CN103540267A - Inorganic adhesive - Google Patents
Inorganic adhesive Download PDFInfo
- Publication number
- CN103540267A CN103540267A CN201310435870.7A CN201310435870A CN103540267A CN 103540267 A CN103540267 A CN 103540267A CN 201310435870 A CN201310435870 A CN 201310435870A CN 103540267 A CN103540267 A CN 103540267A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic adhesive
- adhesive
- adhesive joint
- strong
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an inorganic adhesive, comprising the following constituents in parts by weight: 20-35 parts of copper oxide powder, 10-15 parts of aluminum hydroxide, 1-3 parts of sodium tungstate, 1-3 parts of cobaltous oxide, 1-3 parts of zinc oxide and 10-15 parts of strong phosphoric acid. The inorganic adhesive has the advantages of having strong viscous force, being cured quickly, being resistant to high temperature of 1000 DEG C, and being widely used in adhesive joint of closed and semi-closed turning tools, adhesive joint of dies and adhesive joint of metals.
Description
Technical field
The present invention relates to a kind of formula of tackiness agent, specifically, relate to a kind of inorganic adhesive.
Background technology
Metal and the intermetallic mode being connected greatly mainly with welding, but the impact on metal nature for fear of welding in some cases, the mode that need to take glue to connect.Yet existing glue resistance to elevated temperatures is poor, is unsuitable for the metal sticking under hot environment.
Summary of the invention
The object of the present invention is to provide a kind of inorganic adhesive, the viscous force of this tackiness agent is strong, resistance to elevated temperatures good.
The object of the invention realizes by following technical proposals:
, in weight part, it comprises following component:
Further, a kind of inorganic adhesive, in weight part, it comprises following component:
Advantage of the present invention is: viscous force is strong, quick solidifying, can resistance to 1000 ℃ high temperature, be widely used in the splicing of sealing, semi-enclosed lathe tool, mould glueds joint and metal bonding.
Embodiment
Embodiment 1
, in weight part, it comprises following component: 20 parts of cupric oxide powders, 10 parts, aluminium hydroxide, 1 part of sodium wolframate, 1 part of cobalt oxide, 1 part, zinc oxide, 10 parts of strong phosphoric acid.
Embodiment 2
, in weight part, it comprises following component: 30 parts of cupric oxide powders, 12 parts, aluminium hydroxide, 2 parts of sodium wolframates, 2 parts of cobalt oxides, 2 parts, zinc oxide, 18 parts of strong phosphoric acid.
Embodiment 3
, in weight part, it comprises following component: 35 parts of cupric oxide powders, 15 parts, aluminium hydroxide, 3 parts of sodium wolframates, 3 parts of cobalt oxides, 3 parts, zinc oxide, 15 parts of strong phosphoric acid.
Claims (2)