CN103540246A - 一种免清洗uv固化保形涂料 - Google Patents
一种免清洗uv固化保形涂料 Download PDFInfo
- Publication number
- CN103540246A CN103540246A CN201310485621.9A CN201310485621A CN103540246A CN 103540246 A CN103540246 A CN 103540246A CN 201310485621 A CN201310485621 A CN 201310485621A CN 103540246 A CN103540246 A CN 103540246A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylate
- conformal coating
- clean
- exempts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种免清洗UV固化保形涂料,为以下重量份原料的组合物:丙烯酸酯2份~75份、改性的松香丙烯酸酯1份~15份、活性稀释剂30份~70份、光引发剂0.2份~l5份。与现有技术相比,本发明的有益效果是:成膜后表面电阻较高、冲击强度大、柔韧性好、附着力强、无需进行原材料预聚,工艺简单。
Description
技术领域
本发明涉及一种涂料,尤其是涉及一种免清洗紫外线固化保形涂料。
背景技术
涂敷在已焊插接元件的印刷线路板上的保护性涂料通常称为保形涂料(conformal coating)。它既能使电子产品免受外界有害环境的侵蚀,如尘埃、潮气、化学药品、霉菌的腐蚀作用以及外物刮损、短路等人为操作错误,又可延长电子器件的寿命,提高使用的稳定性从而使电子产品的性能得到改善。
保形涂料的固化方式分为光固化、热固化、潮气固化、电固化和空气固化。光固化型的保形涂料具有固化速度快、适用于热敏性的底材、初始投资低、低挥发性溶剂含量、节省空间等优点。采用光固化保形涂料,可大大提高线路板的涂装生产效率,而且也便于对线路板进行修复和局部快速涂敷保护。但现在的PCB板上的阻焊剂材料对保形涂料的兼容性越来越差,需要对阻焊剂材料进行清洗后才能涂覆,否则固化过程中容易发生脱落,产生气泡等问题,严重影响了保形涂料的效果及性能,若能提高保形涂料与阻焊剂的相容性,即无需进行清洗便可进行涂覆,不仅简化生产工艺、降低生产成本、改善了涂覆的表干效果,而且提高了保形涂层的保护性能,可适用于各种线路板的涂敷保护。
公开号为103254405A的中国发明专利《松香基环氧丙烯酸酯预聚物及其合成方法和用途》公开了松香基环氧改性丙烯酸酯预聚物在制备 UV固化涂料上的应用,并公开一个具体的配方:
并进一步公开了活性稀释剂为甲基丙烯酸 -β- 羟乙酯 (HEMA)、异冰片基丙烯酸酯,β- 羧乙基丙烯酸酯、2- 苯氧基乙基丙烯酸酯、6 一己二醇双丙烯酸酯、二缩丙二醇双丙烯酸酯或三缩丙二醇双丙烯酸酯 ;光引发剂为 2- 羟基 -2- 甲基 -1- 苯基丙酮、1- 羟基环己基苯基甲酮、2- 甲基 -2-(4- 吗啉基 -1-[4-(甲硫基)苯基 ]-1- 丙酮、安息香双甲醚或二苯甲酮 ;其它助剂为流平剂,流平剂为聚二甲基硅氧烷、聚甲基苯基硅氧烷或有机硅改性聚硅氧烷。
但该涂料使用单一的松香基环氧丙烯酸酯预聚物作为主剂,反应而得的涂料需要首先制备预聚物,工艺较为复杂。
发明内容
本发明的目的正是要解决现有技术存在的前述技术问题,提供一种免清洗uv固化保形涂料及其制备方法。
为实现上述目的,本发明提供的技术方案如下:这种免清洗uv固化保形涂包含改性的松香丙烯酸酯作为涂料的树脂类组分,改性的松香丙烯酸酯分子中所含的(甲基)丙烯酰氧基的碳碳双键在光引发剂的作用下进行光固化反应。松香丙烯酸酯中的松香部分可以与多种助焊剂兼容很好的附着在基材的表面,形成性能符合要求的保护干膜。
具体而言,这一种免清洗uv固化保形涂料由以下重量份原料组合而成:丙烯酸酯20份~75份、改性的松香丙烯酸酯1份~15份、活性稀释剂30份~70份、光引发剂0.2份~l5份。
进一步,所述免清洗uv固化保形涂料还添加涂料助剂0.01份~0.05份。
进一步,所述改性的松香丙烯酸酯,包括环氧改性的松香环氧丙烯酸酯以及其他改性的松香丙烯酸酯,如日本荒川化学松香环氧丙烯酸酯101;松香丙烯酸酯在涂料中的用量优选为3份~7份。
进一步,所述丙烯酸树树脂,有环氧(甲基)丙烯酸酯类、聚氨酯(甲基)丙烯酸酯类、聚酯丙烯酸酯、脂肪族丙烯酸酯类、有机硅丙烯酯类以及其他改性丙烯树脂;所述丙烯酸树脂的用量优选为30份~65份。
