CN103497684A - 一种2k灰白底漆 - Google Patents
一种2k灰白底漆 Download PDFInfo
- Publication number
- CN103497684A CN103497684A CN201310438811.5A CN201310438811A CN103497684A CN 103497684 A CN103497684 A CN 103497684A CN 201310438811 A CN201310438811 A CN 201310438811A CN 103497684 A CN103497684 A CN 103497684A
- Authority
- CN
- China
- Prior art keywords
- resin
- white primer
- oil
- ash based
- based white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于涂料领域,具体涉及一种2K灰白底漆,其组分及其质量百分比为:9460树脂25-30%,PE树脂4-8%,立德粉3-6%,硝基纤维素5-8%,965黑浆0.9-1.3%,钛白粉15-18%,膨润土0.3-0.6%,催干剂0.01-0.03%,965BGS蓝0.1-0.2%,硫酸钡5-8%,抗油剂0.06-0.1%,滑石粉13-15%,有机中黄0.2-0.4%,其余为稀释剂。采用本发明的技术方案的有益效果是:采用9460树脂和PE树脂,底漆层的硬度增强,避免使用铅类等有毒物质,更加环保,本发明的2K灰白底漆,附着力高,抗油抗水性能好。
Description
技术领域
本发明属于涂料领域,具体涉及一种2K灰白底漆。
背景技术
目前,一些产品的表面,如塑料件产品的表面的漆层分为一般漆层和面漆层,底漆,是指直涂到物体表面作为坚实基础的涂料,一般由热塑性丙烯酸树脂涂料形成的,面漆层一般由紫外光固化涂料或者双组分聚氨酯丙烯酸酯涂料形成。底漆要求在物面上附着牢固,以增加上层涂料的附着力,提高面漆的装饰性。根据装涂要求可分为头道底漆、二道底漆等。
目前市场上的底漆树脂大都采用热塑性丙烯酸树脂作为树脂主体,这种树脂在加热固化后,漆层硬度比较低,当底漆层为多层漆层时,底漆层的硬度会随着层数的增加而迅速降低,而且,现有的底漆还存在以下技术问题:抗油抗水效果差。
发明内容
本发明的目的是:克服现有技术中底漆硬度低的技术不足,提供一种硬度高、抗油抗水性好的2K灰白底漆。
为解决上述问题,本发明采用的技术方案如下:
一种2K灰白底漆,其组分及其质量百分比为:9460树脂25-30%,PE树脂4-8%,立德粉3-6%,硝基纤维素5-8%,965黑浆0.9-1.3%,钛白粉15-18%,膨润土0.3-0.6%,催干剂0.01-0.03%,965BGS蓝0.1-0.2%,硫酸钡5-8%,抗油剂0.06-0.1%,滑石粉13-15%,有机中黄0.2-0.4%,其余为稀释剂。
进一步的,所述抗油剂选自:435抗油剂、445抗油剂、8990抗油剂中的一种。
进一步的,所述催干剂为稀土催干剂。
进一步的,所述稀释剂的组分及质量百分比为:二甲苯15%、甲醇65%、环己酮20%。
进一步的,所述有机中黄选自:1154有机中黄、1151有机中黄中、965有机中黄的一种。
进一步的,一种2K灰白底漆,其组分及其质量百分比为:9460树脂27%,PE树脂6%,立德粉4%,硝基纤维素6%,965黑浆1%,钛白粉16%,膨润土0.4%,稀土催干剂0.02%,965BGS蓝0.15%,硫酸钡6%,抗油剂0.08%,滑石粉14%,有机中黄0.2-0.4%,其余为稀释剂。
进一步的,一种2K灰白底漆,制备方法如下:按照二甲苯15%、甲醇65%、环己酮20%的比列配置稀释剂;按所述比列加入其他组分:9460树脂25-30%,PE树脂4-8%,立德粉3-6%,硝基纤维素5-8%,965黑浆0.9-1.3%,钛白粉15-18%,膨润土0.3-0.6%,催干剂0.01-0.03%,965BGS蓝0.1-0.2%,硫酸钡5-8%,抗油剂0.06-0.1%,滑石粉13-15%,有机中黄0.2-0.4%,其余为稀释剂,抗油剂用环己酮稀释后加入,然后在35℃条件下研磨搅拌均匀,即得所需2K灰白底漆。
