CN103449730A - 用于观光电梯的隔热玻璃及其制备方法 - Google Patents

用于观光电梯的隔热玻璃及其制备方法 Download PDF

Info

Publication number
CN103449730A
CN103449730A CN2013103694594A CN201310369459A CN103449730A CN 103449730 A CN103449730 A CN 103449730A CN 2013103694594 A CN2013103694594 A CN 2013103694594A CN 201310369459 A CN201310369459 A CN 201310369459A CN 103449730 A CN103449730 A CN 103449730A
Authority
CN
China
Prior art keywords
parts
heat
glass
glass melt
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103694594A
Other languages
English (en)
Other versions
CN103449730B (zh
Inventor
平利中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU JINGYI PACKING Co.,Ltd.
Original Assignee
Wujiang Junda Elevator Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wujiang Junda Elevator Parts Co Ltd filed Critical Wujiang Junda Elevator Parts Co Ltd
Priority to CN201310369459.4A priority Critical patent/CN103449730B/zh
Publication of CN103449730A publication Critical patent/CN103449730A/zh
Application granted granted Critical
Publication of CN103449730B publication Critical patent/CN103449730B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于观光电梯的隔热玻璃及其制备方法，包括以下重量份计的原料：硬脂酸镁20-30份、甘油30-35份、硒1-2份、三磷酸钠10-20份、聚乙烯醇20-30份、二氧化硅10-20份、硅酸钠15-20份、氯化钙2-10份、硼酸2-8份、聚甲基丙烯酸甲酯10-20份。将硬脂酸镁、甘油、硒、三磷酸钠、聚乙烯醇、二氧化硅、硅酸钠、氯化钙、硼酸、聚甲基丙烯酸甲酯混合后熔化，得玻璃熔体；将玻璃熔体倒入模具上，退火，热处理，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置。本发明具有很好的隔热性能，能够很好的隔绝外部温度变化对电梯内部温度的影响。

