CN103465392B - The treatment process of junked tire - Google Patents
The treatment process of junked tire Download PDFInfo
- Publication number
- CN103465392B CN103465392B CN201310423505.4A CN201310423505A CN103465392B CN 103465392 B CN103465392 B CN 103465392B CN 201310423505 A CN201310423505 A CN 201310423505A CN 103465392 B CN103465392 B CN 103465392B
- Authority
- CN
- China
- Prior art keywords
- tire
- rubber powder
- polishing
- specially
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The treatment process of a kind of junked tire of the present invention, comprises 1. cleaning, 2. pulverizing, 3. steam drying, 4. screens, 5. adds pitch, 6. to the drying of modified rubber powder indirect steam method, 7. compressing tablet.Can effective Reaction time shorten, reduce the discharge of pollutant in production process, thus well solve some problems in background technology, and achieve the circulation Appropriate application of resource.
Description
Technical field
The present invention relates to junked tire processing technology field, be specifically related to a kind for the treatment of process of junked tire.
Background technology
Along with automobile becomes the first engine pulling consumption of resident gradually, China is own through facing the Heavy environmental pollution problem that junked tire causes.According to relevant report, China becomes the 3rd automobile after the U.S., Japan and produces the country surpassing ten million per year, becomes genuine " automobile superpower ".But, together arrive with auto age, also have the junked tire that pile up like a mountain.In the country of intense industrialization, because the understanding of the pollution problem to modern society improves rapidly, the ideology of people also trends towards uphold nature gradually, so, waste and used rubber tyre is also become to the focus of people's words.In line with the treatment principle of refuse being carried out to innoxious, minimizing, resource, in the world the process Utilizing question of junked tire is more and more come into one's own at present.The process of junked tire and recycling thereof are the difficult problems attracted attention in the world.Along with developing rapidly of auto industry, the problem of junked tire environmental pollution is on the rise, and has caused people to pay close attention to, junked tire is difficult to biodegradation, can select to destroy by fire or long-term air storage, be embedded in the flowing that underground can hinder air and water, therefore be not suitable for filling out reason process; Pile up like a mountain on the ground, takies a large amount of soil, also can because of ponding the raw mosquito of evil and germ, thus causing the severe contamination of environment, is again the initiating accident sequence of fire, how disposal and utilization junked tire, has become the environmental objective being badly in need of solving.According to statistics, the U.S. about produces 2.5-3.0 more than hundred million every year.Therefore, developed country attaches great importance to recovery and the problem of complex utilization of junked tire, both avoids environmental pollution in the hope of reaching, and can make again the object of resource regeneration.
As can be seen here, the method for process solid waste such as stacking, fill out reason, destroy by fire is all inapplicable to junked tire.Therefore, how to process the focus that newborn " black pollution " solid waste becomes New Times society's discussion and pays close attention to, invention describes the treatment process of junked tire.
Summary of the invention
Object of the present invention is exactly defect for above-mentioned existence and provides a kind for the treatment of process of junked tire, can effective Reaction time shorten, reduce the discharge of pollutant in production process, thus well solve some problems in background technology, and achieve the circulation Appropriate application of resource.
The treatment process technical scheme of junked tire of the present invention is, comprises 1. cleaning, 2. pulverizing, 3. steam drying, 4. screens, 5. adds pitch, 6. to the drying of modified rubber powder indirect steam method, 7. compressing tablet.
1. step is specially, the silt on cleaning sidewall, tire top and greasy dirt, the foreign material such as rubble, screw in removing tyre surface.
2. step is specially, and starts pulverizer oil pump, mixes up reductor gear, is placed in by cleaned tire on tire drum, start swelling switch, tire is anchored on tire drum, polishing gear host-initiated, take out dirt fan starting, open emery wheel top cooling water, cooling water is shape spray; Start wheel hub to advance switch, tire moves to polishing tooth, enters duty after 10 seconds, 3-5 to start polishing second and pulverizes, and main frame polishing tooth and tire subtend are turned round, and tread rubber scrapes by huge shearing force, the tread rubber scraped shows Powdered, collects through spiral separator sedimentation.When within 1-2 minute, cord ply is exposed on polishing tire top, namely return wheel hub, stop, utilize spiral separator to collect rubber powder.
3. step is specially, and then carries out indirect steam drying to rubber powder, baking temperature 40-100 DEG C, drying time 1-5 hour.
