CN103496964A - 可低温烧结的微波介电陶瓷Ca3Bi(PO4)3及其制备方法 - Google Patents

可低温烧结的微波介电陶瓷Ca3Bi(PO4)3及其制备方法 Download PDF

Info

Publication number
CN103496964A
CN103496964A CN201310434646.6A CN201310434646A CN103496964A CN 103496964 A CN103496964 A CN 103496964A CN 201310434646 A CN201310434646 A CN 201310434646A CN 103496964 A CN103496964 A CN 103496964A
Authority
CN
China
Prior art keywords
temperature
hours
sintering
preparation
ca3bi
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310434646.6A
Other languages
English (en)
Other versions
CN103496964B (zh
Inventor
苏聪学
巩美露
方亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pubei Gaomai New Energy Technology Co ltd
Original Assignee
Guilin University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin University of Technology filed Critical Guilin University of Technology
Priority to CN201310434646.6A priority Critical patent/CN103496964B/zh
Publication of CN103496964A publication Critical patent/CN103496964A/zh
Application granted granted Critical
Publication of CN103496964B publication Critical patent/CN103496964B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种可低温烧结的微波介电陶瓷Ca3Bi(PO4)3及其制备方法。可低温烧结的微波介电陶瓷的组成为Ca3Bi(PO4)3。(1)将纯度为99.9%以上的CaCO3、Bi2O3和P2O5的原始粉末按Ca3Bi(PO4)3化学式称量配料。(2)将步骤(1)原料湿式球磨混合12小时,溶剂为蒸馏水,烘干后在750℃大气气氛中预烧6小时。(3)在步骤(2)制得的粉末中添加粘结剂并造粒后,再压制成型,最后在840~870℃大气气氛中烧结4小时;所述的粘结剂采用质量浓度为5%的聚乙烯醇溶液,剂量占粉末总质量的3%。本发明制备的陶瓷在840-870℃烧结良好,其介电常数达到19~20,品质因数Qf值高达74000-93000GHz,谐振频率温度系数小,在工业上有着极大的应用价值。

