CN103509432B - A kind of metal flashing powder coatings - Google Patents
A kind of metal flashing powder coatings Download PDFInfo
- Publication number
- CN103509432B CN103509432B CN201310393539.3A CN201310393539A CN103509432B CN 103509432 B CN103509432 B CN 103509432B CN 201310393539 A CN201310393539 A CN 201310393539A CN 103509432 B CN103509432 B CN 103509432B
- Authority
- CN
- China
- Prior art keywords
- powder
- metal flashing
- raw material
- powder coatings
- compounded mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Does is the invention discloses a kind of metal flashing powder coatings, it made up of the raw material of following weight parts: pearl powder 10-14, Stainless Steel Powder 3-5, ultra micro wax powder 0.8-1.0, triglycidyl isocyanurate 6-10, silicone resin 5-10, E-12 epoxy resin 50-60, hydrophobicity aerosil 1-2, linking agent? TAC3.0-3.5, boric acid 0.3-0.4, compounded mix 5-10; Powder coating of the present invention fully can show metallic pigment flash of light feature and angle chromaticity effect, and the weather resisteant of film is strong, and ageing-resistant, scrubbing resistance, plays a very good protection to basic unit.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of metal flashing powder coatings.
Background technology
Powder coating is form diverse with general coating, and it exists with the state of fines.Owing to not using solvent, so be called powder coating.The principal feature of powder coating has: have harmless, high-level efficiency, saving resource and environmental protection feature.Powder coating be a kind of novel, not containing solvent, 100% solid powdery coating.Have without solvent, pollution-free, save the energy and resource, reduce labor intensity and film physical strength high.
Summary of the invention
The object of the invention is exactly to provide a kind of metal flashing powder coatings.
The present invention is achieved by the following technical solutions:
A kind of metal flashing powder coatings, is characterized in that what it was made up of the raw material of following weight parts:
Pearl powder 10-14, Stainless Steel Powder 3-5, ultra micro wax powder 0.8-1.0, triglycidyl isocyanurate 6-10, silicone resin 5-10, E-12 epoxy resin 50-60, hydrophobicity aerosil 1-2, linking agent TAC3.0-3.5, boric acid 0.3-0.4, compounded mix 5-10;
Described compounded mix is made up of the raw material of following weight parts:
Suzhou soil 40-50, blaue fixe 40-50, aluminium nitride 6-8, sodium silicoaluminate 2-3, lanolin 2-3, polyvinyl alcohol 3-4, methylisothiazolinone 1-2;
Above-mentioned methylisothiazolinone is joined in 6-10 times of water, add Suzhou soil and blaue fixe, insulated and stirred 2-3 hour at 150-200 DEG C, reduction temperature is 100-120 DEG C, adds aluminium nitride, sodium silicoaluminate, lanolin, stirs, finally add polyvinyl alcohol, 1-2 hour is stirred at 60-80 DEG C, dry, grind, cross 60-80 mesh sieve, obtain described compounded mix.
A preparation method for metal flashing powder coatings, comprises the following steps:
Above-mentioned pearl powder, Stainless Steel Powder are mixed with silicone resin, is heated to 130-200 DEG C, insulation 20-30 minute, cooling, compressing tablet, fragmentation, mix with each raw material of residue, melt extrude after being uniformly mixed through forcing machine, cool, grind into powder, obtain described metal flashing powder coatings.
Advantage of the present invention is:
Powder coating of the present invention fully can show metallic pigment flash of light feature and angle chromaticity effect, and the weather resisteant of film is strong, and ageing-resistant, scrubbing resistance, plays a very good protection to basic unit.
Embodiment
Embodiment 1,
A kind of metal flashing powder coatings, it is made up of the raw material of following weight parts (kilogram):
Pearl powder 14, Stainless Steel Powder 3, ultra micro wax powder 1.0, triglycidyl isocyanurate 10, silicone resin 10, E-12 epoxy resin 60, hydrophobicity aerosil 2, linking agent TAC3.5, boric acid 0.4, compounded mix 10;
Described compounded mix is made up of the raw material of following weight parts:
Suzhou soil 40, blaue fixe 50, aluminium nitride 6-8, sodium silicoaluminate 2, lanolin 3, polyvinyl alcohol 3, methylisothiazolinone 2;
Above-mentioned methylisothiazolinone is joined in 10 times of water, add Suzhou soil and blaue fixe, insulated and stirred 2 hours at 200 DEG C, reducing temperature is 120 DEG C, adds aluminium nitride, sodium silicoaluminate, lanolin, stirs, finally add polyvinyl alcohol, stir 2 hours at 80 DEG C, dry, grind, cross 80 mesh sieves, obtain described compounded mix.
A preparation method for metal flashing powder coatings, comprises the following steps:
Above-mentioned pearl powder, Stainless Steel Powder are mixed with silicone resin, is heated to 200 DEG C, be incubated 30 minutes, cooling, compressing tablet, fragmentation, mix with each raw material of residue, melt extrude after being uniformly mixed through forcing machine, cool, grind into powder, obtain described metal flashing powder coatings.
Performance test:
Artificial accelerated aging time >=500h;
Washability number of times >=10000 time.
Claims (2)
1. a metal flashing powder coatings, is characterized in that what it was made up of the raw material of following weight parts:
Pearl powder 10-14, Stainless Steel Powder 3-5, ultra micro wax powder 0.8-1.0, triglycidyl isocyanurate 6-10, silicone resin 5-10, E-12 epoxy resin 50-60, hydrophobicity aerosil 1-2, linking agent TAC3.0-3.5, boric acid 0.3-0.4, compounded mix 5-10;
Described compounded mix is made up of the raw material of following weight parts:
Suzhou soil 40-50, blaue fixe 40-50, aluminium nitride 6-8, sodium silicoaluminate 2-3, lanolin 2-3, polyvinyl alcohol 3-4, methylisothiazolinone 1-2;
Above-mentioned methylisothiazolinone is joined in 6-10 times of water, add Suzhou soil and blaue fixe, insulated and stirred 2-3 hour at 150-200 DEG C, reduce temperature to 100-120 DEG C, add aluminium nitride, sodium silicoaluminate, lanolin, stir, finally add polyvinyl alcohol, 1-2 hour is stirred at 60-80 DEG C, dry, grind, cross 60-80 mesh sieve, obtain described compounded mix.
2. a preparation method for metal flashing powder coatings as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned pearl powder, Stainless Steel Powder are mixed with silicone resin, is heated to 130-200 DEG C, insulation 20-30 minute, cooling, compressing tablet, fragmentation, mix with each raw material of residue, melt extrude after being uniformly mixed through forcing machine, cool, grind into powder, obtain described metal flashing powder coatings.