CN103483739A - Non-poisonous PVC transparent soft bottle - Google Patents
Non-poisonous PVC transparent soft bottle Download PDFInfo
- Publication number
- CN103483739A CN103483739A CN201310437869.8A CN201310437869A CN103483739A CN 103483739 A CN103483739 A CN 103483739A CN 201310437869 A CN201310437869 A CN 201310437869A CN 103483739 A CN103483739 A CN 103483739A
- Authority
- CN
- China
- Prior art keywords
- parts
- transparent soft
- soft bottle
- poisonous
- pvc transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a non-poisonous PVC transparent soft bottle which comprises the following components in parts by mass: 100 parts of PVC, 2-4 parts of AMS, 30-40 parts of DOP, 15-20 parts of MBS, 0.3-0.5 part of Hst, 0.5-1 part of calcium stearate, 0.5-1 part of PDOP, 1-3 parts of ESBO, 1.5-4.5 parts of TVS-8831, 0.5-1 part of mercaptan dioctyltin, 10-15 parts of ABS, 5-10 parts of ACR-201 and 0.2-0.5 part of pigment. The non-poisonous PVC transparent soft bottle has high transparency, 88-90% of light transmittance and fewer smell, is non-poisonous and harmless, acid-base resistant and wear resistant, can be produced widely and continuously replaces the existing materials; the vicat softening point of the non-poisonous PVC transparent soft bottle is 90-100 DEG C, and the tensile strength of the non-poisonous PVC transparent soft bottle is 70-80 MPa.
Description
Technical field
The application belongs to the plastic material field, relates in particular to the transparent soft bottle of a kind of nontoxic PVC.
Background technology
That positive PVC transparent article has is transparent, good looking appearance, be difficult for broken, lightweight, corrosion-resistant, be easy to the advantage such as printing, can make up the shortcomings such as Glass breadks easily, polyethylene transparency be poor.Therefore, at home and abroad developed rapidly, especially in makeup, medicine, food plant wet goods packing, occupied more and more consequence.At home, along with the raising of living standards of the people, increasing to the demand of polyvinyl chloride transparent goods.For satisfying the market needs, improve China's packing of product level, save foreign exchange, Tianjin laboratory in modern age proposes the plan about development PVC clear vial pellet, and lists city PVC one continuous line brainstorm project in through Municipal Economic and Trade Commission's approval.This development work succeeds, and since trial production last year and identifying production, each batch of product all can reach standard-required.
PVC belongs to the basic chemical industry raw material, and product differentiation is less, and under the market structure of perfect competition, cost is just the main factor that affects enterprise competitiveness at home.Due to industrial nature, occupy high specific weight in starting material and energy workinprocess cost, along with the development of social city, technicalization, hommization, design a kind of transparency high, the soft bottle of nontoxic PVC, to meet the need of market, is very important.
Summary of the invention
the technical problem solved:
The application hangs down and the technical problems such as toxicity is large for the transparent soft bottle transparency of existing nontoxic PVC, and the transparent soft bottle of a kind of nontoxic PVC is provided.
technical scheme:
The transparent soft bottle of a kind of nontoxic PVC, be comprised of following raw materials according, take the mass fraction representation as PVC100 part; AMS2-4 part; DOP30-40 part; MBS15-20 part; Hst0.3-0.5 part; Calcium stearate 0.5-1 part; PDOP0.5-1 part; ESBO is 1-3 part; TVS-8831 is 1.5-4.5 part; Mercaptan dioctyltin 0.5-1 part; ABS10-15 part; ACR-201 is 5-10 part; Pigment 0.2-0.5 part.
As a preferred technical solution of the present invention: the transparent soft bottle of described nontoxic PVC, its moiety, the mass fraction representation of take be take the mass fraction representation as PVC100 part as: its composition; AMS3 part; DOP35 part; MBS18 part; Hst0.4 part; 0.7 part of calcium stearate; PDOP0.8 part; ESBO is 2 parts; TVS-8831 is 3 parts; 0.7 part of mercaptan dioctyltin; ABS12 part; ACR-201 is 8 parts; 0.3 part of pigment.
beneficial effect:
The transparent soft bottle of a kind of nontoxic PVC of the present invention adopts above technical scheme compared with prior art, and have following technique effect: 1, the product transparency is high, and transmittance is up to 88%-90%; 2, nontoxic, product odour is little; 3, Vicat softening point 90-100 ℃, tensile strength 70-80MPa; 4, product acid and alkali-resistance, wear-resisting, can the not division of history into periods of widespread production replace current material.
Embodiment
embodiment 1:
A kind of nontoxic PVC transparent soft bottle, its composition be take the mass fraction representation as PVC100 part; AMS2-4 part; DOP30-40 part; MBS15-20 part; Hst0.3-0.5 part; Calcium stearate 0.5-1 part; PDOP0.5-1 part; ESBO is 1-3 part; TVS-8831 is 1.5-4.5 part; Mercaptan dioctyltin 0.5-1 part; ABS10-15 part; ACR-201 is 5-10 part; Pigment 0.2-0.5 part.
Transmittance is up to 88%; 90 ℃ of Vicat softening points, tensile strength 70MPa.
embodiment 2:
A kind of nontoxic PVC transparent soft bottle, its composition be take the mass fraction representation as PVC100 part; AMS2-4 part; DOP30-40 part; MBS15-20 part; Hst0.3-0.5 part; Calcium stearate 0.5-1 part; PDOP0.5-1 part; ESBO is 1-3 part; TVS-8831 is 1.5-4.5 part; Mercaptan dioctyltin 0.5-1 part; ABS10-15 part; ACR-201 is 5-10 part; Pigment 0.2-0.5 part.
Transmittance is up to 90%; 95 ℃ of Vicat softening points, tensile strength 75MPa.
embodiment 3:
The transparent soft bottle of a kind of nontoxic PVC is characterized in that: its composition be take the mass fraction representation as PVC100 part; AMS3 part; DOP35 part; MBS18 part; Hst0.4 part; 0.7 part of calcium stearate; PDOP0.8 part; ESBO is 2 parts; TVS-8831 is 3 parts; 0.7 part of mercaptan dioctyltin; ABS12 part; ACR-201 is 8 parts; 0.3 part of pigment.
Transmittance is up to 90%; 100 ℃ of Vicat softening points, tensile strength 80MPa.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, therefore in the implication suitable with claims of the present invention and any change in scope, all should think to be included in the scope of claims.
Claims (2)
1. the transparent soft bottle of a nontoxic PVC is characterized in that: its composition be take the mass fraction representation as PVC100 part; AMS2-4 part; DOP30-40 part; MBS15-20 part; Hst0.3-0.5 part; Calcium stearate 0.5-1 part; PDOP0.5-1 part; ESBO is 1-3 part; TVS-8831 is 1.5-4.5 part; Mercaptan dioctyltin 0.5-1 part; ABS10-15 part; ACR-201 is 5-10 part; Pigment 0.2-0.5 part.
2. the transparent soft bottle of a kind of nontoxic PVC according to claim 1 is characterized in that: its composition be take the mass fraction representation as PVC100 part; AMS3 part; DOP35 part; MBS18 part; Hst0.4 part; 0.7 part of calcium stearate; PDOP0.8 part; ESBO is 2 parts; TVS-8831 is 3 parts; 0.7 part of mercaptan dioctyltin; ABS12 part; ACR-201 is 8 parts; 0.3 part of pigment.