Description

用于观光电梯的隔热玻璃及其制备方法
技术领域
    本发明涉及玻璃领域，尤其涉及用于观光电梯的隔热玻璃及其制备方法。
背景技术
    观光电梯一般用于景点地区，比如高处的景点需要用到此类电梯，接送游客参观景点，所以观光电梯采用透明装置，使人们看到电梯外的美景，一般均采用玻璃，但是玻璃的隔热效果不好，天气如果太热，电梯内部的温度很快上升，造成人们的不舒适。
发明内容
    针对现有技术的不足，本发明提供了一种用于观光电梯的隔热玻璃及其制备方法，具有隔热效果，保持电梯内部温度的一致，不至于忽冷忽热，对人体健康不利。
    用于观光电梯的隔热玻璃，包括以下重量份计的原料：硬脂酸镁20-30份、甘油30-35份、硒1-2份、三磷酸钠10-20份、聚乙烯醇20-30份、二氧化硅10-20份、硅酸钠15-20份、氯化钙2-10份、硼酸2-8份、聚甲基丙烯酸甲酯10-20份。
用于观光电梯的隔热玻璃的制备方法，包括以下步骤：将硬脂酸镁、甘油、硒、三磷酸钠、聚乙烯醇、二氧化硅、硅酸钠、氯化钙、硼酸、聚甲基丙烯酸甲酯混合后熔化，熔化温度为2000-2200℃，保温1-2 小时，得玻璃熔体；将玻璃熔体倒入模具上，将模具放入退火炉中进行退火，进行热处理10-13h，热处理温度180-220℃ ；将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置，即可。
本发明的玻璃与空白玻璃相比，黑板温差在23-25℃，因此具有良好的隔热性能，能够很好的隔绝外部温度变化对电梯内部温度的影响。而且经测试，本发明比普通玻璃的太阳光反射率提高73-78%，红外反射率提高80-87%，本发明具有很好的隔热性能。
具体实施方式
下面通过具体实施例对本发明作进一步详细介绍。
实施例1
    用于观光电梯的隔热玻璃，包括以下重量份计的原料：硬脂酸镁20份、甘油30份、硒1份、三磷酸钠10份、聚乙烯醇20份、二氧化硅10份、硅酸钠15份、氯化钙2份、硼酸2份、聚甲基丙烯酸甲酯10份。
其制备方法包括以下步骤：将硬脂酸镁、甘油、硒、三磷酸钠、聚乙烯醇、二氧化硅、硅酸钠、氯化钙、硼酸、聚甲基丙烯酸甲酯混合后熔化，熔化温度为2000℃，保温1小时，得玻璃熔体；将玻璃熔体倒入模具上，将模具放入退火炉中进行退火，进行热处理10h，热处理温度180℃ ；将热处理好的玻璃熔体放入冷柜内，急剧降温至35℃，从冷柜内取出玻璃熔体，静置，即可。
实施例2
    用于观光电梯的隔热玻璃，包括以下重量份计的原料：硬脂酸镁30份、甘油35份、硒2份、三磷酸钠20份、聚乙烯醇30份、二氧化硅20份、硅酸钠20份、氯化钙10份、硼酸8份、聚甲基丙烯酸甲酯20份。
其制备方法包括以下步骤：将硬脂酸镁、甘油、硒、三磷酸钠、聚乙烯醇、二氧化硅、硅酸钠、氯化钙、硼酸、聚甲基丙烯酸甲酯混合后熔化，熔化温度为2200℃，保温2 小时，得玻璃熔体；将玻璃熔体倒入模具上，将模具放入退火炉中进行退火，进行热处理13h，热处理温度220℃ ；将热处理好的玻璃熔体放入冷柜内，急剧降温至40℃，从冷柜内取出玻璃熔体，静置，即可。
实施例3
    用于观光电梯的隔热玻璃，包括以下重量份计的原料：硬脂酸镁25份、甘油33份、硒1.5份、三磷酸钠15份、聚乙烯醇25份、二氧化硅15份、硅酸钠18份、氯化钙8份、硼酸5份、聚甲基丙烯酸甲酯15份。
其制备方法包括以下步骤：将硬脂酸镁、甘油、硒、三磷酸钠、聚乙烯醇、二氧化硅、硅酸钠、氯化钙、硼酸、聚甲基丙烯酸甲酯混合后熔化，熔化温度为2100℃，保温1.5小时，得玻璃熔体；将玻璃熔体倒入模具上，将模具放入退火炉中进行退火，进行热处理12h，热处理温度200℃ ；将热处理好的玻璃熔体放入冷柜内，急剧降温至38℃，从冷柜内取出玻璃熔体，静置，即可。
隔热性能参照 GB/T 24480-2009 检测。
  实施例1 实施例2 实施例3
隔热性能（与空白玻璃相比，黑板温差） 23℃ 25℃ 24℃
另外，本发明不限于上述实施方式，只要在不超出本发明的范围内，可以采取各种方式实施本发明。

Claims (2)

1. 用于观光电梯的隔热玻璃，其特征在于包括以下重量份计的原料：硬脂酸镁20-30份、甘油30-35份、硒1-2份、三磷酸钠10-20份、聚乙烯醇20-30份、二氧化硅10-20份、硅酸钠15-20份、氯化钙2-10份、硼酸2-8份、聚甲基丙烯酸甲酯10-20份。
2. 基于权利要求1所述的用于观光电梯的隔热玻璃的制备方法，其特征在于包括以下步骤：将硬脂酸镁、甘油、硒、三磷酸钠、聚乙烯醇、二氧化硅、硅酸钠、氯化钙、硼酸、聚甲基丙烯酸甲酯混合后熔化，熔化温度为2000-2200℃，保温1-2 小时，得玻璃熔体；将玻璃熔体倒入模具上，将模具放入退火炉中进行退火，进行热处理10-13h，热处理温度180-220℃ ；将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置，即可。
CN201310369459.4A 2013-08-22 2013-08-22 用于观光电梯的隔热玻璃及其制备方法 Active CN103449730B (zh)