CN103446619A - 新型可吸收止血材料 - Google Patents
新型可吸收止血材料 Download PDFInfo
- Publication number
- CN103446619A CN103446619A CN201310359740XA CN201310359740A CN103446619A CN 103446619 A CN103446619 A CN 103446619A CN 201310359740X A CN201310359740X A CN 201310359740XA CN 201310359740 A CN201310359740 A CN 201310359740A CN 103446619 A CN103446619 A CN 103446619A
- Authority
- CN
- China
- Prior art keywords
- hemostatic
- guluronic acid
- novel absorbable
- hemostatic material
- absorbable hemostatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种制备方法简单、成本低廉、止血效果较好的新型可吸收止血材料。目前国内的医用止血材料多为水溶性止血纱布,但是纱布止血没有消炎抗菌的作用,而且存在止血速度慢,体内吸收时间长,容易引起炎性反应等缺陷,因此人们把目光投向了止血粉,然而由于现有止血粉制备复杂、价格昂贵、止血效果不理想等原因,并未能被应用为主流止血产品应用。本新型可吸收止血材料为古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油经络合反应或交联反应所生成的古罗糖醛酸聚合物。本发明止血效果较好,具有止血速度快、体内吸收时间短、广谱杀菌消炎,促进伤口愈合等优点、另外其还不受创面大小和部位的影响,广泛适用于战伤、创伤等状况的快速止血。
Description
技术领域
本发明涉及医药技术领域,特别涉及一种制备方法简单、成本造价低廉、止血效果较好的新型可吸收止血材料。
背景技术
出血是战伤中第一位的死亡原因,是创伤中第二位的死亡原因,出血还是创伤病人手术室死亡的主要原因,快速、有效地控制出血可明显减少因出血导致的死亡。目前国内的医用止血材料多为水溶性止血纱布,但是纱布止血没有消炎抗菌的作用,而且存在止血速度慢,体内吸收时间长,容易引起炎性反应等缺陷,因此人们把目光投向了另一种止血材料—止血粉,然而由于现有止血粉制备复杂、价格昂贵、止血效果不理想等原因,并未能被应用为主流止血产品应用。
发明内容
本发明要解决的技术问题是如何克服现有技术的上述缺陷,提供一种新型可吸收止血材料。
为解决上述技术问题,本新型可吸收止血材料为古罗糖醛酸单体经络合反应或交联反应所生成的古罗糖醛酸聚合物,并添加薰衣草精油和丁香精油。
作为优化,所述古罗糖醛酸聚合物宏观呈粉末状,其微观结构单位为多孔微粒。
作为优化,所述多孔微粒直径为500~1000nm,每个多孔微粒上形成100~150个孔。
作为优化,所述古罗糖醛酸聚合物宏观呈粉末状,其微观结构单位为多孔薄膜。
作为优化,所述多孔薄膜厚度为500~1000nm,每张多孔薄膜上形成100~150个孔。
作为优化,所述古罗糖醛酸单体提取自海藻植物。
作为优化,所述海藻植物为褐藻中的海带。
作为优化,所述古罗糖醛酸单体的制备方法为酸法降解。
作为优化,所述古洛糖醛酸聚合物的制备方法为以罗糖醛酸单体为材料、氧化二异丙苯为交联剂,在温度30℃、常压条件下,将古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油在恒温反应釜中交联6小时即得。
作为优化,所述古洛糖醛酸聚合物的制备方法为以三乙醇胺为络合剂,温度30℃、1.5个大气压下,将古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油于恒压反应釜中络合6小时即得。
本发明新型可吸收止血材料制备方法简单、生产成本低廉、止血效果较好,具有止血速度快、体内吸收时间短、广谱杀菌消炎,促进伤口愈合等优点、另外其还不受创面大小和部位的影响,广泛适用于战伤、创伤等状况的快速止血。
具体实施方式
实施例1:本新型可吸收止血材料为古罗糖醛酸单体经络合反应或交联反应所生成的古罗糖醛酸聚合物。所述古罗糖醛酸聚合物宏观呈粉末状,其微观结构单位为多孔微粒。所述多孔微粒直径为500~1000nm,每个多孔微粒上形成100~150个孔。所述古罗糖醛酸单体提取自海藻植物。所述海藻植物为褐藻中的海带。所述古罗糖醛酸单体的制备方法为酸法降解。所述古洛糖醛酸聚合物的制备方法为以罗糖醛酸单体为材料、氧化二异丙苯为交联剂,在温度30℃、常压条件下,将古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油在恒温反应釜中交联6小时即得。
实施例2:本新型可吸收止血材料为古罗糖醛酸单体经络合反应或交联反应所生成的古罗糖醛酸聚合物。所述古罗糖醛酸聚合物宏观呈粉末状,其微观结构单位为多孔薄膜。所述多孔薄膜厚度为500~1000nm,每张多孔薄膜上形成100~150个孔。每个多孔微粒上形成100~150个孔。所述古罗糖醛酸单体提取自海藻植物。所述海藻植物为褐藻中的海带。所述古罗糖醛酸单体的制备方法为酸法降解。所述古洛糖醛酸聚合物的制备方法为以罗糖醛酸单体为材料、氧化二异丙苯为交联剂,在温度30℃、常压条件下,将古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油在恒温反应釜中交联6小时即得。
上述实施方式旨在举例说明本发明可为本领域专业技术人员实现或使用,对上述实施方式进行修改对本领域的专业技术人员来说将是显而易见的,故本发明包括但不限于上述实施方式,任何符合本权利要求书或说明书描述,符合与本文所公开的原理和新颖性、创造性特点的方法、工艺、产品,均落入本发明的保护范围之内。
Claims (10)
1.一种新型可吸收止血材料,其特征是:本材料为古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油经络合反应或交联反应所生成的古罗糖醛酸聚合物。
2.根据权利要求1所述的新型可吸收止血材料,其特征是:所述古罗糖醛酸聚合物宏观呈粉末状,其微观结构单位为多孔微粒。
3.根据权利要求2所述的新型可吸收止血材料,其特征是:所述多孔微粒直径为500~1000nm,每个多孔微粒上形成100~150个孔。
4.根据权利要求1所述的新型可吸收止血材料,其特征是:所述古罗糖醛酸聚合物宏观呈粉末状,其微观结构单位为多孔薄膜。
5.根据权利要求4所述的新型可吸收止血材料,其特征是:所述多孔薄膜厚度为500~1000nm,每张多孔薄膜上形成100~150个孔。
6.根据权利要求1所述的新型可吸收止血材料,其特征是:所述古罗糖醛酸单体提取自海藻植物。
7.根据权利要求6所述的新型可吸收止血材料,其特征是:所述海藻植物为褐藻中的海带。
8.根据权利要求6或者7所述的新型可吸收止血材料,其特征是:所述古罗糖醛酸单体的制备方法为酸法降解。
9.根据权利要求1-7任一所述的新型可吸收止血材料,其特征是:所述古洛糖醛酸聚合物的制备方法为以罗糖醛酸单体为材料、氧化二异丙苯为交联剂,在温度30℃、1.5个大气压下,将古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油于恒压反应釜中交联6小时即得。
10.根据权利要求1-7任一所述的新型可吸收止血材料,其特征是:所述古洛糖醛酸聚合物的制备方法为以三乙醇胺为络合剂,温度30℃、1.5个大气压下,将古罗糖醛酸单体、聚乙烯醇、薰衣草精油和丁香精油于恒压反应釜中络合6小时即得。