CN103509436A - 一种高抗阴极剥离的重防腐粉末涂料组合物 - Google Patents

一种高抗阴极剥离的重防腐粉末涂料组合物 Download PDF

Info

Publication number
CN103509436A
CN103509436A CN201310396125.6A CN201310396125A CN103509436A CN 103509436 A CN103509436 A CN 103509436A CN 201310396125 A CN201310396125 A CN 201310396125A CN 103509436 A CN103509436 A CN 103509436A
Authority
CN
China
Prior art keywords
parts
cathodic disbonding
powder coating
compounded mix
coating composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310396125.6A
Other languages
English (en)
Inventor
郑跃辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI DONGFANGJINHE PRECISION MACHINERY MANUFACTURING Co Ltd
Original Assignee
ANHUI DONGFANGJINHE PRECISION MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI DONGFANGJINHE PRECISION MACHINERY MANUFACTURING Co Ltd filed Critical ANHUI DONGFANGJINHE PRECISION MACHINERY MANUFACTURING Co Ltd
Priority to CN201310396125.6A priority Critical patent/CN103509436A/zh
Publication of CN103509436A publication Critical patent/CN103509436A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高抗阴极剥离的重防腐粉末涂料组合物，它是由下述重量份的原料组成的：E-12环氧树脂45-50、活性炭3-5、准球形硅微粉4-6、双氰胺10-15、过氧化叔丁基0.3-0.8、甲基三丁酮肟基硅烷8-12、三聚磷酸铝15-25、酞青蓝0.5-1、三苯基磷0.1-0.4、聚二甲基硅氧烷1.1-1.3、复合填料7-10；本发明的粉末涂料的优点在于阴极保护时涂层的阴极剥离面积极小，即使存放半年以上依然有很好的流动性。

Description

一种高抗阴极剥离的重防腐粉末涂料组合物
技术领域
    本发明主要涉及一种涂料，尤其涉及一种高抗阴极剥离的重防腐粉末涂料组合物。
背景技术
粉末涂料是与一般涂料完全不同的形态，它是以微细粉末的状态存在的。由于不使用溶剂，所以称为粉末涂料。粉末涂料的主要特点有：具有无害、高效率、节省资源和环保特点。粉末涂料是一种新型的、不含溶剂，100%固体粉末状涂料。具有不用溶剂、无污染、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。
发明内容
本发明目的就是为了提供一种高抗阴极剥离的重防腐粉末涂料组合物。
本发明是通过以下技术方案实现的：
一种高抗阴极剥离的重防腐粉末涂料组合物，其特征在于它是由下述重量份的原料组成的：
E-12环氧树脂45-50、活性炭3-5、准球形硅微粉4-6、双氰胺10-15、过氧化叔丁基0.3-0.8、甲基三丁酮肟基硅烷8-12、三聚磷酸铝15-25、酞青蓝0.5-1、三苯基磷0.1-0.4、聚二甲基硅氧烷1.1-1.3、复合填料7-10；
所述的复合填料是由下述重量份的原料组成的：
苏州土40-50、硫酸钡粉40-50、氮化铝6-8、硅铝酸钠2-3、羊毛脂2-3、聚乙烯醇3-4、甲基异噻唑啉酮1-2；
将上述甲基异噻唑啉酮加入到6-10倍水中，加入苏州土和硫酸钡粉，在150-200℃下保温搅拌2-3小时，降低温度为100-120℃，加入氮化铝、硅铝酸钠、羊毛脂、搅拌均匀，最后加入聚乙烯醇，在60-80℃下搅拌1-2小时，烘干、研磨，过60-80目筛，即得所述复合填料。
一种高抗阴极剥离的重防腐粉末涂料组合物的制备方法，包括以下步骤：
将上述准球形硅微粉、活性炭、三聚磷酸铝混合，在100-150℃下预热6-10分钟，降低温度温度为60-70℃，加入甲基三丁酮肟基硅烷与复合填料，400-500转/分搅拌分散3-4分钟，冷却至常温，与剩余各原料混合，搅拌均匀后经过挤出机熔融挤出，冷却、研碎成粉，包装，即得所述高抗阴极剥离的重防腐粉末涂料组合物。
本发明的优点是：
    本发明的粉末涂料的优点在于阴极保护时涂层的阴极剥离面积极小，即使存放半年以上依然有很好的流动性。
具体实施方式
实施例1，
一种高抗阴极剥离的重防腐粉末涂料组合物，它是由下述重量份（公斤）的原料组成的：
E-12环氧树脂50、活性炭5、准球形硅微粉6、双氰胺15、过氧化叔丁基0.8、甲基三丁酮肟基硅烷12、三聚磷酸铝25、酞青蓝0.5、三苯基磷0.4、聚二甲基硅氧烷1.3、复合填料10；
所述的复合填料是由下述重量份的原料组成的：
苏州土50、硫酸钡粉50、氮化铝8、硅铝酸钠3、羊毛脂3、聚乙烯醇3、甲基异噻唑啉酮1；
将上述甲基异噻唑啉酮加入到10倍水中，加入苏州土和硫酸钡粉，在200℃下保温搅拌2小时，降低温度为120℃，加入氮化铝、硅铝酸钠、羊毛脂、搅拌均匀，最后加入聚乙烯醇，在80℃下搅拌1小时，烘干、研磨，过80目筛，即得所述复合填料。
一种高抗阴极剥离的重防腐粉末涂料组合物的制备方法，包括以下步骤：
将上述准球形硅微粉、活性炭、三聚磷酸铝混合，在150℃下预热10分钟，降低温度温度为60℃，加入甲基三丁酮肟基硅烷与复合填料，500转/分搅拌分散3分钟，冷却至常温，与剩余各原料混合，搅拌均匀后经过挤出机熔融挤出，冷却、研碎成粉，包装，即得所述高抗阴极剥离的重防腐粉末涂料组合物。
性能测试：
人工加速老化时间≥500h；
耐洗刷次数≥10000次。

