CN103539992B - 一种氯丁橡胶电缆护套料及其制备方法 - Google Patents

一种氯丁橡胶电缆护套料及其制备方法 Download PDF

Info

Publication number
CN103539992B
CN103539992B CN201310457991.1A CN201310457991A CN103539992B CN 103539992 B CN103539992 B CN 103539992B CN 201310457991 A CN201310457991 A CN 201310457991A CN 103539992 B CN103539992 B CN 103539992B
Authority
CN
China
Prior art keywords
cable sheath
chloroprene rubber
sheath material
preparation
ptfe micropowder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310457991.1A
Other languages
English (en)
Other versions
CN103539992A (zh
Inventor
毛方忠
吕红军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Ming Dou Electric Power Cable Co Ltd
Original Assignee
Anhui Ming Dou Electric Power Cable Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Ming Dou Electric Power Cable Co Ltd filed Critical Anhui Ming Dou Electric Power Cable Co Ltd
Priority to CN201310457991.1A priority Critical patent/CN103539992B/zh
Publication of CN103539992A publication Critical patent/CN103539992A/zh
Application granted granted Critical
Publication of CN103539992B publication Critical patent/CN103539992B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种氯丁橡胶电缆护套料及其制备方法，其组成原料为：氯丁橡胶、氮化铝粉、改性玻璃纤维、纳米混凝土渣粉末、聚四氟乙烯微粉、促进剂DTDM、防老剂MB、过氧化二异丙苯、双巯基乙酸异辛酯二正辛基锡、2,6-二叔丁基-4-甲基苯酚、硬酯酸单甘油酯和甲基丙烯酸正丁酯；本发明采用氯丁橡胶作为主料，电缆护套的拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率和冲击脆化温度同时具有优异的性能，而且通过对补强剂玻璃纤维的微波和超声波改性处理，可以大大改善电缆护套料的强度，并采用聚四氟乙烯微粉为阻燃剂，阻燃效果明显。

Description

一种氯丁橡胶电缆护套料及其制备方法
技术领域
本发明涉及一种氯丁橡胶电缆护套料及其制备方法，属于电缆护套料制造领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，对电缆护套料的质量要求日益增加，本发明提供一种氯丁橡胶电缆护套料及其制备方法。
发明内容
本发明的目的在于提供一种氯丁橡胶电缆护套料及其制备方法。
为了实现上述目的，本发明采用如下技术方案：
氯丁橡胶电缆护套料，其组成原料的重量份为：氯丁橡胶58-65、氮化铝粉25-30、改性玻璃纤维2.7-3.3、纳米混凝土渣粉末23-28、聚四氟乙烯微粉7.0-9.0、促进剂DTDM1.5-1.7、防老剂MB1.3-1.8、过氧化二异丙苯3.0-4.0、双巯基乙酸异辛酯二正辛基锡2.5-3.5、2,6-二叔丁基-4-甲基苯酚0.8-1.2、硬酯酸单甘油酯0.4-0.6和甲基丙烯酸正丁酯0.2-0.4。
氯丁橡胶电缆护套料，其组成原料的重量份为：氯丁橡胶62、氮化铝粉28、改性玻璃纤维3.0、纳米混凝土渣粉末25、聚四氟乙烯微粉8.0、促进剂DTDM1.6、防老剂MB1.5、过氧化二异丙苯3.5、双巯基乙酸异辛酯二正辛基锡3.0、2,6-二叔丁基-4-甲基苯酚1.0、硬酯酸单甘油酯0.5和甲基丙烯酸正丁酯0.3。
氯丁橡胶电缆护套料的制备方法，包括以下步骤：
（1）制备：将玻璃纤维放入大豆油中，取出沥干即得；
（2）按组成原料的重量份称取步骤（1）的改性玻璃纤维和其他剩余各原料，在110-125℃温度下在密炼后6-8分钟后，然后包辊，包辊温度为55-65℃。
本发明的有益效果：
本发明采用氯丁橡胶作为主料，电缆护套的拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率和冲击脆化温度同时具有优异的性能，而且通过对补强剂玻璃纤维的改性处理，可以大大改善电缆护套料的强度，并采用聚四氟乙烯微粉为阻燃剂，阻燃效果明显。
具体实施方式
实施例1：氯丁橡胶电缆护套料，其组成原料的重量份（kg）为：氯丁橡胶62、氮化铝粉28、改性玻璃纤维3.0、纳米混凝土渣粉末25、聚四氟乙烯微粉8.0、促进剂DTDM1.6、防老剂MB1.5、过氧化二异丙苯3.5、双巯基乙酸异辛酯二正辛基锡3.0、2,6-二叔丁基-4-甲基苯酚1.0、硬酯酸单甘油酯0.5和甲基丙烯酸正丁酯0.3。
氯丁橡胶电缆护套料的制备方法，包括以下步骤：
（1）制备：将玻璃纤维放入大豆油中，取出沥干即得；
（2）按组成原料的重量份称取步骤（1）的改性玻璃纤维和其他剩余各原料，在118℃温度下在密炼后7分钟后，然后包辊，包辊温度为60℃。
通过本发明的实施例1制得的电缆料性能数据：
拉伸强度为17.5-19.6Mpa，断裂伸出率为685-728%，老化后拉伸强度保持率（120℃，96h）88.2%，老化后断裂伸出保持率（120℃，96h）80.2%，冲击脆化温度-45℃--60℃；单根垂直燃烧试验，续燃时间为6.5-8.0秒，烧焦端距上夹具下缘距离为275-310毫米；成束燃烧试验，炭化长度为0.7-1.1米。

Claims (2)

1.一种氯丁橡胶电缆护套料，其特征在于其组成原料的重量份为：氯丁橡胶58-65、氮化铝粉25-30、改性玻璃纤维2.7-3.3、纳米混凝土渣粉末23-28、聚四氟乙烯微粉7.0-9.0、促进剂DTDM1.5-1.7、防老剂MB1.3-1.8、过氧化二异丙苯3.0-4.0、双巯基乙酸异辛酯二正辛基锡2.5-3.5、2,6-二叔丁基-4-甲基苯酚0.8-1.2、硬脂酸单甘油酯0.4-0.6和甲基丙烯酸正丁酯0.2-0.4；
所述的氯丁橡胶电缆护套料的制备方法，包括以下步骤：
（1）制备：将玻璃纤维放入大豆油中，取出沥干即得；
（2）按组成原料的重量份称取步骤（1）的改性玻璃纤维和其他剩余各原料，在110-125℃温度下密炼6-8分钟，然后包辊，包辊温度为55-65℃。
2.根据权利要求1所述的氯丁橡胶电缆护套料，其特征在于其组成原料的重量份为：氯丁橡胶62、氮化铝粉28、改性玻璃纤维3.0、纳米混凝土渣粉末25、聚四氟乙烯微粉8.0、促进剂DTDM1.6、防老剂MB1.5、过氧化二异丙苯3.5、双巯基乙酸异辛酯二正辛基锡3.0、2,6-二叔丁基-4-甲基苯酚1.0、硬脂酸单甘油酯0.5和甲基丙烯酸正丁酯0.3。
CN201310457991.1A 2013-09-30 2013-09-30 一种氯丁橡胶电缆护套料及其制备方法 Expired - Fee Related CN103539992B (zh)