CN103553481A - 一种防水型大理石胶 - Google Patents

一种防水型大理石胶 Download PDF

Info

Publication number
CN103553481A
CN103553481A CN201310470734.1A CN201310470734A CN103553481A CN 103553481 A CN103553481 A CN 103553481A CN 201310470734 A CN201310470734 A CN 201310470734A CN 103553481 A CN103553481 A CN 103553481A
Authority
CN
China
Prior art keywords
marble
waterproof
marble glue
waterproof type
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310470734.1A
Other languages
English (en)
Other versions
CN103553481B (zh
Inventor
刘绍贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Original Assignee
XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd filed Critical XIAMEN LIKASAM WATERPROOF ENGINEERING Co Ltd
Priority to CN201310470734.1A priority Critical patent/CN103553481B/zh
Publication of CN103553481A publication Critical patent/CN103553481A/zh
Application granted granted Critical
Publication of CN103553481B publication Critical patent/CN103553481B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种防水型大理石胶，它包含以下组分：硅酸盐水泥、石英砂、泛碱抑制剂、可再分散乳胶粉、甲酸钙、憎水剂、淀粉醚、纤维素醚以及减水剂。上述各个组分重量比为：硅酸盐水泥20～40；石英砂30～50；泛碱抑制剂0.5～1.5；可再分散乳胶粉10～20；甲酸钙0.25～0.75；憎水剂3～9；淀粉醚0.25～0.75；纤维素醚0.25～0.75；减水剂0.5～1.5.本发明克服了原有大理石胶不防水的缺陷，有很好的物理性能及防水性能。粘贴强度高，产品既可粘贴大理石、又能防水，用此材料粘贴大理石，能防止大理石吐碱、返黄、发白，无需做防水层，大大节省资源，减少综合造价。