Claims (2)

1.一种高抗阴极剥离的重防腐粉末涂料组合物，其特征在于它是由下述重量份的原料组成的：
E-12环氧树脂45-50、活性炭3-5、准球形硅微粉4-6、双氰胺10-15、过氧化叔丁基0.3-0.8、甲基三丁酮肟基硅烷8-12、三聚磷酸铝15-25、酞青蓝0.5-1、三苯基磷0.1-0.4、聚二甲基硅氧烷1.1-1.3、复合填料7-10；
所述的复合填料是由下述重量份的原料组成的：
苏州土40-50、硫酸钡粉40-50、氮化铝6-8、硅铝酸钠2-3、羊毛脂2-3、聚乙烯醇3-4、甲基异噻唑啉酮1-2；
将上述甲基异噻唑啉酮加入到6-10倍水中，加入苏州土和硫酸钡粉，在150-200℃下保温搅拌2-3小时，降低温度为100-120℃，加入氮化铝、硅铝酸钠、羊毛脂、搅拌均匀，最后加入聚乙烯醇，在60-80℃下搅拌1-2小时，烘干、研磨，过60-80目筛，即得所述复合填料。
2.一种如权利要求1所述的高抗阴极剥离的重防腐粉末涂料组合物的制备方法，其特征在于包括以下步骤：
将上述准球形硅微粉、活性炭、三聚磷酸铝混合，在100-150℃下预热6-10分钟，降低温度温度为60-70℃，加入甲基三丁酮肟基硅烷与复合填料，400-500转/分搅拌分散3-4分钟，冷却至常温，与剩余各原料混合，搅拌均匀后经过挤出机熔融挤出，冷却、研碎成粉，包装，即得所述高抗阴极剥离的重防腐粉末涂料组合物。
CN201310396125.6A 2013-09-04 2013-09-04 一种高抗阴极剥离的重防腐粉末涂料组合物 Pending CN103509436A (zh)