CN103469436A - Preparation method for elastic force weaving shell fabric - Google Patents
Preparation method for elastic force weaving shell fabric Download PDFInfo
- Publication number
- CN103469436A CN103469436A CN201310436677.5A CN201310436677A CN103469436A CN 103469436 A CN103469436 A CN 103469436A CN 201310436677 A CN201310436677 A CN 201310436677A CN 103469436 A CN103469436 A CN 103469436A
- Authority
- CN
- China
- Prior art keywords
- preparation
- elastic
- woven fabrics
- shell fabric
- elastic force
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for the elastic force weaving shell fabric. The preparation method takes 70-count mercerized wool, terylene and chinlon as raw materials and comprises the following steps to obtain the elastic force shell fabric: a) spinning, b) dyeing, c) weaving and d) after finishing. The raw materials are in the following blending ratio: 40% of mercerized wool, 35% of terylene and 25% of chinlon. The elastic force shell fabric prepared with the method has the breadth of 160cm and the gram density of 180g/m<2>. The preparation method for the elastic force weaving shell fabric, which is disclosed by the invention, has the characteristics of simple working procedure and easiness in implementation. According to the reasonable selection and the scientific proportioning design of the raw materials, the prepared shell fabric is comfortable, soft, elastic and fashionable, and has the characteristics of wear resistance, thermal insulation as well as stiff and smooth appearance.
Description
Technical field
The present invention relates to the fabric technical field, particularly relate to a kind of preparation method of elastic woven fabrics.
Background technology
At present, along with people are more and more higher to the requirement of quality of life, degree comfortable and easy to wear and the image appearance of clothes are also had higher requirement.The performances such as elastic fabric is capable of expansion and contraction because having, comfortable fittingness, catered to the comfortable arbitrarily and conveniently life style of modern.In addition, inevitably there is the defect on performance in the elastic fabric of single component, and as spinnability, weave difficulty or ease, ABRASION RESISTANCE and warmth retention property etc., therefore, prepare by the plurality of raw materials blending height approval that multi-functional elastic fabric will be subject to the consumer.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of preparation method of elastic woven fabrics, can weave high resilience, soft, wear-resisting and warming comprehensive elastic fabric.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: the preparation method that a kind of elastic woven fabrics is provided, it is raw material that this preparation method adopts 70 mercerized wools, terylene and polyamide fibres, be woven into elastic fabric through following steps: a) spinning, b) dyeing, e) weave, d) the rear arrangement; The blending rate of described raw material is: mercerising hair 40%, terylene 35%, polyamide fibre 25%; Elastic fabric fabric width 160cm prepared by described method, gram density 180g/m
2.
In a preferred embodiment of the present invention, in described step a), spinning process is: wool top, grilling, rove, spun yarn, winder, doubling, double twisting, yarn steaming; Wherein, the described twist is: single thread 700 sth. made by twisting/m, two yarn 1050 sth. made by twisting/m; The line density of described blended yarn is 18.3tex.
In a preferred embodiment of the present invention, in described step b), colouring method is disperse dyeing, and dyeing temperature is 120 ℃, and temperature retention time is 60min.
In a preferred embodiment of the present invention, in described step c), weaving process is: warping, gait, weave, the grey cloth check, give birth to and repair; Wherein, described being woven on air-jet loom undertaken by twill-weave, and the loom speed of a motor vehicle is 600 rev/mins, warp tension 420N, and upper machine fabric width is 165cm.
In a preferred embodiment of the present invention, in described step d), finishing process comprises: crabbing, oven dry, formalize, singe, open washing, oven dry, ripely repair, scald light, decatizing, finished product.
The invention has the beneficial effects as follows: the preparation method of a kind of elastic woven fabrics of the present invention, this preparation method's operation is easy, easy to implement, by the choose reasonable of raw material and the proportion design of science, the fabric made has comfortable softness, high resilience, the characteristics such as wear-resisting, warming, be rich in well-pressed profile simultaneously, there is fashion, popular characteristic.
The accompanying drawing explanation
Fig. 1 is the preparation method's of a kind of elastic woven fabrics of the present invention process flow diagram.
The specific embodiment
Below in conjunction with accompanying drawing, preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
Refer to Fig. 1, the embodiment of the present invention comprises:
A kind of preparation method of elastic woven fabrics, it is raw material that this preparation method adopts 70 mercerized wools, terylene and polyamide fibres, blending rate is: mercerising hair 40%, terylene 35%, polyamide fibre 25%; Wool add the good hand feeling degree that can improve fabric, can improve the thermal property of fabric simultaneously; Terylene has excellent anti-wear performance, improves taking the life-span of fabric; Polyamide fibre is the king of elastomer, and it is soft, be easy to the characteristics such as dyeing, high resilience, also has the characteristics such as well-pressed.
A) spinning, spinning process is: wool top, grilling, rove, spun yarn, winder, doubling, double twisting, yarn steaming; Wherein, the described twist is: single thread 700 sth. made by twisting/m, two yarn 1050 sth. made by twisting/m; The line density of described blended yarn is 18.3tex.
B) dyeing, colouring method is disperse dyeing, and dyeing temperature is 120 ℃, and temperature retention time is 60min.
C) weave, weaving process is: warping, gait, weave, the grey cloth check, give birth to and repair; Wherein, described being woven on air-jet loom undertaken by twill-weave, and the loom speed of a motor vehicle is 600 rev/mins, warp tension 420N, and upper machine fabric width is 165cm.
D) after, arrange, finishing process comprises: crabbing, oven dry, formalize, singe, open washing, oven dry, ripely repair, scald light, decatizing, finished product.
Elastic fabric fabric width 160cm prepared by said method, gram density 180g/m
2, this fabric has comfortable softness, high resilience, the characteristics such as wear-resisting, warming, is rich in well-pressed profile simultaneously, has fashion, popular characteristic.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes specification of the present invention and accompanying drawing content to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in scope of patent protection of the present invention.
Claims (5)
1. the preparation method of an elastic woven fabrics, is characterized in that, it is raw material that this preparation method adopts 70 mercerized wools, terylene and polyamide fibres, through following steps, is woven into elastic fabric: a) spinning, and b) dyeing, e) weave, d) the rear arrangement; The blending rate of described raw material is: mercerising hair 40%, terylene 35%, polyamide fibre 25%; Elastic fabric fabric width 160cm prepared by described method, gram density 180g/m
2.
2. the preparation method of elastic woven fabrics according to claim 1, is characterized in that, in described step a), spinning process is: wool top, grilling, rove, spun yarn, winder, doubling, double twisting, yarn steaming; Wherein, the described twist is: single thread 700 sth. made by twisting/m, two yarn 1050 sth. made by twisting/m; The line density of described blended yarn is 18.3tex.
3. the preparation method of elastic woven fabrics according to claim 1, is characterized in that, in described step b), colouring method is disperse dyeing, and dyeing temperature is 120 ℃, and temperature retention time is 60min.
4. the preparation method of elastic woven fabrics according to claim 1, is characterized in that, in described step c), weaving process is: warping, gait, weave, the grey cloth check, give birth to and repair; Wherein, described being woven on air-jet loom undertaken by twill-weave, and the loom speed of a motor vehicle is 600 rev/mins, warp tension 420N, and upper machine fabric width is 165cm.
5. the preparation method of elastic woven fabrics according to claim 1, is characterized in that, in described step d), finishing process comprises: crabbing, oven dry, formalize, singe, open washing, oven dry, ripely repair, scald light, decatizing, finished product.