CN103526585A - 一种耐高温涂料印花粘合剂及其制备方法 - Google Patents
一种耐高温涂料印花粘合剂及其制备方法 Download PDFInfo
- Publication number
- CN103526585A CN103526585A CN201310501952.7A CN201310501952A CN103526585A CN 103526585 A CN103526585 A CN 103526585A CN 201310501952 A CN201310501952 A CN 201310501952A CN 103526585 A CN103526585 A CN 103526585A
- Authority
- CN
- China
- Prior art keywords
- parts
- endurance
- binding agent
- minute
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种耐高温涂料印花粘合剂,由下列重量份的原料制成:聚醚丙烯酸酯20-25、N-丁氧基甲基丙烯酰胺2-3、乙酰乙酸基甲基丙烯酸乙酯13-16、乙氧基化三羟甲基丙烷三丙烯酸酯12-15、丙氧基化新戊二醇双丙烯酸酯7-9、丙烯酸丁酯3-4、异氰脲酸三缩水甘油酯10-12、OP-102-3、甲基丙烯酸5-6、过硫酸铵1-2、助剂4-5、水50-55。本发明粘合剂具有耐高温、耐候性、耐电弧性和自熄性的特点,还具有优良的柔韧性,固化膜收缩率低的特性;采用本粘合剂的涂料印花工艺简单、色彩浓艳、轮廓清晰、花型稳定,牢度好,有着广阔的发展前途。
Description
技术领域
本发明属于纺织印染助剂技术领域,尤其涉及一种耐高温涂料印花粘合剂及其制备方法。
背景技术
所谓涂料印花是借助粘合剂的作用,将不溶于水、对织物没有亲和性和反应性的颜料固着在织物上,从而达到着色的目的。据最新资料介绍,目前世界上大约有一半产量的印花织物为涂料印花。涂料印花粘合剂是涂料印花浆的主要成分,涂料印花成品质量的优劣直接受印花粘合剂性能的影响。
目前印花粘合剂的品质不一,因粘合剂质量问题引起的印花次品率在3%以上,造成了巨大的经济损失,且印花粘合剂的质量直接影响到印花的质量、精细度、面料的档次,因此,需要研发更优质的粘合剂。
发明内容
本发明的目的在于提供一种耐高温涂料印花粘合剂及其制备方法,该粘合剂具有耐高温、柔韧性好的特点。
本发明的技术方案如下:
一种耐高温涂料印花粘合剂,其特征在于由下列重量份的原料制成:聚醚丙烯酸酯20-25、N-丁氧基甲基丙烯酰胺2-3、乙酰乙酸基甲基丙烯酸乙酯13-16、乙氧基化三羟甲基丙烷三丙烯酸酯12-15、丙氧基化新戊二醇双丙烯酸酯7-9、丙烯酸丁酯3-4、异氰脲酸三缩水甘油酯10-12、OP-10 2-3、甲基丙烯酸5-6、过硫酸铵1-2、助剂4-5、水50-55;所述的助剂由下列重量份的原料制成:硅烷偶联剂KH-570 2-3、交联剂 TAC1-2、茶多酚2-3、苯乙烯3-4、苯乙烯基苯酚聚氧乙烯醚2.5-3.0、柠檬精油0.1-0.2、吗啉1-2、单硬脂酸甘油酯4-5、新戊二醇3-4、醋酸乙烯酯2-3、抗氧剂1035 2-3、二甘醇7-9、乙醇12-15;制备方法是将交联剂 TAC、苯乙烯、醋酸乙烯酯、新戊二醇、乙醇混合,加热至65-75℃,搅拌反应45-60分钟,继续升温至85-95℃,加入其它剩余成分,搅拌反应40-60分钟即得。
