CN103540177A - Epoxy micaceous iron ash primer - Google Patents
Epoxy micaceous iron ash primer Download PDFInfo
- Publication number
- CN103540177A CN103540177A CN201310468766.8A CN201310468766A CN103540177A CN 103540177 A CN103540177 A CN 103540177A CN 201310468766 A CN201310468766 A CN 201310468766A CN 103540177 A CN103540177 A CN 103540177A
- Authority
- CN
- China
- Prior art keywords
- parts
- micaceous iron
- agent
- epoxy micaceous
- priming paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of oil paints, in particular to an epoxy micaceous iron ash primer. The epoxy micaceous iron ash primer comprises the following components in parts by weight: 20-30 parts of epoxy resin, 20-25 parts of acrylic resin, 10-15 parts of mica iron oxide, 2-5 parts of curing agent, 2-4 parts of acrylic acid, 0.2-0.8 part of dispersing agent, 0.2-0.5 part of wetting agent, 20-25 parts of diluent and 0.08-0.12 part of anti-settling agent. The technical scheme provided by the invention has the following beneficial effects: organic modified bentonite is added in the epoxy micaceous iron ash primer so that the leveling property of a coating is good without sagging, and the settling time of the pigments is prolonged; furthermore, the epoxy micaceous iron ash primer provided by the invention hardly falls off, can be quickly dried, has strong impact force resistance, excellent adhesive force, flexibility, water resistance and excellent anti-rust performance, is environment-friendly, and has no harm to a human body in construction.
Description
Technical field
The present invention relates to paint technology field, particularly a kind of epoxy micaceous iron ash priming paint.
Background technology
Priming paint is the first layer of paint system, is to be directly coated onto body surface as the coating of finish paint solid foundation.For improving the sticking power of finish paint, increase finish paint fullness ratio, alkali-resistivity is provided, anti-corrosion function etc. is provided, priming paint lays particular emphasis on and improves sticking power, anti-corrosion function, alkali-resistivity etc., can guarantee the even absorption of finish paint, make paint system performance best effect simultaneously.Requirement is adhere firmly on object plane, to increase the sticking power of upper coating, improves the ornamental of finish paint.According to coating specification, can be divided into priming coat, surfacer etc.
Existing epoxy micaceous iron ash priming paint is difficult for being attached to smooth plane, easily occurs the phenomenon that comes off, had a strong impact on quality and the outward appearance of product, and rate of drying is slow, and production efficiency is low; Meanwhile, impact resistance, hiding rare, hardness and glossiness etc. are all poor.
Summary of the invention
The object of the invention is: overcome the technical deficiency that the ash of epoxy micaceous iron in prior art priming paint easily comes off, rate of drying is low, a kind of difficult drop-off, rate of drying is fast, impact resistance is strong epoxy micaceous iron ash priming paint are provided.
To achieve these goals, the technical solution used in the present invention is as follows:
An ash priming paint, its mass parts is composed as follows: 20～30 parts of epoxy resin, 20～25 parts of acrylic resins, 10～15 parts of iron micas, 2～5 parts, solidifying agent, 2～4 parts, vinylformic acid, 0.2～0.8 part of dispersion agent, 0.2～0.5 part of wetting agent, 20～25 parts of thinners, 0.08～0.12 part of anti-settling agent.
Further, described solidifying agent is selected from: at least one in aminoethyl piperazine, diethyl amino propylamine, trimethylhexamethylenediamine, hexanediamine modifier.
Further, described dispersion agent is selected from: at least one in triethyl hexyl phosphoric acid, sodium lauryl sulphate, methyl amyl alcohol, derivatived cellulose, polyacrylamide, fatty acid polyglycol ester.
Further, described wetting agent is selected from: at least one in sulphonated oil, soybean lecithin, propylene glycol, polyoxyethylene surfactant.
Further, the mass parts of described thinner consists of: 50 parts of dimethylbenzene, 10 parts of pimelinketone, 40 parts of isobutyl acetates.
Further, described anti-settling agent is selected from: at least one in the N-Methyl pyrrolidone solution of organic bentonite, aerosil, modification polyureas.
Further, described anti-settling agent is the N-Methyl pyrrolidone solution of modification polyureas.
Further, an ash priming paint, its mass parts is composed as follows: 25 parts of epoxy resin, 22 parts of acrylic resins, 12 parts of iron micas, 3.5 parts, solidifying agent, 3 parts, vinylformic acid, 0.5 part of dispersion agent, 0.3 part of wetting agent, 22.5 parts of thinners, 0.1 part of anti-settling agent.
In the present invention, adding organic modified bentonite object is: organic bentonite is that to take natural montmorillonite be mainly that hectorite is raw material, reacts and forms with salt (as quaternary ammonium salt).Aspect coating, organobentonite is generally as anti-settling agent, thickening material use, and its mechanism that prevents precipitation is the rheological property of change system, makes it have thixotropy, thereby prevents color stuffing sedimentation.
The present invention adopts the object of the N-Methyl pyrrolidone solution of modification polyureas to be: it is by incompatible selectively with coating system, under suitable stirring velocity, produce tiny, needle crystal, by the linkage force between crystallization, form tridimensional network, thereby for system provides stronger thixotropy, also just provide superior anti-settling, sag prevention performance.When coating is stored, the N-Methyl pyrrolidone soln using tridimensional network of modification polyureas is held each pigment component, effectively prevents the sedimentation of face, filler, and viscosity rises simultaneously.
Adopt the beneficial effect of technical scheme of the present invention to be: in the present invention, to add organic bentonite, coating leveling is good, no sag phenomenon, and extended settling time of pigment, and priming paint tool difficult drop-off of the present invention, rate of drying is fast, impact resistance is strong, have good sticking power, snappiness, water resistance and good rustless property, environmental protection, constructs to human body without injury.