Description

一种防水型大理石胶
技术领域
本发明涉及一种大理石胶，具体来说是一种防水型大理石胶，属于建筑材料技术领域。
背景技术
传统在墙壁上安装大理石的方法都是在墙壁上打上若干个孔，然后打入膨胀螺丝，随后在大理石上切上四个槽以锁住这些钢丝绳，再用钢丝绳把大理石与膨胀螺丝锁起来，加入填充料，随后再勾缝。但是在一段时间后，膨胀螺丝和钢丝绳容易老化或受腐蚀生锈，引起极大的安全隐患。尽管后来在中国专利申请201010505594.3公开一种装饰面大理石薄板与基材符合的胶粘剂及其制备方法，然而，它是一种装饰面大理石薄板与基材符合的胶粘剂及其制备方法。因大理石体重较重，其粘贴剂强度不够，容易脱落，并且，它无法将大理石粘贴墙面上。
后来，本申请人为了克服上述技术缺陷，提出了改进方案并获得了201110098659.1号中国发明专利。然而，在实践使用过程中，本申请人发现该技术方案所获得的大理石胶仍缺乏防水功能，用户需要在贴大理石的基层上做防水层，进而增加施工成本，并且，该产品的粘合强度还不够高，为了实现大理石胶的防水效果，进一步提高大理石胶的粘合强度，最大限度的避免粘合后5-20分钟内大理石下滑甚至脱落的现象，终而得本发明。
发明内容
本发明的目的在于提供一种防水型大理石胶，克服了原有贴大理石胶不防水的缺陷，有很好的物理性能、及防水性能。粘贴强度高，产品既可粘贴大理石、又能防水，用此材料粘贴大理石，能防止大理石吐碱、返黄、发白，减少做防水工序，大大节省资源，减少综合造价。
本发明的目的是通过以下技术方案来实现的：一种防水型大理石胶，其特征在于，它包含以下组分：硅酸盐水泥、石英砂、泛碱抑制剂、可再分散乳胶粉、甲酸钙、憎水剂、淀粉醚、纤维素醚以及减水剂。
在上述的技术方案中，还可以添加有填充料。
其中，上述的防水型大理石胶，其所述各个组分重量比为：
Figure BSA0000095986560000021
在具体实施例中，上述的组分的重量比多采用以下几种配比，分别是：
(1)该防水型大理石胶，其组分重量比为：
Figure BSA0000095986560000022
Figure BSA0000095986560000031
(2)该防水型大理石胶，其组分重量比为：
Figure BSA0000095986560000032
(3)该防水型大理石胶，其组分重量比为：
Figure BSA0000095986560000033
Figure BSA0000095986560000041
在上述组分的重量比情况下，可以添加重量比为0.25～0.75的填充料，其中，它用以调整产品的粘合强度。
具体来说，上述任一技术方案所述石英砂的颗粒大小为80～120目。
作为进一步细化，所述硅酸盐水泥为建筑材料内通用的普通硅酸盐42.5高标号水泥。
在发明技术方案中，硅酸盐水泥的作用是提高凝结的速度，石英砂则能增加产品强度；泛碱抑制剂则是用于防止大理石发黄、吐碱、返白；可再分散乳胶粉可使产品具有高粘结能力，甲酸钙可提前有效增强大理石胶的强度；憎水剂使得产品具有很好的防水效果；淀粉醚可防止贴大理石时下滑，增加粘结力，改变原有大理石胶的胶力不足的缺陷；纤维素醚用以增加大理石胶的粘稠度；减水剂有助于缩减产品的水量，增加产品的整体强度。
本发明所述的防水型大理石胶，它主要包含以下组分硅酸盐水泥、石英砂、泛碱抑制剂、可再分散乳胶粉、甲酸钙、憎水剂、淀粉醚、纤维素醚以及减水剂，以该组分制得的防水大理石胶，具有很好的防水性能，粘贴强度高，产品既可粘贴大理石，又能防水，用此材料粘贴大理石，无需做防水层，避免粘合后大理石5-20分钟内出现下滑甚至脱落的现象，也可减少做防水工序，大大节省资源，减少综合造价。
具体实施方式
下面结合实施例进一步描述本发明的技术方案，但要求保护的范围并不局限于所述。
实施例1
本实施例所述的防水型大理石胶，它由以下重量比的组分组成：
Figure BSA0000095986560000051
实施例2
本实施例所述的防水型大理石胶，它由以下重量比的组分组成：
Figure BSA0000095986560000061
实施例3
本实施例所述的防水型大理石胶，它由以下重量比的组分组成：
Figure BSA0000095986560000062
实施例4
本实施例所述的防水型大理石胶，它由以下重量比的组分组成：
Figure BSA0000095986560000063
Figure BSA0000095986560000071
实施例5
本实施例所述的防水型大理石胶，它由以下重量比的组分组成：
Figure BSA0000095986560000072
对以上各实施例制得的防水型大理石胶，对其进行性能检测，得下表：
检测项目 检测结果
拉伸强度/MPa 大于或等于2.4
晾置时间(20min) 大于或等于1.4
浸水后的拉伸胶粘强度(Mpa) 大于或等于2.4
热老化后的拉伸胶粘强度(Mpa) 大于或等于1.6
抗渗压力(28d Mpa) 大于或等于1.0
从以上实施例及上表得知，本发明所述的防水型大理石胶，成型产品与混凝土同寿命，具有很好的物理性能，防水性能好，粘贴强度高，产品既可粘贴大理石，又能防水，用此材料粘贴大理石，无需增加防水层，避免粘合后的大理石5-20分钟内出现下滑甚至脱落的现象，也可减少做防水工序，大大节省资源，减少综合造价。

Claims (9)

1.一种防水型大理石胶，其特征在于，它包含以下组分：硅酸盐水泥、石英砂、泛碱抑制剂、可再分散乳胶粉、甲酸钙、憎水剂、淀粉醚、纤维素醚以及减水剂。
2.根据权利要求1所述的防水型大理石胶，其特征在于：所述各个组分重量比为：
3.根据权利要求2所述的防水型大理石胶，其特征在于：它的组分重量比为：
Figure FSA0000095986550000012
Figure FSA0000095986550000021
4.根据权利要求2所述的防水型大理石胶，其特征在于：它的组分重量比为：
Figure FSA0000095986550000022
5.根据权利要求2所述的防水型大理石胶，其特征在于：它的组分重量比为：
Figure FSA0000095986550000023
Figure FSA0000095986550000031
6.根据权利要求1所述的防水型大理石胶，其特征在于：它还包含有填充料。
7.根据权利要求2至6任一权利要求所述的防水型大理石胶，其特征在于：它还包含有填充料，填充料的组分重量比为0.25～0.75。
8.根据权利要求1至6任一权利要求所述的防水型大理石胶，其特征在于：所述石英砂的颗粒大小为80～120目。
9.根据权利要求1至6任一权利要求所述的防水型大理石胶，其特征在于：所述硅酸盐水泥为普通硅酸盐42.5高标号水泥。
CN201310470734.1A 2013-10-11 2013-10-11 一种防水型大理石胶 Active CN103553481B (zh)