CN103469579A - 一种锦纶纤维帘子线浸胶液 - Google Patents

一种锦纶纤维帘子线浸胶液 Download PDF

Info

Publication number
CN103469579A
CN103469579A CN 201310380721 CN201310380721A CN103469579A CN 103469579 A CN103469579 A CN 103469579A CN 201310380721 CN201310380721 CN 201310380721 CN 201310380721 A CN201310380721 A CN 201310380721A CN 103469579 A CN103469579 A CN 103469579A
Authority
CN
China
Prior art keywords
parts
soft water
component
naoh
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201310380721
Other languages
English (en)
Inventor
沈明
刘瑞强
张功明
魏爱云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG LUPU TECHNOLOGY Co Ltd
Original Assignee
SHANDONG LUPU TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG LUPU TECHNOLOGY Co Ltd filed Critical SHANDONG LUPU TECHNOLOGY Co Ltd
Priority to CN 201310380721 priority Critical patent/CN103469579A/zh
Publication of CN103469579A publication Critical patent/CN103469579A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种锦纶纤维帘子线浸胶液，涉及浸胶液配方领域，包括A和B两部分组分，所述A组分包含有如下重量份数的原料:甲醛1.26-2.34、间苯二酚1.42-2.16、氢氧化钠0.04-0.06、软水21.4-23.6；所述B组分包含有如下重量份数的原料：丁吡胶乳16.98-18.08、天然胶乳34.2-35.95、氢氧化钠0.027-0.044、软水18.7-21.4。本发明配方简单，浸胶过程比较容易，得到的浸胶液性能稳定，具有较高的强度和较好的性能，成本低廉。

