CN103497564B - Dry powder latex paint water resistant putty powder - Google Patents
Dry powder latex paint water resistant putty powder Download PDFInfo
- Publication number
- CN103497564B CN103497564B CN201310385713.XA CN201310385713A CN103497564B CN 103497564 B CN103497564 B CN 103497564B CN 201310385713 A CN201310385713 A CN 201310385713A CN 103497564 B CN103497564 B CN 103497564B
- Authority
- CN
- China
- Prior art keywords
- powder
- dry
- add
- latex
- dry powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of Dry powder latex paint water resistant putty powder, be made up of the raw material of following weight part: dry powder 15-25, sierozem power 30-40, dicalcium powder 10-20, modified talc powder 20-30, Vltra tears 0.5-1.5, hydroxypropylguar gum 0.4-0.6, redispersable latex powder 2-3.Putty powder of the present invention has the performances such as excellent water tolerance, acid and alkali-resistance, weather resisteant, scrub resistance, mildew-resistant, and cohesive strength is high, not easy to crack, do not come off, non-scale, not hollowing, be easy to painted, in bright gay color, not fugitive color, traditional putty and the emulsion paint decoration for buildings inner-outer wall can be replaced.
Description
Technical field
The present invention relates to a kind of Dry powder latex paint water resistant putty powder, belong to building material technical field.
Background technology
Dry powder emulsion paint is the same with emulsion paint, main raw material(s) has filmogen, color stuffing and functional agent etc., be the general color dry powder dope of a kind of Multifunction internal-external wall, there is flexible, many application properties, flexibility is high, cohesive strength is extra-high, splitting resistance is excellent, fast in colour, good decorating effect, application property are good, use cost is low, transportation cost is low, packing cost is low, be easy to the advantages such as storage.The general low gradeization of the dry powder emulsion paint putty powder that on existing market, building decoration uses, its water tolerance, weathering resistance are poor, can not adapt to the requirement of decorating inner and external walls.
Summary of the invention
The object of the invention is to for the deficiencies in the prior art, the Dry powder latex paint water resistant putty powder that a kind of water-tolerant, good weatherability, resistance to acids and bases are good is provided.
The technical solution used in the present invention is as follows:
A kind of Dry powder latex paint water resistant putty powder, is made up of the raw material of following weight part: dry powder 15-25, sierozem power 30-40, dicalcium powder 10-20, modified talc powder 20-30, Vltra tears 0.5-1.5, hydroxypropylguar gum 0.4-0.6, redispersable latex powder 2-3;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 4-8:2-3:1-2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 1-2%, the sodium polyacrylate of 2-3%, the calcium lignin sulphonate of 1-2%, vinyl three ('beta '-methoxy oxyethyl group) silane of 0.5-1%, 2000-3000rpm speed lapping 10-15min, dry, pulverize, cross 400-500 mesh sieve, then add appropriate water making beating and make the slurries that concentration is 40-50%, add the Sodium dodecylbenzene sulfonate of 2-3%, the polyvinylpyrrolidone of 3-5%, the organosilicon crylic acid latex of 4-8%, the butyl of 0.5-1%, the Lauryl Alcohol ester of 1-2%, stir 1-2h, filter, dry, pulverize porphyrize, cross 300-400 mesh sieve.
Preferably, a kind of Dry powder latex paint water resistant putty powder, is made up of the raw material of following weight part: dry powder 20, sierozem power 30, dicalcium powder 20, modified talc powder 30, Vltra tears 1, hydroxypropylguar gum 0.5, redispersable latex powder 2;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 5:2:2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 1%, the sodium polyacrylate of 2%, the calcium lignin sulphonate of 1%, vinyl three ('beta '-methoxy oxyethyl group) silane of 0.5%, 3000rpm speed lapping 10min, dry, pulverize, cross 500 mesh sieves, then add appropriate water making beating and make the slurries that concentration is 50%, add the Sodium dodecylbenzene sulfonate of 2%, the polyvinylpyrrolidone of 3%, the organosilicon crylic acid latex of 5%, the butyl of 0.5%, the Lauryl Alcohol ester of 1%, stir 2h, filter, dry, pulverize porphyrize, cross 400 mesh sieves.