4. step is specially, with 30-60 object sieve screening rubber powder.
5. step is specially, and then adds asphalt modification rubber powder.
6. step is specially, and use indirect steam method to carry out drying, temperature 50-70 DEG C to modified rubber powder, the time is 1-2 hour.
7. step is specially, mill thin-pass modified glue powder, roll spacing at 0.1-0.2mm, after 8-15 time, compressing tablet.
7. step is specially, mill thin-pass modified glue powder, after 10 times, and compressing tablet.
The modified glue powder adopting present invention process to prepare can be mixed in multiple rubber compounding, is applied to production.
Beneficial effect of the present invention is: junked tire treatment process of the present invention effectively can process junked tire, treatment process is simple, eliminate public hazards, decreasing pollution, turn waste into wealth and have positive effect for environmental protection, decrease the discharge of waste gas waste water simultaneously, the modified glue powder adopting present invention process to prepare can be mixed in multiple rubber compounding, be applied to rubber production, can production cost be effectively reduced.
detailed description of the invention:
In order to understand the present invention better, describe technical scheme of the present invention in detail with instantiation below, but the present invention is not limited thereto.
Embodiment 1
1. step is specially, the silt on cleaning sidewall, tire top and greasy dirt, the foreign material such as rubble, screw in removing tyre surface.
2. step is specially, and starts pulverizer oil pump, mixes up reductor gear, is placed in by cleaned tire on tire drum, start swelling switch, tire is anchored on tire drum, polishing gear host-initiated, take out dirt fan starting, open emery wheel top cooling water, cooling water is shape spray; Start wheel hub to advance switch, tire moves to polishing tooth, enters duty after 10 seconds, 3-5 to start polishing second and pulverizes, and main frame polishing tooth and tire subtend are turned round, and tread rubber scrapes by huge shearing force, the tread rubber scraped shows Powdered, collects through spiral separator sedimentation.When within 1-2 minute, cord ply is exposed on polishing tire top, namely return wheel hub, stop, utilize spiral separator to collect rubber powder.
3. step is specially, and then carries out indirect steam drying to rubber powder, baking temperature 50 DEG C, 3 hours drying times.
4. step is specially, with 30 object sieve screening rubber powders.
5. step is specially, and then adds asphalt modification rubber powder.
6. step is specially, and use indirect steam method to carry out drying, temperature 60 C to modified rubber powder, the time is 1-2 hour.
7. step is specially, mill thin-pass modified glue powder, roll spacing at 0.1-0.2mm, after 10 times, compressing tablet.
The modified glue powder adopting present invention process to prepare can be mixed in multiple rubber compounding, is applied to production.
Embodiment 2:
1. step is specially, the silt on cleaning sidewall, tire top and greasy dirt, the foreign material such as rubble, screw in removing tyre surface.
2. step is specially, and starts pulverizer oil pump, mixes up reductor gear, is placed in by cleaned tire on tire drum, start swelling switch, tire is anchored on tire drum, polishing gear host-initiated, take out dirt fan starting, open emery wheel top cooling water, cooling water is shape spray; Start wheel hub to advance switch, tire moves to polishing tooth, enters duty after 10 seconds, 3-5 to start polishing second and pulverizes, and main frame polishing tooth and tire subtend are turned round, and tread rubber scrapes by huge shearing force, the tread rubber scraped shows Powdered, collects through spiral separator sedimentation.When within 1-2 minute, cord ply is exposed on polishing tire top, namely return wheel hub, stop, utilize spiral separator to collect rubber powder.
3. step is specially, and then carries out indirect steam drying to rubber powder, baking temperature 60 DEG C, 4 hours drying times.
4. step is specially, with 60 object sieve screening rubber powders.
5. step is specially, and then adds asphalt modification rubber powder.
6. step is specially, and use indirect steam method to carry out drying, temperature 70 C to modified rubber powder, the time is 1.5 hours.
7. step is specially, mill thin-pass modified glue powder, roll spacing at 0.1-0.2mm, after 8 times, compressing tablet.
The modified glue powder adopting present invention process to prepare can be mixed in multiple rubber compounding, is applied to production.
Embodiment 3:
1. step is specially, the silt on cleaning sidewall, tire top and greasy dirt, the foreign material such as rubble, screw in removing tyre surface.
