CN103450759A - 一种膨胀型防火颜料 - Google Patents
一种膨胀型防火颜料 Download PDFInfo
- Publication number
- CN103450759A CN103450759A CN2013103681541A CN201310368154A CN103450759A CN 103450759 A CN103450759 A CN 103450759A CN 2013103681541 A CN2013103681541 A CN 2013103681541A CN 201310368154 A CN201310368154 A CN 201310368154A CN 103450759 A CN103450759 A CN 103450759A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire retardant
- expansion fire
- flame
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种膨胀型防火颜料，其组分的重量份数为：丙烯酸树脂：20~25份、环氧一聚硫：21~24份、磷酸二氢铵：17~22份、醋酸锌：7~12份、聚磷酸铵钾：11~16、双氰胺：3~6；难燃剂：5~20份、发泡剂：5~20份、填料：3~15份。本发明克服了现有防火颜料阻燃能力以及阻止火焰传播差的缺点，具有当暴露于火焰上时，可产生阻燃能力，从而阻止火焰的传播。
Description
技术领域
本发明涉及防火颜料，特别涉及膨胀型防火涂。
背景技术
膨胀型防火颜料就是涂膜受热膨胀形成蜂窝状炭化层，使火焰热量受到隔离而减少或减缓对底材的传递，同时在高温时颜料分解出不燃气体，隔绝并稀释了空气，另外涂层在防火时发生的一系列物理和化学反应吸收了大量热量从而起到阻燃和延缓火焰扩展、蔓延，为人们提供灭火的时间。膨胀型防火颜料受热膨胀后，产生的多孔泡沫防御层，比原涂层厚几十甚至几百倍，且膨胀后泡沫层的导热系数比末膨胀前的涂层至少低一个数量级，涂得很薄就可达到很好的防火效果
现有的膨胀型防火颜料，当暴露于火焰上时，阻燃能力不够好，不能有效阻止火焰的传播。
发明内容
本发明的目的是提供一种综合性能优良的膨胀型防火颜料，具有非常优异的阻燃能力以及阻止火焰的传播能力。
为达到上述目的，本发明是通过以下的技术方案来实现的：一种膨胀型防火颜料，其组分的重量份数为：
丙烯酸树脂：20~25份；
环氧一聚硫：21~24份；
磷酸二氢铵：17~22份；
醋酸锌：7~12份；
聚磷酸铵钾：11~16；
双氰胺：3~6；
难燃剂：5~20份；
发泡剂：5~20份；
填料：3~15份。
进一步地，所述难燃剂为淀粉、或季戊四醇或蔗糖。
进一步地，所述发泡剂为三聚氰胺、氯化石蜡和磷酸三聚氰胺按照1:2:1混合的混合物。
进一步地，所述填料为碳酸钙、氢氧化铝和硼酸锌中至少一种。
本发明的有益效果是：本发明提供一种膨胀型防火颜料，克服了现有防火颜料阻燃能力以及阻止火焰传播差的缺点，具有当暴露于火焰上时，可产生阻燃能力，从而阻止火焰的传播。
具体实施方式
为更好地理解本发明，下面通过两个实施例对本发明作进一步具体的阐述，但不可理解为对本发明的限定，对于本领域的技术人员根据上述发明内容所作的一些非本质的改进与调整，也视为落在本发明的保护范围内。
实施例1
本实施例的一种膨胀型防火颜料，其组分的重量份数为：
丙烯酸树脂：25份；
环氧一聚硫：21份；
磷酸二氢铵：22份；
醋酸锌：7份；
聚磷酸铵钾：16；
双氰胺：6；
淀粉：20份；
碳酸钙：15份；
三聚氰胺、氯化石蜡和磷酸三聚氰胺按照1:2:1混合的混合物：20份。
实施例2
本实施例的一种膨胀型防火颜料，其组分的重量份数为：
丙烯酸树脂：20份；
环氧一聚硫：24份；
磷酸二氢铵：17份；
醋酸锌：12份；
聚磷酸铵钾：11；
双氰胺：3；
季戊四醇：5份；
碳酸钙：3份；
三聚氰胺、氯化石蜡和磷酸三聚氰胺按照1:2:1混合的混合物：5份。
实施例3
本实施例的一种膨胀型防火颜料，其组分的重量份数为：
丙烯酸树脂：23份；
环氧一聚硫：22份；
磷酸二氢铵：29份；
醋酸锌：11份；
聚磷酸铵钾：14；
双氰胺：5；
蔗糖：13份；
硼酸锌：13份；
三聚氰胺、氯化石蜡和磷酸三聚氰胺按照1:2:1混合的混合物：14份。
Claims (4)
1.一种膨胀型防火颜料，其特征在于，其组分的重量份数为：
丙烯酸树脂：20~25份；
环氧一聚硫：21~24份；
磷酸二氢铵：17~22份；
醋酸锌：7~12份；
聚磷酸铵钾：11~16；
双氰胺：3~6；
难燃剂：5~20份；
发泡剂：5~20份；
填料：3~15份。
2.根据权利要求1所述的一种膨胀型防火颜料，其特征在于，所述难燃剂为淀粉、或季戊四醇、或蔗糖。
3.根据权利要求1所述的一种膨胀型防火颜料，其特征在于，所述发泡剂为三聚氰胺、氯化石蜡和磷酸三聚氰胺按照1:2:1混合的混合物。
4.根据权利要求1所述的一种膨胀型防火颜料，其特征在于，所述填料为碳酸钙、氢氧化铝和硼酸锌中的至少一种。