Description

一种锦纶纤维帘子线浸胶液
技术领域
本发明涉及浸胶液配方领域，具体的说是一种锦纶纤维帘子线浸胶液。
背景技术
锦纶纤维线可用于多种场合，通常锦纶纤维线是由锦纶纤维单丝浸胶后捻合而成，但不同的浸胶液对锦纶纤维线的强度和性能有不同的效果。锦纶帘子线与橡胶的粘合力，直接决定了轮胎的使用性能和使用寿命，一般的锦纶帘子线很难与橡胶发生物理和化学性的粘结，通常浸胶液浸润性能差。
发明内容
为解决上述存在的技术问题，本发明提供了一种锦纶纤维帘子线浸胶液，浸胶过程简单，浸胶液强度高，性能好。
为达到上述目的，本发明所采用的技术方案是：
一种锦纶纤维帘子线浸胶液，包括A和B两部分组分，
所述A组分包含有如下重量份数的原料: 甲醛1.26-2.34、 间苯二酚1.42-2.16、氢氧化钠0.04-0.06、软水21.4-23.6；
所述B组分包含有如下重量份数的原料：丁吡胶乳16.98-18.08、天然胶乳34.2-35.95、氢氧化钠0.027-0.044、软水18.7-21.4。
作为优选的方案，所述A组分包含有如下重量份数的原料: 甲醛1.28-2.34、 间苯二酚1.42-2.16、氢氧化钠0.04-0.05、软水21.4-22.6；
所述B组分包含有如下重量份数的原料：丁吡胶乳17.98-18.02、天然胶乳34.2-34.95、氢氧化钠0.028-0.044、软水18.8-21.4。
本发明配方简单，浸胶过程比较容易，得到的浸胶液性能稳定，具有较高的强度和较好的性能，成本低廉,极易与橡胶发生物理和化学性的粘结，浸胶液浸润性能好。
具体实施方式
下面结合具体实施例对本发明进行详细描述：
实施例1：
所述A组分包含有如下重量份数的原料: 甲醛1.28、 间苯二酚1.42、氢氧化钠0.04、软水21.4；
所述B组分包含有如下重量份数的原料：丁吡胶乳17.98、天然胶乳34.2、氢氧化钠0.028、软水18.8。
取1.28份的甲醛、1.42份的间苯二酚和0.04份的氢氧化钠，在一定条件下预混合，形成两者的预缩合物然后加入21.4份的软水，使得两者进一步反应，获得可溶性粘合剂，即为A组分。该粘合剂对橡胶本体具有较强的粘合力，可使锦纶纤维帘子线在高强度下仍能与橡胶本体很好的结合并增强帘子线的强度；然后取17.98份的丁吡胶乳、34.2份的天然胶乳、0.028份的氢氧化钠和18.8份的软水，在一定条件下混合即得B组分，将A和B两组分混合，B组分的加入进一步增强了浸胶液的粘合力，取一定量的锦纶纤维长丝在上述混合液中进行浸胶，初捻捻度为80捻/米，复捻捻度为85捻/米，所得帘子线具有较高强度。
实施例2：
所述A组分包含有如下重量份数的原料: 甲醛1.26、 间苯二酚1.52、氢氧化钠0.05、软水22.4；
所述B组分包含有如下重量份数的原料：丁吡胶乳16.98、天然胶乳35.2、氢氧化钠0.027、软水18.7。
取1.26份的甲醛、1.52份的间苯二酚和0.05份的氢氧化钠，在一定条件下预混合，形成两者的预缩合物然后加入22.4份的软水，使得两者进一步反应，获得可溶性粘合剂，即为A组分。该粘合剂对橡胶本体具有较强的粘合力，可使锦纶纤维帘子线在高强度下仍能与橡胶本体很好的结合并增强帘子线的强度；然后取16.98份的丁吡胶乳、35.2份的天然胶乳、0.027份的氢氧化钠和18.7份的软水，在一定条件下混合即得B组分，将A和B两组分混合，B组分的加入进一步增强了浸胶液的粘合力，取一定量的锦纶纤维长丝在上述混合液中进行浸胶，初捻捻度为80捻/米，复捻捻度为85捻/米，所得帘子线具有较高强度。
实施例3：
所述A组分包含有如下重量份数的原料: 甲醛2.34、 间苯二酚2.16、氢氧化钠0.06、软水23.6；
所述B组分包含有如下重量份数的原料：丁吡胶乳18.08、天然胶乳35.95、氢氧化钠0.044、软水21.4。
取2.34份的甲醛、2.16份的间苯二酚和0.06份的氢氧化钠，在一定条件下预混合，形成两者的预缩合物然后加入23.6份的软水，使得两者进一步反应，获得可溶性粘合剂，即为A组分。该粘合剂对橡胶本体具有较强的粘合力，可使锦纶纤维帘子线在高强度下仍能与橡胶本体很好的结合并增强帘子线的强度；然后取18.08份的丁吡胶乳、35.95份的天然胶乳、0.044份的氢氧化钠和21.4份的软水，在一定条件下混合即得B组分，将A和B两组分混合，B组分的加入进一步增强了浸胶液的粘合力，取一定量的锦纶纤维长丝在上述混合液中进行浸胶，初捻捻度为80捻/米，复捻捻度为85捻/米，所得帘子线具有较高强度。
实施例4：
所述A组分包含有如下重量份数的原料: 甲醛2.34、 间苯二酚1.42、氢氧化钠0.06、软水21.4；
所述B组分包含有如下重量份数的原料：丁吡胶乳18.08、天然胶乳34.2、氢氧化钠0.044、软水18.7。
取2.34份的甲醛、1.42份的间苯二酚和0.06份的氢氧化钠，在一定条件下预混合，形成两者的预缩合物然后加入21.4份的软水，使得两者进一步反应，获得可溶性粘合剂，即为A组分。该粘合剂对橡胶本体具有较强的粘合力，可使锦纶纤维帘子线在高强度下仍能与橡胶本体很好的结合并增强帘子线的强度；然后取18.08份的丁吡胶乳、34.2份的天然胶乳、0.044份的氢氧化钠和18.7份的软水，在一定条件下混合即得B组分，将A和B两组分混合，B组分的加入进一步增强了浸胶液的粘合力，取一定量的锦纶纤维长丝在上述混合液中进行浸胶，初捻捻度为80捻/米，复捻捻度为85捻/米，所得帘子线具有较高强度。
当然，上述说明并非是对本发明的限制，本发明也并不仅限于上述举例，本技术领域的技术人员在本发明的实质范围内所做出的变化、改型、添加或替换，也应属于本发明的保护范围。

Claims (2)

1.一种锦纶纤维帘子线浸胶液，其特征在于，包括A和B两部分组分，
所述A组分包含有如下重量份数的原料: 甲醛1.26-2.34、 间苯二酚1.42-2.16、氢氧化钠0.04-0.06、软水21.4-23.6；
所述B组分包含有如下重量份数的原料：丁吡胶乳16.98-18.08、天然胶乳34.2-35.95、氢氧化钠0.027-0.044、软水18.7-21.4。
2.根据权利要求1所述的一种锦纶纤维帘子线浸胶液，其特征在于，
所述A组分包含有如下重量份数的原料: 甲醛1.28-2.34、 间苯二酚1.42-2.16、氢氧化钠0.04-0.05、软水21.4-22.6；
所述B组分包含有如下重量份数的原料：丁吡胶乳17.98-18.02、天然胶乳34.2-34.95、氢氧化钠0.028-0.044、软水18.8-21.4。
CN 201310380721 2013-08-28 2013-08-28 一种锦纶纤维帘子线浸胶液 Pending CN103469579A (zh)