采用本发明的技术方案的有益效果是:采用9460树脂和PE树脂,底漆层的硬度增强,避免使用铅类等有毒物质,更加环保,本发明的2K灰白底漆,附着力高,抗油抗水性能好。
具体实施方式
为了进一步阐述本发明,下面给出一些实施例。这些实施例完全是例证性的,它们仅用来对本发明进行具体描述,不应理解为对本发明的限制。
实施例1
一种2K灰白底漆,其组分及其质量百分比为:9460树脂30%,PE树脂4%,立德粉3%,硝基纤维素5%,965黑浆0.9%,钛白粉18%,膨润土0.3%,催干剂0.01%,965BGS蓝0.1%,硫酸钡5%,抗油剂0.06%,滑石粉13%,有机中黄0.2-0.4%,其余为稀释剂。
其制备方法如下:按照二甲苯15%、甲醇65%、环己酮20%的比列配置稀释剂,按上述比例加入其他组分,抗油剂用环己酮稀释后加入,然后在30℃条件下研磨搅拌均匀,即得所需2K灰白底漆。
实施例2
一种2K灰白底漆,其组分及其质量百分比为:9460树脂27%,PE树脂6%,立德粉4%,硝基纤维素6%,965黑浆1%,钛白粉16%,膨润土0.4%,稀土催干剂0.02%,965BGS蓝0.15%,硫酸钡6%,抗油剂0.08%,滑石粉14%,有机中黄0.4%,其余为稀释剂。
其制备方法如下:按照二甲苯15%、甲醇65%、环己酮20%的比例配置稀释剂,按上述比列加入其他组分,抗油剂用环己酮稀释后加入,然后在35℃条件下研磨搅拌均匀,即得所需2K灰白底漆。
本实施例为最佳实施方式。
实施例3
一种2K灰白底漆,其组分及其质量百分比为:9460树脂25%,PE树脂8%,立德粉6%,硝基纤维素8%,965黑浆1.3%,钛白粉15%,膨润土0.6%,催干剂0.03%,965BGS蓝0.2%,硫酸钡8%,抗油剂0.1%,滑石粉15%,有机中黄0.4%,其余为稀释剂。
其制备方法如下:按照二甲苯15%、甲醇65%、环己酮20%的比例配置稀释剂,按上述比例加入其他组分,抗油剂用环己酮稀释后加入,然后在40℃条件下研磨搅拌均匀,即得所需2K灰白底漆。
尽管上述实施例已本发明的技术方案进行了详细地描述,但是本发明的技术方案并不限于以上实施例,在不脱离本发明的思想和宗旨的情况下,对本发明的技术方案所做的任何改动都将落入本发明的权利要求书所限定的范围。
Claims (7)
1.一种2K灰白底漆,其特征在于,所述2K灰白底漆的组分及其质量百分比为:9460树脂25-30%,PE树脂4-8%,立德粉3-6%,硝基纤维素5-8%,965黑浆0.9-1.3%,钛白粉15-18%,膨润土0.3-0.6%,催干剂0.01-0.03%,965BGS蓝0.1-0.2%,硫酸钡5-8%,抗油剂0.06-0.1%,滑石粉13-15%,有机中黄0.2-0.4%,其余为稀释剂。
2.根据权利要求1所述的一种2K灰白底漆,其特征在于,所述抗油剂选自:435抗油剂、445抗油剂、8990抗油剂中的一种。
3.根据权利要求1所述的一种2K灰白底漆,其特征在于,所述催干剂为稀土催干剂。
4.根据权利要求1所述的一种2K灰白底漆,其特征在于,所述稀释剂的组分及质量百分比为:二甲苯15%、甲醇65%、环己酮20%。
5.根据权利要求1所述的一种2K灰白底漆,其特征在于,所述有机中黄选自:1154有机中黄、1151有机中黄中、965有机中黄的一种。
6.根据权利要求1所述的一种2K灰白底漆,其特征在于,所述2K灰白底漆的组分及其质量百分比为:9460树脂27%,PE树脂6%,立德粉4%,硝基纤维素6%,965黑浆1%,钛白粉16%,膨润土0.4%,稀土催干剂0.02%,965BGS蓝0.15%,硫酸钡6%,抗油剂0.08%,滑石粉14%,有机中黄0.2-0.4%,其余为稀释剂。
7.一种2K灰白底漆,其制备方法如下:按照二甲苯15%、甲醇65%、环己酮20%的比例配置稀释剂;按所述比例加入其他组分:9460树脂25-30%,PE树脂4-8%,立德粉3-6%,硝基纤维素5-8%,965黑浆0.9-1.3%,钛白粉15-18%,膨润土0.3-0.6%,催干剂0.01-0.03%,965BGS蓝0.1-0.2%,硫酸钡5-8%,抗油剂0.06-0.1%,滑石粉13-15%,有机中黄0.2-0.4%,其余为稀释剂,抗油剂用环己酮稀释后加入,然后在35℃条件下研磨搅拌均匀,即得所需2K灰白底漆。