进一步,所述活性稀释剂含有碳碳双键,可用的活性稀释剂有(甲基)丙烯酸酯、N-乙烯基吡咯烷酮、N-乙烯基己内酰胺、苯乙烯及其衍生物、乙烯基醚等。其中效果较好的是(甲基)丙烯酸酯,而乙烯基醚可作为辅助的活性稀释剂,除了可显著降低粘度外,还能对暗固化有促进作用。N-乙烯基吡咯烷酮因怀疑毒性而很少采用了;苯乙烯及其衍生物也是因为毒性和刺激性气味而很少采用;所述活性稀释剂的优选的用量为40份~60份。
进一步,所述光引发剂为用于光引发自由基聚合的光引发剂,典型的光引发剂如Ciba公司的IRGACURE-184、IRGACURE 651、DAROCUR1173等;所述光引发剂优选的用量为1份~5份。
进一步,所述的涂料助剂为流平剂、消泡剂和/或偶联剂。
本发明上述的免清洗uv固化保形涂料,光固化的条件可以是可见光或紫外光,以紫外光较好。固化光源为可发出包含可见光或/和紫外光波长光波的光源,如中压汞灯、低压汞灯、高压汞灯、无极灯、氙灯、金属卤化物灯等,也可以使用太阳光照射固化。固化时间一般为0.5~1800秒,视所用光源种类和强度而定。优选的固化时间为5~60秒。
与现有技术相比,本发明的有益效果是:成膜后表面电阻较高、冲击强度大、柔韧性好、附着力强、无需进行原材料预聚,工艺简单。
具体实施方式
通过下表1所述各组分形成对比例和实施例1-8对本发明的免清洗uv固化保形涂料作进一步说明,其中所述的原料配比均为重量比。
表1
对比例 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | 实施例7 | 实施例8 | |
聚氨酯丙烯酸酯CN981 | 95 | 20 | 15 | 75 | |||||
聚酯丙烯酸酯CN146 | 49 | 45 | 25 | 24 | |||||
改性环氧丙烯酸酯CN115 | 40 | 44 | 35 | 27 | |||||
稀释剂丙烯酸异冰片酯IBOA | 20 | 25 | 11 | 46 | 30 | 32 | 20 | ||
丙烯酸四氢呋喃酯SR285 | 50 | 20 | 20 | 30 | 24 | 20 | 14 | ||
2-苯氧基乙基丙烯酸酯SR339 | 16 | 23 | 16 | 15 | 24 | 10 | |||
松香环氧丙烯酸酯101 | 1 | 3 | 5 | 6 | 7 | 9 | 11 | 15 | |
光引发剂IRGACURE-184 | 0.05 | 0.1 | 2 | 3 | 2 | 5 | 14 | 10 | 10 |
光引发剂2,4,6-三甲基苯甲酰基-二苯基氧化膦 | 0.2 | 3 | 1 | 2 | 1 | 2 | |||
流平剂BYK333 | 0.02 | 0.02 | 0.005 | 0.01 | 0.01 | 0.01 | |||
流平剂920 | 0.03 | 0.04 | 0.005 | 0.02 | 0.01 | ||||
荧光增白剂2.5-双(5-叔丁基-2-苯并噁唑基)噻吩 OB | 0.001 | 0.01 | 0.01 | 0.01 |
表2对比例及实施例1-8所得涂料的固化膜性能测试所采用的方法
测试性能 | 测试方法 |
铅笔硬度 | GB/T1730-93 |
附着力 | GB 1720-79 |
冲击强度 | GB/T1732-93 |
柔韧性 | GB/T1731-93 |
对比例及实施例1-8所得涂料的固化膜物理机械性能测试结果
从上表可以看出,实施例1-8在表面电阻、冲击强度、柔韧性、附着力等方面的性能参数均优于对比例。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (7)
1.一种免清洗UV固化保形涂料,为以下重量份原料的组合物:丙烯酸酯2份~75份、改性松香丙烯酸酯1份~15份、活性稀释剂30份~70份、光引发剂0.2份~l5份。
2.权利要求1的一种免清洗UV固化保形涂料,还添加0.01份~0.05份的涂料助剂。
3.权利要求1的一种免清洗UV固化保形涂料,所述改性松香丙烯酸酯为环氧改性的松香环氧丙烯酸酯;所述改性松香丙烯酸酯为3份~7份。
4.权利要求1的一种免清洗UV固化保形涂料,所述丙烯酸脂包括环氧(甲基)丙烯酸酯类、聚氨酯(甲基)丙烯酸酯类、聚酯丙烯酸酯类,脂肪族丙烯酸酯类,有机硅丙烯酯类;所述丙烯酸脂为30份~65份。
5.权利要求1的一种免清洗UV固化保形涂料,所述活性稀释剂含有碳碳双键,包括(甲基)丙烯酸酯、乙烯基醚;所述活性稀释剂为40份~60份。
6.权利要求1的一种免清洗UV固化保形涂料,所述光引发剂包括Ciba公司的IRGACURE-184、IRGACURE 651、DAROCUR1173;所述光引发剂的用量为1份~5份。
7.权利要求1的一种免清洗UV固化保形涂料,所述的涂料助剂为流平剂、消泡剂和/或偶联剂。