Description

可低温烧结的微波介电陶瓷 Ca3Bi(PO4)3 及其制备方法
技术领域
本发明涉及介电陶瓷材料,特别是涉及在微波频率使用的介质基板、谐振器和滤波器等微波元器件的微波介电陶瓷材料及其制备方法。
背景技术
微波介电陶瓷是指应用于微波频段(主要是UHF、SHF频段)电路中作为介质材料并完成一种或多种功能的陶瓷,在现代通讯中被广泛用作谐振器、滤波器、介质基片和介质导波回路等元器件,是现代通信技术的关键基础材料,已在便携式移动电话、汽车电话、无绳电话、电视卫星接受器和军事雷达等方面有着十分重要的应用,在现代通讯工具的小型化、集成化过程中正发挥着越来越大的作用。
应用于微波频段的介电陶瓷,应满足如下介电特性的要求:(1)系列化介电常数εr以适应不同频率及不同应用场合的要求;(2)高的品质因数Q值或介质损耗tanδ以降低噪音,一般要求Qf≥3000 GHz;(3) 谐振频率的温度系数τƒ尽可能小以保证器件具有好的热稳定性,一般要求-10/℃≤τƒ ≤+10 ppm/℃。国际上从20世纪30年代末就有人尝试将电介质材料应用于微波技术。
根据相对介电常数εr的大小与使用频段的不同,通常可将已被开发和正在开发的微波介电陶瓷分为4类。
(1)超低介电常数微波介电陶瓷,主要代表是Al2O3-TiO2、Y2BaCuO5、MgAl2O4和Mg2SiO4等,其εr≤20,品质因数Q×f≥50000GHz,τƒ≤10 ppm/°C。主要用于微波基板以及高端微波元器件。
(2)低εr和高Q值的微波介电陶瓷,主要是BaO-MgO-Ta2O5, BaO-ZnO-Ta2O5或BaO-MgO-Nb2O5, BaO-ZnO-Nb2O5系统或它们之间的复合系统MWDC材料。其εr=25~30, Q=(1~2)×104(在f≥10 GHz下), τƒ≈0。主要应用于f≥8 GHz的卫星直播等微波通信机中作为介质谐振器件。
(3)中等εr和Q值的微波介电陶瓷,主要是以BaTi4O9、Ba2Ti9O20和(Zr、Sn)TiO4等为基的MWDC材料,其εr=35~40,Q=(6~9)×103(在f=3~-4GHz下),τƒ≤5 ppm/°C。主要用于4~8 GHz 频率范围内的微波军用雷达及通信系统中作为介质谐振器件。
(4)高εr而Q值较低的微波介电陶瓷,主要用于0.8~4GHz 频率范围内民用移动通讯系统,这也是微波介电陶瓷研究的重点。80年代以来,Kolar、Kato等人相继发现并研究了类钙钛矿钨青铜型BaO—Ln2O3—TiO2系列(Ln=La、 Sm、 Nd或Pr等,简称BLT系)、复合钙钛矿结构CaO—Li2O—Ln2O3—TiO2系列、铅基系列材料、Ca1-xLn2x/3TiO3系等高εr微波介电陶瓷,其中BLT体系的BaO—Nd2O3—TiO2材料介电常数达到90,铅基系列 (Pb,Ca)ZrO3介电常数达到105。
以上这些材料体系的烧结温度一般高于1300°C,不能直接与Ag和Cu 等低熔点金属共烧形成多层陶瓷电容器。近年来,随着低温共烧陶瓷技术(Low Temperature Co-fired Ceramics, LTCC)的发展和微波多层器件发展的要求,国内外的研究人员对一些低烧体系材料进行了广泛的探索和研究,主要是采用微晶玻璃或玻璃-陶瓷复合材料体系,因低熔点玻璃相具有相对较高的介质损耗,玻璃相的存在大大提高了材料的介质损耗。因此研制无玻璃相的可低烧的微波介电陶瓷是当前研究的重点。
发明内容
本发明的目的是提供一种具有低损耗与良好的热稳定性,同时烧结温度低的微波介电陶瓷及其制备方法。
本发明涉及的可低温烧结的微波介电陶瓷的化学组成为:Ca3Bi(PO4)3
所述可低温烧结的微波介电陶瓷的制备方法具体步骤为:
(1)将纯度为99.9%以上的CaCO3、Bi2O3和P2O5的原始粉末按Ca3Bi(PO4)3化学式称量配料。
(2)将步骤(1)原料湿式球磨混合12小时,溶剂为蒸馏水,烘干后在750℃大气气氛中预烧6小时。
(3)在步骤(2)制得的粉末中添加粘结剂并造粒后,再压制成型,最后在840~870℃大气气氛中烧结4小时;所述的粘结剂采用质量浓度为5%的聚乙烯醇溶液,剂量占粉末总质量的3%。
本发明制备的陶瓷在840-870℃烧结良好,其介电常数达到19~20,品质因数Qf值高达74000-93000GHz,谐振频率温度系数小,在工业上有着极大的应用价值。
具体实施方式
实施例:
表1示出了构成本发明的不同烧结温度的4个具体实施例及其微波介电性能。其制备方法如上所述,用圆柱介质谐振器法进行微波介电性能的评价。
本发明决不限于以上实施例。烧结温度的上下限、区间取值都能实现本发明,在此不一一列举实施例。
本陶瓷可广泛用于各种介质基板、谐振器和滤波器等微波器件的制造,可满足移动通信、卫星通信等系统的技术需要。
表1:
Figure 2013104346466100002DEST_PATH_IMAGE001

Claims (1)

1.一种磷酸盐作为可低温烧结微波介电陶瓷的应用,其特征在于所述磷酸盐的化学组成式为:Ca3Bi(PO4)3;
所述磷酸盐的制备方法具体步骤为:
(1)将纯度为99.9%以上的CaCO3、Bi2O3和P2O5的原始粉末按Ca3Bi(PO4)3化学式称量配料;
(2)将步骤(1)原料湿式球磨混合12小时,溶剂为蒸馏水,烘干后在750℃大气气氛中预烧6小时;
(3)在步骤(2)制得的粉末中添加粘结剂并造粒后,再压制成型,最后在840~870℃大气气氛中烧结4小时;所述的粘结剂采用质量浓度为5%的聚乙烯醇溶液,剂量占粉末总质量的3%。
CN201310434646.6A 2013-09-23 2013-09-23 可低温烧结的微波介电陶瓷Ca3Bi(PO4)3及其制备方法 Expired - Fee Related CN103496964B (zh)