CN103465587A - 高强度复合面料的制备方法 - Google Patents

高强度复合面料的制备方法 Download PDF

Info

Publication number
CN103465587A
CN103465587A CN2013103656179A CN201310365617A CN103465587A CN 103465587 A CN103465587 A CN 103465587A CN 2013103656179 A CN2013103656179 A CN 2013103656179A CN 201310365617 A CN201310365617 A CN 201310365617A CN 103465587 A CN103465587 A CN 103465587A
Authority
CN
China
Prior art keywords
polyester filament
tack coat
composite bed
polyester
coated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103656179A
Other languages
English (en)
Inventor
蒋建业
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN TIENIU SHIRT FACTORY
Original Assignee
KUNSHAN TIENIU SHIRT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN TIENIU SHIRT FACTORY filed Critical KUNSHAN TIENIU SHIRT FACTORY
Priority to CN2013103656179A priority Critical patent/CN103465587A/zh
Publication of CN103465587A publication Critical patent/CN103465587A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高强度复合面料的制备方法，包括如下步骤：在基布一侧涂布第一粘结层，然后将涤纶长丝纤维层通过热压贴和在第一粘结层上，再涂布第二粘结层，最后将PE/PP复合层热压贴和在第二粘结层上；所述涤纶长丝纤维层中的涤纶长丝纤维通过如下方法制备：将PET聚酯熔融后，加入乙二醇和二氧化锗催化剂的混合液，进行醇解重聚反应，控制反应产物粘度为0.7-0.8dl/g，进入纺丝箱体进行纺丝，纺丝箱体温度为300℃-350℃。本发明采用复合热压方式形成高强度复合面料，加工路线简单，易操作，成本低，易于工业化生产。

Description

高强度复合面料的制备方法
技术领域
本发明涉及一种制备具有高强度的复合型面料的方法。
背景技术
特斯林面料是无梭织机生产的特种纺织品，经纬均采用特殊包覆结构的复合纱线，即PVC/PET皮芯型纱线。该类面料具有表面光滑、防水防油、耐磨、使用寿命长等优点。但是制造需特种设备，工艺较复杂，且主要采用的PVC材料中含有氯乙烯单体，有一定毒害性。
发明内容
本发明要解决的技术问题是提供一种高强度复合面料的制备方法，以克服现有技术存在的上述缺陷。
为解决上述技术问题，本发明所述高强度复合面料的制备方法，包括如下步骤：在基布一侧涂布第一粘结层，然后将涤纶长丝纤维层通过热压贴和在第一粘结层上，再涂布第二粘结层，最后将PE/PP复合层热压贴和在第二粘结层上；所述涤纶长丝纤维层中的涤纶长丝纤维通过如下方法制备：将PET聚酯熔融后，加入乙二醇和二氧化锗催化剂的混合液，进行醇解重聚反应，控制反应产物粘度为0.7-0.8dl/g，进入纺丝箱体进行纺丝，纺丝箱体温度为300℃-350℃。
优选地是,所述乙二醇的用量为PET聚酯重量百分比的1-2%，所述二氧化锗催化剂的用量为PET聚酯重量百分比的0.01-0.025%。
优选地是,所述第一和第二粘结层为含有粘结剂的涂层，所述粘结剂采用常规粘结剂即可。
优选地是,所述PE/PP复合层为PE和PP按照质量比10：3-10的共聚材料。
优选地是,PE/PP复合层中还可以添加颜料。
优选地是,所述基布厚度为0.22-0.25mm，粘结剂层厚度为0.03-0.05mm，涤纶长丝纤维层厚度为0.12-0.15mm，PE/PP复合层厚度为0.2-0.25mm。
本发明制备的高强度复合面料采用PE/PP复合材料取代PVC材料，环保安全，并且采用复合热压方式形成高强度复合面料，加工路线简单，易操作，成本低，易于工业化生产。表面光滑、防水防油、耐磨、使用寿命长、无毒安全。
具体实施方式
实施例1
高强度复合面料的制备：
在基布一侧涂布第一粘结层，然后将涤纶长丝纤维层通过热压贴和在第一粘结层上，再涂布第二粘结层，最后将PE/PP复合层热压贴和在第二粘结层上。所述基布厚度为0.22mm，粘结剂层厚度为0.05mm，涤纶长丝纤维层厚度为0.15mm，PE/PP复合层厚度为0.2mm。
所述涤纶长丝纤维层中的涤纶长丝纤维通过如下方法制备：将PET聚酯熔融后，加入乙二醇和二氧化锗催化剂的混合液，进行醇解重聚反应，控制反应产物粘度为0.7dl/g，进入纺丝箱体进行纺丝，纺丝箱体温度为300℃℃。所述乙二醇的用量为PET聚酯重量百分比的1%，所述二氧化锗催化剂的用量为PET聚酯重量百分比的0.01%。
所述PE/PP复合层为PE和PP按照质量比10：3的共聚材料。
实施例2
高强度复合面料的制备：
在基布一侧涂布第一粘结层，然后将涤纶长丝纤维层通过热压贴和在第一粘结层上，再涂布第二粘结层，最后将PE/PP复合层热压贴和在第二粘结层上。所述基布厚度为0.25mm，粘结剂层厚度为0.03mm，涤纶长丝纤维层厚度为0.12mm，PE/PP复合层厚度为0.25mm。
所述涤纶长丝纤维层中的涤纶长丝纤维通过如下方法制备：将PET聚酯熔融后，加入乙二醇和二氧化锗催化剂的混合液，进行醇解重聚反应，控制反应产物粘度为0.8dl/g，进入纺丝箱体进行纺丝，纺丝箱体温度为350℃。所述乙二醇的用量为PET聚酯重量百分比的2%，所述二氧化锗催化剂的用量为PET聚酯重量百分比的0.025%。
所述PE/PP复合层为PE和PP按照质量比1：1的共聚材料。

Claims (5)

1.一种高强度复合面料的制备方法，其特征在于，包括如下步骤：在基布一侧涂布第一粘结层，然后将涤纶长丝纤维层通过热压贴和在粘结层上，再涂布第二粘结层，最后将PE/PP复合层热压贴和在第二粘结层上；所述涤纶长丝纤维层中的涤纶长丝纤维通过如下方法制备：将PET聚酯熔融后，加入乙二醇和二氧化锗催化剂的混合液，进行醇解重聚反应，控制反应产物粘度为0.7-0.8dl/g，进入纺丝箱体进行纺丝，纺丝箱体温度为300℃-350℃。
2.根据权利要求1所述的方法，其特征在于，所述乙二醇的用量为PET聚酯的1-2%，所述二氧化锗催化剂的用量为PET聚酯0.01-0.025%。
3.根据权利要求1所述的方法，其特征在于，所述PE/PP复合层为PE和PP按照质量比10：3-10的共聚材料。
4.根据权利要求1所述的方法，其特征在于，在PE/PP复合层中添加颜料。
5.根据权利要求1所述的方法，其特征在于，所述基布厚度为0.22-0.25mm，所述第一粘结层和第二粘结层厚度为0.03-0.05mm，涤纶长丝纤维层厚度为0.12-0.15mm，PE/PP复合层厚度为0.2-0.25mm。
CN2013103656179A 2013-08-21 2013-08-21 高强度复合面料的制备方法 Pending CN103465587A (zh)