CN103450760A - 一种室内外金属制件用装饰漆及其加工工艺 - Google Patents
一种室内外金属制件用装饰漆及其加工工艺 Download PDFInfo
- Publication number
- CN103450760A CN103450760A CN2013104022310A CN201310402231A CN103450760A CN 103450760 A CN103450760 A CN 103450760A CN 2013104022310 A CN2013104022310 A CN 2013104022310A CN 201310402231 A CN201310402231 A CN 201310402231A CN 103450760 A CN103450760 A CN 103450760A
- Authority
- CN
- China
- Prior art keywords
- resistance
- container
- pigment
- indoor
- dimethylbenzene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种室内外金属制件用装饰漆及其加工工艺,包括成分的比重为46%-67%的热固性丙烯酸树脂,15-26%的丁醚化氨基树脂;7%-12%的颜料,0.09-0.2%的流平剂,0.1-0.3%的消泡剂,4.5%的丁醇,5%-8%的二甲苯,1%-2%CAC,其制作工艺,步骤为:将树脂和60%溶剂倒入容器中并开始搅拌,在搅拌的过程中依次加入颜料、助剂,充分搅拌均匀。送料泵抽入卧式砂磨机研磨,待研磨至20目左右,抽入容器搅拌20分钟后再加入剰余溶剂,直到所有的原料充分混合达到粘度至(涂-4、黏度计)80S-100S。效果是丰满亮丽,而且耐黄变性能好,耐候性强,并具有优异的耐磨、耐水、酸、盐及良好的腐蚀性。
Description
技术领域
本发明涉及用一种室内外金属制件用装饰漆,主要用于五金厂生产的室内外用钢制防盗门、铝合金门窗和其他小型钢铝制品上,可直接涂布于金属门窗材料的表面,经高温烘烤干燥后成漆膜,具有装饰用和防腐的双重功能。
背景技术
由于传统的溶剂型防盗门用漆采用的是醇酸树脂和氨基树脂做为主要基料,醇酸树脂本身的耐候性、耐水性不是很理想,造成防盗门表面漆膜易产生黄变、锈点等,不但影响了防盗门的外观装饰性能。
发明内容:
为了解决上述问题,本发明的目的是提供一种比传统的酸度酸氨基烘烤漆更加丰满亮丽,而且耐黄变性能好,耐候性强,并具有优异的耐磨、耐水、酸、盐及良好的腐蚀性,在室内外环境下的装饰性能和防腐效果有着令人满意的效果的室内外金属制件用装饰漆其加工工艺
本发明的技术方案是:一种室内外金属制件用装饰漆,各组分的质量百分比如下:
序号 | 原 料 名 称 | 投 料 量(wt%) |
1 | 热固性丙烯酸树脂 | 46-67 |
2 | 丁醚化氨基树脂 | 15-26 |
3 | 颜料 | 7-12 |
4 | 消泡剂 | 0.1-0.3 |
5 | 流平剂 | 0.09-0.2 |
6 | 二甲苯 | 5-8 |
7 | 正丁醇 | 4.5 |
8 | 乙二醇 醋酸酯 | 1-3 |
进一步,本发明的另一目的是提供上述装饰漆的制备方法,具体包括以下步骤:
首先,按照热固性丙烯酸树脂46-67 wt%、丁醚化氨基树脂15-26 wt%、颜料7-12 wt%、消泡剂0.1-0.3 wt%、流平剂0.09-0.2 wt%、二甲苯5-8 wt%、正丁醇4.5 wt%和乙二醇 醋酸酯1-3 wt%分别称取,将热固性丙烯酸树脂、丁醚化氨基树脂和由二甲苯、正丁醇和乙二醇醋酸酯组成有机溶剂总质量60%加入容器内启动设备,低速搅拌,依次将颜料粉、消泡剂和流平剂缓慢均匀加入到容器中,搅拌均匀,得到混合料,备用;
其次、通过送料泵将混合料抽入到砂磨机中进行研磨,充分分散后研磨至细度15目-20目,备用;
