CN103469560A - 抗紫外线纯棉织物的整理方法 - Google Patents
抗紫外线纯棉织物的整理方法 Download PDFInfo
- Publication number
- CN103469560A CN103469560A CN2013103657237A CN201310365723A CN103469560A CN 103469560 A CN103469560 A CN 103469560A CN 2013103657237 A CN2013103657237 A CN 2013103657237A CN 201310365723 A CN201310365723 A CN 201310365723A CN 103469560 A CN103469560 A CN 103469560A
- Authority
- CN
- China
- Prior art keywords
- uvioresistant
- finishing agent
- parts
- pure cotton
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗紫外线纯棉织物的整理方法,包括如下步骤:将棉织物通过轧槽,在80~95℃下同时加入含有复合抗菌整理剂的浸渍液,浸轧车速控制在20~50米/分钟;然后将织物在115~130℃之间恒温0.5~2小时;降至常温后用中和剂水洗至pH值为6.5~6.8,烘干即得到所述抗紫外线纯棉织物;所述抗紫外线整理剂由如下重量份的组分组成:二氧化硅30~40份、沸石5~8份、2,4-二羟基二苯甲酮10~15份、N,N-二正丁基二硫代氨基甲酸镍20~25份、聚丙烯酸钠分散剂0.8-1.2份。本发明兼具两种抗紫外线整理剂的优点,可和纯棉织物牢固结合,耐久性强,对纯棉织物有优良的防紫外作用,无毒安全。
Description
技术领域
本发明涉及一种抗紫外线纯棉织物的整理方法。
背景技术
一般来说,适当的紫外线对人体是有益的,它能促进维生素D的合成,对佝偻病有抑制作用,并具有消毒杀菌作用。但近年来,由于人类生产和生活大量地排放氟里昂之类的氯氟化烃化合物,使地球的保护伞即大气层日益遭到破坏,特别是在地球两极及我国青藏高原上空出现了臭氧空洞,地球的保护圈即臭氧层变薄变稀,到达地面的紫外线辐射量增多,因过度的紫外线照射引起的疾病越来越多。一般情况下,人体皮肤所能接受紫外线的安全辐射量每天应在20kJ/m2以内,而紫外线到达地面的辐射量阴天时约40~60kJ/m2,晴天时约80~100kJ/m2,炎夏烈日时可达100~200kJ/m2,普通衣料对紫外线的遮蔽率一般在50%左右,远远达不到防护要求。另外,长期的紫外线照射也会引起纺织品的褪色和老化。因此,有必要对纺织品进行抗紫外线整理。
光照射到物体上时,一部分被物体表面反射;部分被物体吸收;其他的则透过物体。具有紫外线防护功能的纤维及制品,当紫外光照射时,除其中的一部分从纤维织物上的孔隙透过外(其透过量视织物的组织和厚度等不同),其他的不是被紫外线防护剂反射,就是被选择性吸收,并将其能量转换成热能释放,以达到将减少紫外线的目的。严格地讲,能将紫外线反射的物质叫紫外线屏蔽剂,对紫外线有强烈选择性吸收并能进行能量转换而减少它的透过量的物质叫紫外线吸收剂。但实际上屏蔽与吸收同时存在,它们从不同的途径提高了纤维及纺织品的紫外线防护功能。
纤维种类不同,其紫外线透过率也不同。棉、真丝等天然纤维对紫外线的吸收能力低,因而抗紫外线线性能差,其中棉织物是紫外线最易透过的面料。
目前常用的抗紫外线整理剂分无机和有机两大类。常用的抗紫外线整理剂大多是金属、金属氧化物及其盐类,例如TiO2、ZnO、Al2O3、高岭土、滑石粉、炭黑、氧化铁、氧化亚铅和CaCO3等。无机抗紫外线整理剂和织物纤维结合能力较差。有机抗紫外线整理剂主要是吸收紫外线并进行能量转换,将紫外线变成低能量的热能或波长较短的电磁波,从而达到抗紫外线辐射的目的。一般具有共轭结构或氢键。该类抗紫外线整理剂具有一定毒性。
