1-2、硬脂酸锌1-2、玫瑰精油0.1-0.2；制备方法是将硅藻土、玉石混合放入煅烧炉中在710-740℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
本发明所述耐磨聚碳酸酯水杯壳体材料，由以下具体步骤制成：
（1）将聚四氟乙烯加热至熔融状态，加入抗氧剂1010、月桂酸钙、硬脂酸、氧化聚乙烯蜡、钛白粉、助剂，搅拌捏合15-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将干燥后的聚碳酸酯加热至235-275℃，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。
本发明具有以下优点：本发明耐磨聚碳酸酯材料具有较好的耐磨性，摩擦系数低，强度高，抗冲击性好，使用温度范围广，成型收缩率低，成型稳定，表面光洁度好，成本低，适合大面积推广。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种耐磨聚碳酸酯水杯壳体材料，由下列重量份（公斤）的原料制成：聚碳酸酯500、聚四氟乙烯24、抗氧剂1010 1、月桂酸钙3、硬脂酸2、氧化聚乙烯蜡10、钛白粉12、抗氧剂565 0.9、柠檬酸三丁酯4、聚异丁烯3、助剂10；
所述助剂由下列重量份（公斤）的原料制成：硅藻土40、丙烯酸二甲基氨基乙酯5、二缩三丙二醇二丙烯酸酯3、氧化锌5、玉石4、3-氨丙基三甲氧基硅烷2、交联剂TAC2、葡萄糖酸锌2、硬脂酸锌2、玫瑰精油0.1；制备方法是将硅藻土、玉石混合放入煅烧炉中在710-740℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
本发明所述耐磨聚碳酸酯水杯壳体材料，由以下具体步骤制成：
（1）将聚四氟乙烯加热至熔融状态，加入抗氧剂1010、月桂酸钙、硬脂酸、氧化聚乙烯蜡、钛白粉、助剂，搅拌捏合15-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将干燥后的聚碳酸酯加热至235-275℃，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。
本发明材料拉伸强度为50-55MPa, 伸长率10-15%，弯曲强度70-80MPA，缺口冲击强度370J/M。
Claims (2)
1.一种耐磨聚碳酸酯水杯壳体材料，其特征在于，由下列重量份的原料制成：聚碳酸酯500-520、聚四氟乙烯24-28、抗氧剂1010 1-2、月桂酸钙3-4、硬脂酸2-3、氧化聚乙烯蜡10-12、钛白粉12-15、抗氧剂565 0.9-1.1、柠檬酸三丁酯4-5、聚异丁烯3-4、助剂10-12；
所述助剂由下列重量份的原料制成：硅藻土40-45、丙烯酸二甲基氨基乙酯4-5、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石4-5、3-氨丙基三甲氧基硅烷2-3、交联剂TAC1-2、葡萄糖酸锌1-2、硬脂酸锌1-2、玫瑰精油0.1-0.2；制备方法是将硅藻土、玉石混合放入煅烧炉中在710-740℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
2.根据权利要求1所述耐磨聚碳酸酯水杯壳体材料，其特征在于，由以下具体步骤制成：
（1）将聚四氟乙烯加热至熔融状态，加入抗氧剂1010、月桂酸钙、硬脂酸、氧化聚乙烯蜡、钛白粉、助剂，搅拌捏合15-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将干燥后的聚碳酸酯加热至235-275℃，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。