最后,将研磨好的混合料抽入容器中,搅拌20分钟后再加入剰余溶剂,充分混合调整粘度至涂-4、黏度计)80S-100S;待完全混匀后,出料罐装。
本发明的有益效果:由于采用上述技术方案,具有以下特点:
● 具有优异的施工性能 ;
● 大大减少了有机挥发物对环境的污染 ;
● 卓越的防水性和耐老化性能 ;
● 漆膜坚硬,具有耐冲击力,耐磨性和广泛的耐油性和耐溶剂性能 ;
● 能与大部分高性能防锈漆和面漆配套使用 ;
● 对基层层有很好的附着力 ;
● 在多种大气环境条件下具有优越的施工特性。
具体实施方式
下面结合具体实施例对本发明的技术方案做进一步说明。
实施例
具体实施方式
下面结合具体实施例对本发明的技术方案做进一步说明。
实施例1
首先,按照热固性丙烯酸树脂46 wt%、丁醚化氨基树脂26 wt%、颜料12 wt%、消泡剂0.3 wt%、流平剂0.2 wt%、二甲苯8 wt%、正丁醇4.5 wt%和乙二醇 醋酸酯3 wt%分别称取,将热固性丙烯酸树脂、丁醚化氨基树脂和由二甲苯、正丁醇和乙二醇醋酸酯组成有机溶剂总质量60%加入容器内启动设备,低速搅拌,依次将颜料粉、消泡剂和流平剂缓慢均匀加入到容器中,搅拌均匀,得到混合料,备用;
其次、通过送料泵将混合料抽入到砂磨机中进行研磨,充分分散后研磨至细度20目,备用;
最后,将研磨好的混合料抽入容器中,搅拌20分钟后再加入剰余溶剂,充分混合调整粘度至涂-4、黏度计)80S-100S;待完全混匀后,出料罐装。
实施例2
首先,按照热固性丙烯酸树脂67 wt%、丁醚化氨基树脂15wt%、颜料7 wt%、消泡剂0.1 wt%、流平剂0.09wt%、二甲苯5.31wt%、正丁醇4.5 wt%和乙二醇 醋酸酯1 wt%分别称取,将热固性丙烯酸树脂、丁醚化氨基树脂和由二甲苯、正丁醇和乙二醇醋酸酯组成有机溶剂总质量60%加入容器内启动设备,低速搅拌,依次将颜料粉、消泡剂和流平剂缓慢均匀加入到容器中,搅拌均匀,得到混合料,备用;
其次、通过送料泵将混合料抽入到砂磨机中进行研磨,充分分散后研磨至细度15目,备用;
最后,将研磨好的混合料抽入容器中,搅拌20分钟后再加入剰余溶剂,充分混合调整粘度至涂-4、黏度计)80S-100S;待完全混匀后,出料罐装。
实施例3
首先,按照热固性丙烯酸树脂57 wt%、丁醚化氨基树脂20 wt%、颜料9 wt%、消泡剂0.2 wt%、流平剂0.11 wt%、二甲苯6.5wt%、正丁醇4.5 wt%和乙二醇 醋酸酯2.6 wt%分别称取,将热固性丙烯酸树脂、丁醚化氨基树脂和由二甲苯、正丁醇和乙二醇醋酸酯组成有机溶剂总质量60%加入容器内启动设备,低速搅拌,依次将颜料粉、消泡剂和流平剂缓慢均匀加入到容器中,搅拌均匀,得到混合料,备用;
其次、通过送料泵将混合料抽入到砂磨机中进行研磨,充分分散后研磨至细度17目,备用;
最后,将研磨好的混合料抽入容器中,搅拌20分钟后再加入剰余溶剂,充分混合调整粘度至涂-4、黏度计)80S-100S;待完全混匀后,出料罐装。
Claims (2)
1.一种室内外金属制件用装饰漆,其特征在于,该装饰漆各组分的质量百分比如下:
。
2.一种如权利要求1所述的室内外金属制件用装饰漆的制备方法,其特征在于,具体包括以下步骤:
首先,按照热固性丙烯酸树脂46-67 wt%、丁醚化氨基树脂15-26 wt%、颜料7-12 wt%、消泡剂0.1-0.3 wt%、流平剂0.09-0.2 wt%、二甲苯5-8 wt%、正丁醇4.5 wt%和乙二醇 醋酸酯1-3 wt%分别称取,将热固性丙烯酸树脂、丁醚化氨基树脂和由二甲苯、正丁醇和乙二醇醋酸酯组成有机溶剂总质量的60%加入容器内启动设备,低速搅拌,依次将颜料粉、消泡剂和流平剂缓慢均匀加入到容器中,搅拌均匀,得到混合料,备用;
其次、通过送料泵将混合料抽入到砂磨机中进行研磨,充分分散后研磨至细度15目-20目,备用;
最后,将研磨好的混合料抽入容器中,搅拌20分钟后再加入剰余溶剂,充分混合调整粘度至涂-4、黏度计为80S-100S;待完全混匀后,出料罐装。