CN103492329B - 玻璃板的制造方法 - Google Patents

玻璃板的制造方法 Download PDF

Info

Publication number
CN103492329B
CN103492329B CN201380000355.4A CN201380000355A CN103492329B CN 103492329 B CN103492329 B CN 103492329B CN 201380000355 A CN201380000355 A CN 201380000355A CN 103492329 B CN103492329 B CN 103492329B
Authority
CN
China
Prior art keywords
brick
glass
molten tin
quality
oxide compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201380000355.4A
Other languages
English (en)
Chinese (zh)
Other versions
CN103492329A (zh
Inventor
三浦丈宜
谷井史朗
林泰夫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Inc
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Publication of CN103492329A publication Critical patent/CN103492329A/zh
Application granted granted Critical
Publication of CN103492329B publication Critical patent/CN103492329B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B18/00—Shaping glass in contact with the surface of a liquid
    • C03B18/02—Forming sheets
    • C03B18/16—Construction of the float tank; Use of material for the float tank; Coating or protection of the tank wall
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B18/00—Shaping glass in contact with the surface of a liquid
    • C03B18/02—Forming sheets
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
    • C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium
    • C03C3/093—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium containing zinc or zirconium
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/10—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on aluminium oxide
    • C04B35/101—Refractories from grain sized mixtures
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/10—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on aluminium oxide
    • C04B35/101—Refractories from grain sized mixtures
    • C04B35/106—Refractories from grain sized mixtures containing zirconium oxide or zircon (ZrSiO4)
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3201—Alkali metal oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3206—Magnesium oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3208—Calcium oxide or oxide-forming salts thereof, e.g. lime
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P40/00—Technologies relating to the processing of minerals
    • Y02P40/50—Glass production, e.g. reusing waste heat during processing or shaping
    • Y02P40/57—Improving the yield, e-g- reduction of reject rates

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Ceramic Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Structural Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Glass Compositions (AREA)
CN201380000355.4A 2012-03-27 2013-02-15 玻璃板的制造方法 Active CN103492329B (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012072495 2012-03-27
JP2012-072495 2012-03-27
PCT/JP2013/053756 WO2013145922A1 (fr) 2012-03-27 2013-02-15 Procédé de fabrication d'une plaque de verre

Publications (2)

Publication Number Publication Date
CN103492329A CN103492329A (zh) 2014-01-01
CN103492329B true CN103492329B (zh) 2015-12-02

Family

ID=49259204

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201380000355.4A Active CN103492329B (zh) 2012-03-27 2013-02-15 玻璃板的制造方法

Country Status (5)

Country Link
JP (1) JPWO2013145922A1 (fr)
KR (1) KR101384375B1 (fr)
CN (1) CN103492329B (fr)
TW (1) TW201339110A (fr)
WO (1) WO2013145922A1 (fr)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015224150A (ja) * 2014-05-27 2015-12-14 旭硝子株式会社 無アルカリガラスの製造方法
JP2016098160A (ja) * 2014-11-25 2016-05-30 旭硝子株式会社 フロートガラス製造装置、およびフロートガラス製造方法
DE102017124625A1 (de) * 2016-12-22 2018-06-28 Schott Ag Dünnglassubstrat, Verfahren und Vorrichtung zu dessen Herstellung

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5420087A (en) * 1993-02-17 1995-05-30 Didier-Werke Ag Refractory or fireproof brick as tin bath bottom brick
CN1898168A (zh) * 2003-12-26 2007-01-17 旭硝子株式会社 无碱玻璃、其制造方法及液晶显示板

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07109129A (ja) * 1993-10-12 1995-04-25 Yootai:Kk フロートバス内張用耐火れんが
JP3988209B2 (ja) * 1996-06-03 2007-10-10 旭硝子株式会社 無アルカリガラスおよび液晶ディスプレイパネル
JP4612331B2 (ja) * 2004-04-30 2011-01-12 オーセラ株式会社 フロートバス用耐火材及びフロートバス
JP4789058B2 (ja) * 2004-06-23 2011-10-05 日本電気硝子株式会社 無アルカリガラス基板
TW200927686A (en) * 2007-10-25 2009-07-01 Asahi Glass Co Ltd Method for production of non-alkali glass
JP5446030B2 (ja) * 2007-12-19 2014-03-19 日本電気硝子株式会社 ガラス基板

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5420087A (en) * 1993-02-17 1995-05-30 Didier-Werke Ag Refractory or fireproof brick as tin bath bottom brick
CN1898168A (zh) * 2003-12-26 2007-01-17 旭硝子株式会社 无碱玻璃、其制造方法及液晶显示板

Also Published As

Publication number Publication date
CN103492329A (zh) 2014-01-01
KR101384375B1 (ko) 2014-04-10
TW201339110A (zh) 2013-10-01
KR20130119441A (ko) 2013-10-31
JPWO2013145922A1 (ja) 2015-12-10
WO2013145922A1 (fr) 2013-10-03

Similar Documents

Publication Publication Date Title
US9309139B2 (en) High volume production of display quality glass sheets having low zirconia levels
KR102696612B1 (ko) 유리판 및 그 제조 방법
EP2398745A1 (fr) « isopipe » à base de spinelle utilisé pour la fabrication par fusion de plaques de verre contenant des alcalis
CN103492329B (zh) 玻璃板的制造方法
US11584680B2 (en) Alkali-free glass substrate
CN104876425A (zh) 用于制造浮法玻璃板的浮法工艺和浮法玻璃板
JPWO2020071193A1 (ja) 無アルカリガラス板
WO2019124271A1 (fr) Procédé de production d'une plaque de verre
TW201345849A (zh) 玻璃板
CN107709252B (zh) 玻璃基板的制造方法及玻璃基板制造装置
US10974986B2 (en) Alkali-free glass substrate
CN115667159B (zh) 最小化在贵金属系统中制造的玻璃中的结晶铑-铂缺陷的形成
US11718553B2 (en) Alkali-free glass substrate
KR102080003B1 (ko) 유리판의 제조 방법 및 유리판
TWI850202B (zh) 無鹼玻璃基板
KR102702560B1 (ko) 유리 기판
CN104487390B (zh) 玻璃板的制造方法以及玻璃板
KR20220072779A (ko) 무알칼리 유리 기판 및 무알칼리 플로트 유리 기판의 제조 방법
JP2020158382A (ja) 無アルカリガラス基板
CN104114505A (zh) 平板玻璃制造装置和平板玻璃制造方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CP01 Change in the name or title of a patent holder

Address after: Tokyo, Japan

Patentee after: AGC Corporation

Address before: Tokyo, Japan

Patentee before: Asahi Glass Co., Ltd.

CP01 Change in the name or title of a patent holder