所述耐高温涂料印花粘合剂的制备方法,其特征在于包括以下步骤:将聚醚丙烯酸酯、N-丁氧基甲基丙烯酰胺、乙酰乙酸基甲基丙烯酸乙酯、乙氧基化三羟甲基丙烷三丙烯酸酯、丙氧基化新戊二醇双丙烯酸酯、丙烯酸丁酯、异氰脲酸三缩水甘油酯、甲基丙烯酸混合,在800-1200转/分搅拌下,以7-9℃/分的速率加热到60-70℃;加入OP-10,以5-7℃/分的速率加热到80-90℃,加入过硫酸铵、水及其他剩余成分的混合液,继续搅拌反应2.5-3小时,即得。
本发明的有益效果
本发明粘合剂具有耐高温、耐候性、耐电弧性和自熄性的特点,还具有优良的柔韧性,固化膜收缩率低的特性;采用本粘合剂的涂料印花工艺简单、色彩浓艳、轮廓清晰、花型稳定,牢度好,有着广阔的发展前途。
具体实施方式
一种耐高温涂料印花粘合剂,由下列重量份的原料制成:聚醚丙烯酸酯23、N-丁氧基甲基丙烯酰胺2.5、乙酰乙酸基甲基丙烯酸乙酯15、乙氧基化三羟甲基丙烷三丙烯酸酯13、丙氧基化新戊二醇双丙烯酸酯8、丙烯酸丁酯3.5、异氰脲酸三缩水甘油酯11、OP-10 2.5、甲基丙烯酸5.5、过硫酸铵1.5、助剂4.5、水53;所述的助剂由下列重量份(公斤)的原料制成:硅烷偶联剂KH-570 2、交联剂 TAC1、茶多酚3、苯乙烯3、苯乙烯基苯酚聚氧乙烯醚2.5、柠檬精油0.1、吗啉1、单硬脂酸甘油酯4、新戊二醇3、醋酸乙烯酯2、抗氧剂1035 2、二甘醇7、乙醇15;制备方法是将交联剂 TAC、苯乙烯、醋酸乙烯酯、新戊二醇、乙醇混合,加热至65-75℃,搅拌反应45-60分钟,继续升温至85-95℃,加入其它剩余成分,搅拌反应40-60分钟即得。
所述耐高温涂料印花粘合剂的制备方法,包括以下步骤:将聚醚丙烯酸酯、N-丁氧基甲基丙烯酰胺、乙酰乙酸基甲基丙烯酸乙酯、乙氧基化三羟甲基丙烷三丙烯酸酯、丙氧基化新戊二醇双丙烯酸酯、丙烯酸丁酯、异氰脲酸三缩水甘油酯、甲基丙烯酸混合,在1000转/分搅拌下,以8℃/分的速率加热到65℃;加入OP-10,以6℃/分的速率加热到85℃,加入过硫酸铵、水及其他剩余成分的混合液,继续搅拌反应2.7小时,即得。
该耐高温涂料印花粘合剂用于印花织物,按GB标准检测,干摩擦牢度3级,湿摩擦牢度在2-3级,刷洗牢度3-4级,粘色牢度4级,皂洗后褪色牢度3-4级。
Claims (2)
1.一种耐高温涂料印花粘合剂,其特征在于由下列重量份的原料制成:聚醚丙烯酸酯20-25、N-丁氧基甲基丙烯酰胺2-3、乙酰乙酸基甲基丙烯酸乙酯13-16、乙氧基化三羟甲基丙烷三丙烯酸酯12-15、丙氧基化新戊二醇双丙烯酸酯7-9、丙烯酸丁酯3-4、异氰脲酸三缩水甘油酯10-12、OP-10 2-3、甲基丙烯酸5-6、过硫酸铵1-2、助剂4-5、水50-55;所述的助剂由下列重量份的原料制成:硅烷偶联剂KH-570 2-3、交联剂 TAC1-2、茶多酚2-3、苯乙烯3-4、苯乙烯基苯酚聚氧乙烯醚2.5-3.0、柠檬精油0.1-0.2、吗啉1-2、单硬脂酸甘油酯4-5、新戊二醇3-4、醋酸乙烯酯2-3、抗氧剂1035 2-3、二甘醇7-9、乙醇12-15;制备方法是将交联剂 TAC、苯乙烯、醋酸乙烯酯、新戊二醇、乙醇混合,加热至65-75℃,搅拌反应45-60分钟,继续升温至85-95℃,加入其它剩余成分,搅拌反应40-60分钟即得。
2.根据权利要求1所述耐高温涂料印花粘合剂的制备方法,其特征在于包括以下步骤:将聚醚丙烯酸酯、N-丁氧基甲基丙烯酰胺、乙酰乙酸基甲基丙烯酸乙酯、乙氧基化三羟甲基丙烷三丙烯酸酯、丙氧基化新戊二醇双丙烯酸酯、丙烯酸丁酯、异氰脲酸三缩水甘油酯、甲基丙烯酸混合,在800-1200转/分搅拌下,以7-9℃/分的速率加热到60-70℃;加入OP-10,以5-7℃/分的速率加热到80-90℃,加入过硫酸铵、水及其他剩余成分的混合液,继续搅拌反应2.5-3小时,即得。