Embodiment
According to specific embodiment, the present invention will be further described below.
Embodiment 1
A kind of epoxy micaceous iron ash priming paint, its mass parts is composed as follows: 20 parts of epoxy resin, 20 parts of acrylic resins, 10 parts of iron micas, 2 parts of aminoethyl piperazines, 2 parts, vinylformic acid, 0.2 part of polyacrylamide, fatty acid polyglycol ester, 0.2 part of polyoxyethylene surfactant, 20 parts of thinners, 0.08 part of organic bentonite.
The mass parts of the thinner in the present invention consists of: 50 parts of dimethylbenzene, 10 parts of pimelinketone, 40 parts of isobutyl acetates.
In the present invention, added organic bentonite, coating leveling is good, no sag phenomenon, and extended settling time of pigment.
The cithrol that the present invention adds is soluble in oil and organic solvent, has good level and smooth, emulsifying effect, further like this snappiness, sticking power and the impact resistance that improves epoxy micaceous iron ash priming paint.
Embodiment 2
A kind of epoxy micaceous iron ash priming paint, its mass parts is composed as follows: 25 parts of epoxy resin, 22 parts of acrylic resins, 12 parts of mica oxidations, 3.5 parts of diethyl amino propylamines, 3 parts, vinylformic acid, 0.5 part of methyl amyl alcohol, derivatived cellulose, fatty acid polyglycol ester, 0.3 part of soybean lecithin, propylene glycol, 22.5 parts of thinners, 0.1 part of the N-Methyl pyrrolidone solution of modification polyureas.
The mass parts of the thinner in the present invention consists of: 50 parts of dimethylbenzene, 10 parts of pimelinketone, 40 parts of isobutyl acetates.
The N-Methyl pyrrolidone solution of the modification polyureas adding in the present invention, by incompatible selectively with paint base system, under suitable stirring velocity, produce tiny, needle crystal, by the linkage force between crystallization, form tridimensional network, thereby for system provides stronger thixotropy, also just provide superior anti-settling, sag prevention performance.When priming paint is stored, the N-Methyl pyrrolidone soln using tridimensional network of modification polyureas is held each pigment component, effectively prevents the sedimentation of face, filler, and viscosity rises simultaneously.
The present embodiment is preferred forms.
Embodiment 3
A kind of epoxy micaceous iron ash priming paint, its mass parts is composed as follows: 30 parts of epoxy resin, 25 parts of acrylic resins, 15 parts of iron micas, 5 parts of trimethylhexamethylenediamine, hexanediamine modifiers, 4 parts, vinylformic acid, 0.8 part of derivatived cellulose, polyacrylamide, fatty acid polyglycol ester, 0.5 part of sulphonated oil, propylene glycol, 25 parts of thinners, 0.12 part of organic bentonite.
The mass parts of the thinner in the present invention consists of: 50 parts of dimethylbenzene, 10 parts of pimelinketone, 40 parts of isobutyl acetates.
Although above-described embodiment describes in detail technical scheme of the present invention, but technical scheme of the present invention is not limited to above embodiment, in the situation that not departing from thought of the present invention and aim, any change that technical scheme of the present invention is done all will fall into claims limited range of the present invention.
Claims (8)
1. epoxy micaceous iron ash priming paint, it is characterized in that, its mass parts is composed as follows: 20～30 parts of epoxy resin, 20～25 parts of acrylic resins, 10～15 parts of iron micas, 2～5 parts, solidifying agent, 2～4 parts, vinylformic acid, 0.2～0.8 part of dispersion agent, 0.2～0.5 part of wetting agent, 20～25 parts of thinners, 0.08～0.12 part of anti-settling agent.
2. a kind of epoxy micaceous iron ash priming paint according to claim 1, is characterized in that, described solidifying agent is selected from: at least one in aminoethyl piperazine, diethyl amino propylamine, trimethylhexamethylenediamine, hexanediamine modifier.
3. a kind of epoxy micaceous iron ash priming paint according to claim 1, it is characterized in that, described dispersion agent is selected from: at least one in triethyl hexyl phosphoric acid, sodium lauryl sulphate, methyl amyl alcohol, derivatived cellulose, polyacrylamide, fatty acid polyglycol ester.
4. a kind of epoxy micaceous iron ash priming paint according to claim 1, is characterized in that, described wetting agent is selected from: at least one in sulphonated oil, soybean lecithin, propylene glycol, polyoxyethylene surfactant.
5. a kind of epoxy micaceous iron ash priming paint according to claim 1, is characterized in that, the mass parts of described thinner consists of: 50 parts of dimethylbenzene, 10 parts of pimelinketone, 40 parts of isobutyl acetates.
6. a kind of epoxy micaceous iron ash priming paint according to claim 1, is characterized in that, described anti-settling agent is selected from: at least one in the N-Methyl pyrrolidone solution of organic bentonite, aerosil, modification polyureas.
7. a kind of epoxy micaceous iron ash priming paint according to claim 1, is characterized in that, described anti-settling agent is the N-Methyl pyrrolidone solution of modification polyureas.
8. a kind of epoxy micaceous iron ash priming paint according to claim 1, it is characterized in that, its mass parts is composed as follows: 25 parts of epoxy resin, 22 parts of acrylic resins, 12 parts of iron micas, 3.5 parts, solidifying agent, 3 parts, vinylformic acid, 0.5 part of dispersion agent, 0.3 part of wetting agent, 22.5 parts of thinners, 0.1 part of anti-settling agent.