CN103449753A - 石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉 - Google Patents
石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉 Download PDFInfo
- Publication number
- CN103449753A CN103449753A CN 201210182578 CN201210182578A CN103449753A CN 103449753 A CN103449753 A CN 103449753A CN 201210182578 CN201210182578 CN 201210182578 CN 201210182578 A CN201210182578 A CN 201210182578A CN 103449753 A CN103449753 A CN 103449753A
- Authority
- CN
- China
- Prior art keywords
- parts
- mortar
- thickening
- plastering mortar
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉，它涉及建筑材料领域。它的配方组成为：高分子助剂1-2份，纤维素醚类增稠剂1-4份，改性多元醇减缩剂1-5份，聚羧酸类减水剂2-6份，聚丙烯纤维25-50份，木质纤维10-20份、矿渣150-250份、钠基膨润土280-340份、其余用粉煤灰补足；它的制备工艺为：将上述配方材料均匀混合而成；本发明能有效改善砂浆操作性、和易性、粘聚性，提供优良的稳定性和耐久性，满足机械施工的要求，提高工质量和效率；也能提高砂浆的韧性和抗裂性，有效解决砂浆易开裂的质量通病。
Description
技术领域：
本发明涉及建筑材料领域，具体涉及以石灰岩机制砂为细集料配制的干混抹灰砂浆抗裂砂浆增稠粉的配方及生产工艺。
背景技术：
近年来，随着建筑业技术的进步和文明施工要求的提高，节能环保的干混砂浆逐渐替代现场拌制砂浆成为抹灰工程的主要建筑材料之一。目前，建筑行业响应国家节能减排号召，鼓励使用建筑废料替代日渐枯竭的不可再生自然砂资源，拟使用在破碎石灰岩石生产过程中产生的储量大、价格优的石灰岩机制砂(粒径＜5mm)，但由于其石粉含量大，增加了砂浆拌制时的用水量，增加了干混砂浆收缩率，易导致砂浆开裂，影响干混砂浆的质量。
干混砂浆作为一种脆性材料，在以一定厚度涂抹于基体表面的过程中，由于基层含水率和平整度的差异，与基层接触的砂浆硬化速度不同，而砂浆涂抹厚度不均匀，易引起砂浆内部应力分布不均。在砂浆层凝结硬化过程中，随着水泥的水化、环境温度和湿度等变化，砂浆与基层、砂浆内部、砂浆与空气接触面出现应力差，产生收缩变形。砂浆硬化后，长期处于冷热冻融循环、干湿循环、化学侵蚀等外在环境的影响，不断地产生温度变形、干湿变形和化学变形，最终导致砂浆开裂。特别是随着加气混凝土砌块、空心砌块、轻质砖等新型墙体材料的大力推广和应用，建筑物墙身抹灰开裂等质量问题频频出现。
因此，针对砂浆内应力大、收缩变形明显等问题，研制砂浆增韧、抗裂的实用材料，避免砂浆开裂，将进一步扩大干混砂浆的应用范围和市场接受度。
发明内容：
本发明的目的是提供解决石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉，它能有效改善砂浆操作性、和易性、粘聚性，提供优良的稳定性和耐久性，满足机械施工的要求，提高工质量和效率；也能提高砂浆的韧性和抗裂性，有效解决砂浆易开裂的质量通病。
为了解决背景技术所存在的问题，本发明是采用以下技术方案：它的配方组成为：高分子助剂1-2份，纤维素醚类增稠剂1-4份，改性多元醇减缩剂1-5份，聚羧酸类减水剂2-6份，聚丙烯纤维25-50份，木质纤维10-20份、矿渣150-250份、钠基膨润土280-340份、其余用粉煤灰补足；它的制备工艺为：将上述配方材料均匀混合而成。
本发明具有以下有益效果：能有效改善砂浆操作性、和易性、粘聚性，防止砂浆泌水、离析、沉降，提供优良的稳定性和耐久性，适应工业化生产和施工的可泵性等要求，满足机械施工的要求，提高工质量和效率；能有效解决以石灰岩机制砂配制干混抹灰砂浆易开裂的质量问题，提高砂浆的韧性和抗裂性；降低砂浆生产材料成本，扩大砂浆原材料选择范围。
具体实施方式：
具体实施方式一：本具体实施方式采用以下技术方案：它的配方组成为：高分子助剂1份，纤维素醚类增稠剂1份，改性多元醇减缩剂1份，聚羧酸类减水剂2份，聚丙烯纤维25份，木质纤维10份、矿渣150份、钠基膨润土280份、其余用粉煤灰补足；它的制备工艺为：将上述配方材料均匀混合而成。
具体实施方式二：本具体实施方式与具体实施方式一不同之处在于它的配方组成为：高分子助剂1.5份，纤维素醚类增稠剂2份，改性多元醇减缩剂3份，聚羧酸类减水剂4份，聚丙烯纤维35份，木质纤维15份、矿渣200份、钠基膨润土300份、其余用粉煤灰补足；其制备工艺与具体实施方式一相同。
具体实施方式三：本具体实施方式与具体实施方式一不同之处在于它的配方组成为：高分子助剂2份，纤维素醚类增稠剂4份，改性多元醇减缩剂5份，聚羧酸类减水剂6份，聚丙烯纤维50份，木质纤维20份、矿渣250份、钠基膨润土340份、其余用粉煤灰补足；其制备工艺与具体实施方式一相同。
Claims (4)
1.石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉，其特征在于它的配方组成为：高分子助剂1-2份，纤维素醚类增稠剂1-4份，改性多元醇减缩剂1-5份，聚羧酸类减水剂2-6份，聚丙烯纤维25-50份，木质纤维10-20份、矿渣150-250份、钠基膨润土280-340份、其余用粉煤灰补足；它的制备工艺为：将上述配方材料均匀混合而成。
2.根据权利要求1所述的石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉，其特征在于它的配方组成为：高分子助剂1份，纤维素醚类增稠剂1份，改性多元醇减缩剂1份，聚羧酸类减水剂2份，聚丙烯纤维25份，木质纤维10份、矿渣150份、钠基膨润土280份、其余用粉煤灰补足。
3.根据权利要求1所述的石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉，其特征在于它的配方组成为：高分子助剂1.5份，纤维素醚类增稠剂2份，改性多元醇减缩剂3份，聚羧酸类减水剂4份，聚丙烯纤维35份，木质纤维15份、矿渣200份、钠基膨润土300份、其余用粉煤灰补足。
4.根据权利要求1所述的石灰岩机制砂专用干混抹灰砂浆抗裂增稠粉，其特征在于它的配方组成为：高分子助剂2份，纤维素醚类增稠剂4份，改性多元醇减缩剂5份，聚羧酸类减水剂6份，聚丙烯纤维50份，木质纤维20份、矿渣250份、钠基膨润土340份、其余用粉煤灰补足。