开发一种即无毒安全、又具有优异耐久性的抗紫外线棉织物成为重要的研究课题。
发明内容
本发明要解决的技术问题是提供一种抗紫外线纯棉织物的整理方法,以克服现有技术存在的上述缺陷。
为解决上述技术问题,本发明抗紫外线纯棉织物的整理方法,包括如下步骤:将棉织物通过轧槽,在80~95℃下同时加入含有复合抗菌整理剂的浸渍液,浸轧车速控制在20~50米/分钟;然后将织物在115~130℃之间恒温0.5~2小时;降至常温后用中和剂水洗至pH值为6.5~6.8,烘干即得到所述抗紫外线纯棉织物;所述抗紫外线整理剂由如下重量份的组分组成:
抗紫外线整理剂可采用一般的混合方法,优选采用如下方法制备:
将2,4-二羟基二苯甲酮、N,N-二正丁基二硫代氨基甲酸镍和沸石混合,然后同时缓慢加入二氧化硅和聚丙烯酸钠分散剂,1~2小时内投料完毕,继续混合20~30分钟。
作为一种优选方案,所述二氧化硅的粒径为0.05-0.12微米。
抗紫外线整理剂各组分混合后加水配成质量含量不低于15%的浸渍液;优选配成质量含量35~50%的浸渍液。
所述聚丙烯酸钠分散剂优选粘度300~350mPa·s。
本发明将无机和有机类抗紫外线整理剂有机结合,精选特定的助剂复合而成,兼具两种抗紫外线整理剂的优点,可和纯棉织物牢固结合,耐久性强,对纯棉织物有优良的防紫外作用,无毒安全。
具体实施方式
实施例1
抗紫外线整理剂的制备:
将2,4-二羟基二苯甲酮10克、N,N-二正丁基二硫代氨基甲酸镍25克和沸石6克混合,然后同时缓慢加入粒径为0.10微米的二氧化硅30克和聚丙烯酸钠分散剂0.9克,1小时内投料完毕,继续混合20分钟。然后加水配制成质量含固量为40%的浸渍液。
抗紫外线织物的整理:
将棉织物通过轧槽,在95℃下同时加入含有复合抗菌整理剂的浸渍液,浸轧车速控制在20米/分钟;然后将织物在115℃之间恒温2小时;降至常温后用中和剂水洗至pH值为6.5,烘干即得到所述抗紫外线纯棉织物。
实施例2
抗紫外线整理剂的制备:
将2,4-二羟基二苯甲酮15克、N,N-二正丁基二硫代氨基甲酸镍20克和沸石5克混合,然后同时缓慢加入二氧化硅40克和聚丙烯酸钠分散剂1.2克,1小时内投料完毕,继续混合30分钟。然后加水配制成质量含固量为35%的浸渍液。
抗紫外线织物的整理:
将棉织物通过轧槽,在80℃下同时加入含有复合抗菌整理剂的浸渍液,浸轧车速控制在50米/分钟;然后将织物在130℃之间恒温0.5小时;降至常温后用中和剂水洗至pH值为6.8,烘干即得到所述抗紫外线纯棉织物。
应用实施例
1、耐久性
将织物用含1克/升的中性洗涤剂以1:50的织物与洗涤剂溶液的比例,在60℃左右洗涤30分钟,离心机脱水后60℃左右干燥。按上述方法分别洗涤5次、30次。
2、抗紫外线性能
按照国家标准GB-T18830-2002《纺织品抗紫外线性能的评定》的方法测定织物在不同洗涤条件下的抗紫外线性能,结果如下:
表1不同洗涤次数后的抗紫外线性能
表中a表示未经洗涤的织物,b表示洗涤5次,c表示洗涤30次。
可见,本发明纯棉织物的抗紫外线效果优异,并且具有优良的耐水洗性能,经多次洗涤后仍具有良好的抗紫外线性能。
Claims (6)
2.根据权利要求1所述的方法,其特征在于,抗紫外线整理剂采用如下方法制备:将2,4-二羟基二苯甲酮、N,N-二正丁基二硫代氨基甲酸镍和沸石混合,然后同时缓慢加入二氧化硅和聚丙烯酸钠分散剂,1~2小时内投料完毕,继续混合20~30分钟。
3.根据权利要求1所述的方法,其特征在于,所述二氧化硅的粒径为0.05-0.12微米。
4.根据权利要求1所述的方法,其特征在于,抗紫外线整理剂各组分混合后加水配成质量含量不低于15%的浸渍液。
5.根据权利要求1所述的方法,其特征在于,抗紫外线整理剂各组分混合后加水配成质量含量35~50%的浸渍液。
6.根据权利要求1所述的方法,其特征在于,所述聚丙烯酸钠分散剂粘度300~350mPa·s。