CN103450417B - The floor material that a kind of high rigidity is withstand voltage - Google Patents
The floor material that a kind of high rigidity is withstand voltage Download PDFInfo
- Publication number
- CN103450417B CN103450417B CN201310367064.0A CN201310367064A CN103450417B CN 103450417 B CN103450417 B CN 103450417B CN 201310367064 A CN201310367064 A CN 201310367064A CN 103450417 B CN103450417 B CN 103450417B
- Authority
- CN
- China
- Prior art keywords
- floor material
- parts
- withstand voltage
- high rigidity
- methylethylketone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to the floor material that a kind of high rigidity is withstand voltage, floor material is made up of according to weight ratio following composition: polypropylene 26 ~ 28 parts, furane resin 9 ~ 13 parts, Magnesium hydrogen carbonate are 11 ~ 12 parts, Calcium Pyrophosphate is 7 ~ 9 parts, vinyl cyanide 11 ~ 13 parts, phenyl ether are 5 ~ 6 parts, methylethylketone is 3 ~ 5 parts.The floor material prepared has high rigidity and withstand voltage feature.
Description
Technical field
The present invention relates to a kind of floor material, particularly relate to the floor material that a kind of high rigidity is withstand voltage.
Background technology
The floor material of cleaning shop in use, can run into problems.Such as floor material due to hardness lower, the phenomenon of easily subsiding.Hardness is lower also can cause the irregular problem of floor material.If the hardness of floor material own is lower, compressive strength is also inadequate, then can govern the Application Areas of floor material greatly.By adding some other compositions, floor material being improved in hardness and voltage endurance capability, is the direction of a new research.
Summary of the invention
The technical problem solved: floor material hardness and compressive strength poor, limit its use in cleaning shop.
Technical scheme: the invention discloses the floor material that a kind of high rigidity is withstand voltage, floor material is made up of according to weight ratio following composition: polypropylene 26 ~ 28 parts, furane resin 9 ~ 13 parts, Magnesium hydrogen carbonate are 11 ~ 12 parts, Calcium Pyrophosphate is 7 ~ 9 parts, vinyl cyanide 11 ~ 13 parts, phenyl ether are 5 ~ 6 parts, methylethylketone is 3 ~ 5 parts.Terrace preparation method of the present invention is as follows: get polypropylene 26 ~ 28kg, furane resin 9 ~ 13kg, Magnesium hydrogen carbonate is 11 ~ 12kg, Calcium Pyrophosphate is 7 ~ 9kg, vinyl cyanide 11 ~ 13kg, phenyl ether be 5 ~ 6kg, methylethylketone is 3 ~ 5kg.Stirred at 80 DEG C by each composition, after insulation 1h, be cooled to room temperature after airtight, finished product is the withstand voltage floor material of high rigidity.
Beneficial effect: the present invention prepares terrace and has the advantage that hardness is high and compressive strength is high, can be applied in the terrace laying of cleaning shop.Wherein, the pencil hardness of floor material is 5H to 6H, and the compressive strength of floor material is 42 ~ 46Mpa.Be provided with good hardness and compressive strength.
Embodiment
Embodiment 1
Get polypropylene 28kg, furane resin 13kg, Magnesium hydrogen carbonate is 11kg, Calcium Pyrophosphate is 7kg, vinyl cyanide 11kg, phenyl ether be 5kg, methylethylketone is 5kg.Stirred at 80 DEG C by each composition, after insulation 1h, be cooled to room temperature after airtight, finished product is the withstand voltage floor material of high rigidity.
Embodiment 2
Preparation method is with embodiment 1, and in the present embodiment, each component content is: polypropylene 27kg, furane resin 11kg, Magnesium hydrogen carbonate are 12kg, Calcium Pyrophosphate is 8kg, vinyl cyanide 13kg, phenyl ether are 6kg, methylethylketone is 3kg.
Embodiment 3
Preparation method is with embodiment 1, and in the present embodiment, each component content is: polypropylene 26kg, furane resin 9kg, Magnesium hydrogen carbonate are 11kg, Calcium Pyrophosphate is 9kg, vinyl cyanide 12kg, phenyl ether are 5kg, methylethylketone is 4kg.
Floor material hardness compressive strength is tested
Its hardness of products measure of Example 1, embodiment 2, embodiment 3 and compressive strength, testing standard is GB/T6739-1996 and GB/T17671-1999.Test result sees the following form.
The pencil hardness of floor material is between 5H to 6H, and compressive strength is at 42 ~ 46Mpa.Be provided with good hardness and compressive strength, can on a large scale in cleaning shop.
Claims (5)
1. the floor material that a high rigidity is withstand voltage, it is characterized in that, floor material is made up of according to weight ratio following composition: polypropylene 26 ~ 28 parts, furane resin 9 ~ 13 parts, Magnesium hydrogen carbonate are 11 ~ 12 parts, Calcium Pyrophosphate is 7 ~ 9 parts, vinyl cyanide 11 ~ 13 parts, phenyl ether are 5 ~ 6 parts, methylethylketone is 3 ~ 5 parts; The preparation method of floor material is as follows: get polypropylene 26 ~ 28kg, furane resin 9 ~ 13kg, Magnesium hydrogen carbonate is 11 ~ 12kg, Calcium Pyrophosphate is 7 ~ 9kg, vinyl cyanide 11 ~ 13kg, phenyl ether be 5 ~ 6kg, methylethylketone is 3 ~ 5kg, each composition is stirred at 80 DEG C, after insulation 1h, be cooled to room temperature after airtight, finished product is the withstand voltage floor material of high rigidity.
2. the floor material that a kind of high rigidity according to claim 1 is withstand voltage, is characterized in that in floor material composition, polypropylene is 26 parts.
3. the floor material that a kind of high rigidity according to claim 1 is withstand voltage, is characterized in that in floor material composition, furane resin are 9 parts.
4. the floor material that a kind of high rigidity according to claim 1 is withstand voltage, is characterized in that in floor material composition, Magnesium hydrogen carbonate is 12 parts.
5. the floor material that a kind of high rigidity according to claim 1 is withstand voltage, is characterized in that in the middle of floor material composition, methylethylketone is 5 parts.