CN103469044A - 一种铜铝铁合金材料 - Google Patents
一种铜铝铁合金材料 Download PDFInfo
- Publication number
- CN103469044A CN103469044A CN2013103713909A CN201310371390A CN103469044A CN 103469044 A CN103469044 A CN 103469044A CN 2013103713909 A CN2013103713909 A CN 2013103713909A CN 201310371390 A CN201310371390 A CN 201310371390A CN 103469044 A CN103469044 A CN 103469044A
- Authority
- CN
- China
- Prior art keywords
- sillman
- alloy material
- bronze material
- alloy
- impelling strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种铜铝铁合金材料，铜铝铁合金材料由以下成分组成：Cu为12wt%～14wt%、Mg为5wt%～11wt%、Mn为0.7wt%～1.3wt%、Cr为3wt%～4wt%、Ir为0.13wt%～0.22wt%、Al为34wt%～56wt%、余量为Fe。制备得到的铜铝铁合金材料具有很高的冲击韧性。
Description
技术领域
本发明涉及一种合金材料，特别是涉及一种铜铝铁合金材料。
背景技术
在合金材料受到外部冲击时，合金材料的韧性大小和抗冲击能力非常关键，如果韧性较差，抗冲击能力较小，则会对合金材料的质构产生破坏性影响。此时，如果合金材料具有非常高的冲击韧性，则可以避免上述危害的产生。目前，提高合金材料的冲击韧性，是相关领域研究的一个热点，如何能够大幅度提高合金材料的冲击韧性，是困扰着相关领域技术人员的一个难点。
发明内容
要解决的技术问题：普通合金材料冲击韧性低的问题。
技术方案：本发明公开了一种铜铝铁合金材料，合金材料由以下成分组成：Cu为12 wt%～14wt%、Mg为5wt%～11wt%、Mn为0.7 wt%～1.3wt%、Cr为3wt%～4wt%、Ir为0.13wt%～0.22wt%、Al为34wt%～56wt%、余量为Fe。制备得到的铜铝铁合金材料具有很高的冲击韧性。合金材料制备步骤如下：取所需的各化学成分，按照上述重量比例将所有成分投入至融炼炉中，保持真空，进行冶炼，加热温度至1150℃，加热后热轧成合金板，再将温度缓慢降低至室温，降温速率为40℃/s，制备得到铜铝铁合金材料。
有益效果：本发明制备得到的铜铝铁合金材料具有非常高的冲击韧性。铜铝铁合金材料的测试标准为GB/T1817-1995，冲击韧性值为630至660J，具有良好的冲击韧性。可以用于抵抗外力的冲击。
具体实施方式
实施例1
取所需的各化学成分，Cu为14wt%、Mg为11wt%、Mn为1.3wt%、Cr为3wt%、Ir为0.13wt%、Al为34wt%、余量为Fe。将所有成分投入至融炼炉中，保持真空，进行冶炼，加热温度至1150℃，加热后热轧成合金板，再将温度缓慢降低至室温，降温速率为40℃/s，制备得到铜铝铁合金材料。
实施例2
制备方法同实施例1，各成分组成比例为：Cu为12wt%、Mg为5wt%、Mn为0.7wt%、Cr为3.5wt%、Ir为0.17wt%、Al为45wt%、余量为Fe。
实施例3
制备方法同实施例1，各成分组成比例为：Cu为13wt%、Mg为8wt%、Mn为1.0wt%、Cr为4wt%、Ir为0.22wt%、Al为56wt%、余量为Fe。
对实施例1、实施例2、实施例3的产品进行了冲击韧性测试。测试的标准为GB/T1817-1995，实施例1、实施例2、实施例3产品的冲击韧性值分别为630J、645J、660J，具有良好的冲击韧性。
Claims (5)
1.一种铜铝铁合金材料，其特征在于铜铝铁合金材料由以下成分组成：Cu为12 wt%～14wt%、Mg为5wt%～11wt%、Mn为0.7 wt%～1.3wt%、Cr为3wt%～4wt%、Ir为0.13wt%～0.22wt%、Al为34wt%～56wt%、余量为Fe。
2.根据权利要求1所述的铜铝铁合金材料，其特征在于铜铝铁合金材料组成中Cu为14wt%。
3.根据权利要求1所述的铜铝铁合金材料，其特征在于铜铝铁合金材料组成中Mn为0.7wt%。
4.根据权利要求1所述的铜铝铁合金材料，其特征在于铜铝铁合金材料组成中Cr为3wt%。
5.根据权利要求1所述的铜铝铁合金材料，其特征在于铜铝铁合金材料组成中Ir为0.13wt%。