CN103450764A - 一种塑料漆的加工方法 - Google Patents
一种塑料漆的加工方法 Download PDFInfo
- Publication number
- CN103450764A CN103450764A CN 201210171144 CN201210171144A CN103450764A CN 103450764 A CN103450764 A CN 103450764A CN 201210171144 CN201210171144 CN 201210171144 CN 201210171144 A CN201210171144 A CN 201210171144A CN 103450764 A CN103450764 A CN 103450764A
- Authority
- CN
- China
- Prior art keywords
- resin
- plastic paint
- butanone
- processing method
- ethylene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种塑料漆的加工方法,包括下列加工步骤:(1)备料:热塑性丙烯酸树脂:20%-25%;醋酸乙烯共聚物树脂:5%-8%;异丁醇4%-7%;纤维素树脂:5%-12%;液态甲苯:12%-20%;丁酮7%-15%;二丙酮醇2%-5%;丁脂:10%-18%;(2)、按上述物料配料:将丁脂、液态甲苯加入容器中混合;再按上述比例依次加入热塑性丙烯酸树脂、丁酮、异丁醇、醋酸乙烯共聚物树脂、纤维素树脂、二丙酮醇,在摄氏20度-35度温度下搅拌30分钟,转速每分钟800至1200转,得到塑料漆;(3)、加入各种颜色的色浆,配出各种颜色的塑料漆。本发明生产设备简单,便于操作,使用方便。
Description
技术领域
本发明涉及一种涂料,特别是涉及一种塑料漆的加工方法。
背景技术
塑料包装盒在人们日常生活中很常用,为使外观更加美观,往往要在表面喷漆,由于有些塑料如聚乙烯塑胶不带静电离子,所以一般的涂料对它没有附着力,目前这类塑料喷涂前先做电极及初期处理,然后才能喷涂。
发明内容
本发明的目的就是提供一种塑料漆的加工方法,使用该方法生产的漆可以直接喷涂。
为达到上述目的,本发明采用下列技术方案:
一种塑料漆的加工方法,包括下列加工步骤:
(1)备料:
热塑性丙烯酸树脂:20%-25%;
醋酸乙烯共聚物树脂:5%-8%;
异丁醇4%-7%;
纤维素树脂:5%-12%;
液态甲苯:12%-20%;
丁酮7%-15%;
二丙酮醇2%-5%;
丁脂:10%-18%;
(2)、按上述物料配料:将丁脂、液态甲苯加入容器中混合;再按上述比例依次加入热塑性丙烯酸树脂、丁酮、异丁醇、醋酸乙烯共聚物树脂、纤维素树脂、二丙酮醇,在摄氏20度-35度温度下搅拌30分钟,转速每分钟800至1200转,得到塑料漆;
(3)、加入各种颜色的色浆,配出各种颜色的塑料漆。
本发明的有益效果:生产设备简单,便于操作,使用方便。
具体实施方式
实施例1:
一种塑料漆的加工方法,包括下列加工步骤:
(1)备料:
热塑性丙烯酸树脂::24%;
醋酸乙烯共聚物树脂:6%;
异丁醇6%;
纤维素树脂:12%;
液态甲苯:18%;
丁酮:13%;
二丙酮醇:4%;
丁脂:17%;
(2)、按上述物料配料:将丁脂、液态甲苯加入容器中混合;再按上述比例依次加入热塑性丙烯酸树脂、丁酮、异丁醇、醋酸乙烯共聚物树脂、纤维素树脂、二丙酮醇,在摄氏25度-温度下搅拌30分钟,转速每分钟1000转,得到塑料漆;
(3)、加入各种颜色的色浆,配出各种颜色的塑料漆。
实施例2:
一种塑料漆的加工方法,包括下列加工步骤:
(1)备料:
热塑性丙烯酸树脂:22%;
醋酸乙烯共聚物树脂:8%;
异丁醇5%;
纤维素树脂:12%;
液态甲苯:19%;
丁酮:12%;
二丙酮醇:5%;
丁脂:17%;
(2)、按上述物料配料:将丁脂、液态甲苯加入容器中混合;再按上述比例依次加入热塑性丙烯酸树脂、丁酮、异丁醇、醋酸乙烯共聚物树脂、纤维素树脂、二丙酮醇,在摄氏25度温度下搅拌30分钟,转速每分钟1000转,得到塑料漆;
(3)、加入各种颜色的色浆,配出各种颜色的塑料漆。
Claims (1)
1.一种塑料漆的加工方法,包括下列加工步骤:
(1)备料:
热塑性丙烯酸树脂:20%-25%;
醋酸乙烯共聚物树脂:5%-8%;
异丁醇4%-7%;
纤维素树脂:5%-12%;
液态甲苯:12%-20%;
丁酮7%-15%;
二丙酮醇2%-5%;
丁脂:10%-18%;
(2)、按上述物料配料:将丁脂、液态甲苯加入容器中混合;再按上述比例依次加入热塑性丙烯酸树脂、丁酮、异丁醇、醋酸乙烯共聚物树脂、纤维素树脂、二丙酮醇,在摄氏20度-35度温度下搅拌30分钟,转速每分钟800至1200转,得到塑料漆;
(3)、加入各种颜色的色浆,配出各种颜色的塑料漆。