Preparation method: above-mentioned raw materials is added high-altitude mixing and blending machine and stir 20-40 minute, packing, gets product.
During use, can blade coating polishing or spraying after Dry powder latex paint water resistant putty powder of the present invention and water are stirred according to the ratio of weight ratio 1: 0.3-0.6.
Beneficial effect of the present invention:
Putty powder of the present invention has the performances such as excellent water tolerance, acid and alkali-resistance, weather resisteant, scrub resistance, mildew-resistant, and cohesive strength is high, not easy to crack, do not come off, non-scale, not hollowing, be easy to painted, in bright gay color, not fugitive color, traditional putty and the emulsion paint decoration for buildings inner-outer wall can be replaced.
Embodiment
A kind of Dry powder latex paint water resistant putty powder, is made up of the raw material of following weight (kg): dry powder 20, sierozem power 30, dicalcium powder 20, modified talc powder 30, Vltra tears 1, hydroxypropylguar gum 0.5, redispersable latex powder 2;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 5:2:2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 1%, the sodium polyacrylate of 2%, the calcium lignin sulphonate of 1%, vinyl three ('beta '-methoxy oxyethyl group) silane of 0.5%, 3000rpm speed lapping 10min, dry, pulverize, cross 500 mesh sieves, then add appropriate water making beating and make the slurries that concentration is 50%, add the Sodium dodecylbenzene sulfonate of 2%, the polyvinylpyrrolidone of 3%, the organosilicon crylic acid latex of 5%, the butyl of 0.5%, the Lauryl Alcohol ester of 1%, stir 2h, filter, dry, pulverize porphyrize, cross 400 mesh sieves.
Above-mentioned raw materials is added high-altitude mixing and blending machine and stir 30 minutes, packing, get product.
During use, can blade coating polishing or spraying after Dry powder latex paint water resistant putty powder of the present invention and water are stirred according to the ratio of weight ratio 1: 0.5.
The Performance Detection of putty powder of the present invention is as follows:
Claims (2)
1. a Dry powder latex paint water resistant putty powder, it is characterized in that, be made up of the raw material of following weight part: dry powder 15-25, sierozem power 30-40, dicalcium powder 10-20, modified talc powder 20-30, Vltra tears 0.5-1.5, hydroxypropylguar gum 0.4-0.6, redispersable latex powder 2-3;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 4-8:2-3:1-2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 1-2%, the sodium polyacrylate of 2-3%, the calcium lignin sulphonate of 1-2%, vinyl three ('beta '-methoxy oxyethyl group) silane of 0.5-1%, 2000-3000rpm speed lapping 10-15min, dry, pulverize, cross 400-500 mesh sieve, then add appropriate water making beating and make the slurries that concentration is 40-50%, add the Sodium dodecylbenzene sulfonate of 2-3%, the polyvinylpyrrolidone of 3-5%, the organosilicon crylic acid latex of 4-8%, the butyl of 0.5-1%, the Lauryl Alcohol ester of 1-2%, stir 1-2h, filter, dry, pulverize porphyrize, cross 300-400 mesh sieve.
2. Dry powder latex paint water resistant putty powder according to claim 1, it is characterized in that, be made up of the raw material of following weight part: dry powder 20, sierozem power 30, dicalcium powder 20, modified talc powder 30, Vltra tears 1, hydroxypropylguar gum 0.5, redispersable latex powder 2;
The preparation method of described modified talc powder is as follows: take talcum powder by weight 5:2:2:1, wilkinite, jade powder, boron mud mixes, add the trolamine of 1%, the sodium polyacrylate of 2%, the calcium lignin sulphonate of 1%, vinyl three ('beta '-methoxy oxyethyl group) silane of 0.5%, 3000rpm speed lapping 10min, dry, pulverize, cross 500 mesh sieves, then add appropriate water making beating and make the slurries that concentration is 50%, add the Sodium dodecylbenzene sulfonate of 2%, the polyvinylpyrrolidone of 3%, the organosilicon crylic acid latex of 5%, the butyl of 0.5%, the Lauryl Alcohol ester of 1%, stir 2h, filter, dry, pulverize porphyrize, cross 400 mesh sieves.