2. step is specially, and starts pulverizer oil pump, mixes up reductor gear, is placed in by cleaned tire on tire drum, start swelling switch, tire is anchored on tire drum, polishing gear host-initiated, take out dirt fan starting, open emery wheel top cooling water, cooling water is shape spray; Start wheel hub to advance switch, tire moves to polishing tooth, enters duty after 10 seconds, 3-5 to start polishing second and pulverizes, and main frame polishing tooth and tire subtend are turned round, and tread rubber scrapes by huge shearing force, the tread rubber scraped shows Powdered, collects through spiral separator sedimentation.When within 1-2 minute, cord ply is exposed on polishing tire top, namely return wheel hub, stop, utilize spiral separator to collect rubber powder.
3. step is specially, and then carries out indirect steam drying to rubber powder, baking temperature 40 DEG C, 5 hours drying times.
4. step is specially, with 30 object sieve screening rubber powders.
5. step is specially, and then adds asphalt modification rubber powder.
6. step is specially, and use indirect steam method to carry out drying, temperature 70 C to modified rubber powder, the time is 1 hour.
7. step is specially, mill thin-pass modified glue powder, roll spacing at 0.1-0.2mm, after 12 times, compressing tablet.
The modified glue powder adopting present invention process to prepare can be mixed in multiple rubber compounding, is applied to production.
Embodiment 4:
1. step is specially, the silt on cleaning sidewall, tire top and greasy dirt, the foreign material such as rubble, screw in removing tyre surface.
2. step is specially, and starts pulverizer oil pump, mixes up reductor gear, is placed in by cleaned tire on tire drum, start swelling switch, tire is anchored on tire drum, polishing gear host-initiated, take out dirt fan starting, open emery wheel top cooling water, cooling water is shape spray; Start wheel hub to advance switch, tire moves to polishing tooth, enters duty after 10 seconds, 3-5 to start polishing second and pulverizes, and main frame polishing tooth and tire subtend are turned round, and tread rubber scrapes by huge shearing force, the tread rubber scraped shows Powdered, collects through spiral separator sedimentation.When within 1-2 minute, cord ply is exposed on polishing tire top, namely return wheel hub, stop, utilize spiral separator to collect rubber powder.
3. step is specially, and then carries out indirect steam drying to rubber powder, baking temperature 100 DEG C, 1 hour drying time.
4. step is specially, with 60 object sieve screening rubber powders.
5. step is specially, and then adds asphalt modification rubber powder.
6. step is specially, and use indirect steam method to carry out drying, temperature 50 C to modified rubber powder, the time is 2 hours.
7. step is specially, mill thin-pass modified glue powder, roll spacing at 0.1-0.2mm, after 8 times, compressing tablet.
The modified glue powder adopting present invention process to prepare can be mixed in multiple rubber compounding, is applied to production.
Claims (2)
1. a treatment process for junked tire, is characterized in that, comprises the following steps:
1. clean;
The silt on cleaning sidewall, tire top and greasy dirt, the foreign material in removing tyre surface;
2. pulverize;
Start pulverizer oil pump, mix up reductor gear, be placed in by cleaned tire on tire drum, start swelling switch, be anchored on by tire on tire drum, polishing gear host-initiated, take out dirt fan starting, open emery wheel top cooling water, cooling water is shape spray; Start wheel hub to advance switch, tire moves to polishing tooth, enters duty after 10 seconds, 3-5 to start polishing second and pulverizes, and main frame polishing tooth and tire subtend are turned round, and tread rubber scrapes by huge shearing force, the tread rubber scraped shows Powdered, collects through spiral separator sedimentation; When within 1-2 minute, cord ply is exposed on polishing tire top, namely return wheel hub, stop, utilize spiral separator to collect rubber powder;
3. steam drying;
Then indirect steam drying is carried out to rubber powder, baking temperature 40-100 DEG C, drying time 1-5 hour;
4. screen;
With 30-60 object sieve screening rubber powder;
5. pitch is added;
Then asphalt modification rubber powder is added;
6. dry to modified rubber powder indirect steam method;
Use indirect steam method to carry out drying, temperature 50-70 DEG C to modified rubber powder, the time is 1-2 hour;
7. compressing tablet;
Mill thin-pass modified glue powder, roll spacing at 0.1-0.2mm, after 8-15 time, compressing tablet.
2. the treatment process of junked tire according to claim 1, is characterized in that, 7. step is specially, mill thin-pass modified glue powder, after 10 times, and compressing tablet.