CN103436105A - 一种多彩橘红涂料的配方 - Google Patents
一种多彩橘红涂料的配方 Download PDFInfo
- Publication number
- CN103436105A CN103436105A CN2013102810189A CN201310281018A CN103436105A CN 103436105 A CN103436105 A CN 103436105A CN 2013102810189 A CN2013102810189 A CN 2013102810189A CN 201310281018 A CN201310281018 A CN 201310281018A CN 103436105 A CN103436105 A CN 103436105A
- Authority
- CN
- China
- Prior art keywords
- yellow
- red
- coating
- pearlescence
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种多彩橘红涂料的配方,各组分的质量百分比为:黄珠光粉0.4~0.8%,硝化棉35~45%,稀料15~20%,二丁酯2~4%,钼铬红12~17%,2029红0.6~1.2%,有机中黄0.5~1%,466助剂0.05~0.15%,树脂18~22%。本发明采用两种颜料的混合,并掺杂有黄珠光粉,通过一次喷涂,可得到豪华美观多彩的图案,且因珠光粉的加入而使外观形成为凹凸不平,并能发生色散而获得多种颜色花纹、立体感强、光泽优雅、外观质感较好。且整个涂料具有耐酸碱、耐水洗、耐污染、耐磨、粘结强度高等特性,可涂于灰泥、水泥、石棉、砖、木、金属的表面。
Description
技术领域
本发明涉及一种多彩橘红涂料,特别是涉及一种多彩橘红涂料的配方及制备方法。
背景技术
近几年,随着涂料技术的不断发展和新兴建筑节能市场的不断扩大,建筑涂料的应用日益普及和推广。但这些涂料大多以普通乳胶漆、弹性乳胶漆、质感涂料等一次施工只能形成单一色彩的图层为主,对于公共建筑和高档居住建筑,外立面要求多彩效果的,普通涂料又很难实现。采用多次喷涂实现多彩效果,颜色色相越多,施工技术难度越大,施工质量较难控制。因此,能一次喷涂形成多种色相相互交错的多彩涂料技术成为了行业的热点。
发明内容
本发明的目的是提供一种多彩橘红涂料配方解决目前涂料中大多以普通乳胶漆、弹性乳胶漆、质感涂料等一次施工只能形成单一色彩的图层为主,对于公共建筑和高档居住建筑,外立面要求多彩效果的,普通涂料又很难实现。采用多次喷涂实现多彩效果,颜色色相越多,施工技术难度越大,施工质量较难控制的问题。
本发明的技术解决方案是:本发明公开了一种多彩橘红涂料的配方,采用两种颜色的颜料,钼铬红和有机中黄,成为橘红色,又掺杂进黄色珠光粉,使得上料之后整体效果显得凹凸不平,各组分的质量百分比为:
黄珠光粉 0.4~0.8%
硝化棉 35~45%
稀料 15~20%
二丁酯 2~4%
钼铬红 12~17%
2029红 0.6~1.2%
有机中黄 0.5~1%
466助剂 0.05~0.15%
树脂 18~22%
进一步的改进在于:由以下具体质量百分比的成份组成:
黄珠光粉 0.52%
硝化棉 41.58%
稀料 17.67%
二丁酯 2.81%
钼铬红 14.97%
2029红 0.94%
有机中黄 0.62%
466助剂 0.10%
树脂 20.79%
一种根据上述配方来制备多彩橘红涂料的方法,具体步骤如下:
步骤一:将硝化棉、二丁酯、树脂加入搅拌釜,控制搅拌釜温度为30~40℃,搅拌30~40分钟,得到混合溶液;
步骤二:将钼铬红、2029红、有机中黄颜料添加到步骤一所得的混合溶液中,并用搅拌釜再次搅拌30~40分钟,使其搅拌均匀;
步骤三:将黄珠光粉加入搅拌釜进行搅拌;
步骤四:出釜于高速分散机中,于30~40℃进行强力搅拌,使珠光粉达到涂料所需粒度和浓度;
步骤五:边搅拌,边缓慢加入466助剂;
步骤六:边搅拌,边缓慢加入稀料,使得涂料达到所需粘度;
步骤七:出料分装,测固含量、附着力、柔韧性等物理机械性能,各项指标合格后包装入库。
本发明的有益效果:本发明采用两种颜料的混合,并掺杂有黄珠光粉,通过一次喷涂,可得到豪华美观多彩的图案,且因珠光粉的加入而使外观形成为凹凸不平,并能发生色散而获得多种颜色花纹、立体感强、光泽优雅、外观质感较好。且整个涂料具有耐酸碱、耐水洗、耐污染、耐磨、粘结强度高等特性,可涂于灰泥、水泥、石棉、砖、木、金属的表面。对宾馆、影院、文化娱乐场所、商店、写字楼等都能起到美化的作用。
具体实施方式
为了加深本发明的理解,下面将结合实施例对本发明做进一步详细描述,该实施例仅用于解释本发明,并不对的保护范围构成限定。
实施例1:
本实施例提供一种多彩橘红涂料的配方,由以下质量百分比的成份组成:
黄珠光粉 0.4%
硝化棉 42.35%
稀料 20%
二丁酯 2%
钼铬红 12%
2029红 0.6%
有机中黄 0.5%
466助剂 0.15%
树脂 22%
根据上述配方来制备多彩橘红涂料,具体步骤如下:
步骤一:将硝化棉、二丁酯、树脂加入搅拌釜,控制搅拌釜温度为30~40℃,搅拌30~40分钟,得到混合溶液;
步骤二:将钼铬红、2029红、有机中黄颜料添加到步骤一所得的混合溶液中,并用搅拌釜再次搅拌30~40分钟,使其搅拌均匀;
步骤三:将黄珠光粉加入搅拌釜进行搅拌;
步骤四:出釜于高速分散机中,于30~40℃进行强力搅拌,使珠光粉达到涂料所需粒度和浓度;
步骤五:边搅拌,边缓慢加入466助剂;
步骤六:边搅拌,边缓慢加入稀料,使得涂料达到所需粘度;
步骤七:出料分装,测固含量、附着力、柔韧性等物理机械性能,各项指标合格后包装入库。
本实施例的有益效果:本实施例采用两种颜料的混合,并掺杂有黄珠光粉,通过一次喷涂,可得到豪华美观多彩的图案,且因珠光粉的加入而使外观形成为凹凸不平,并能发生色散而获得多种颜色花纹、立体感强、光泽优雅、外观质感较好。且整个涂料具有耐酸碱、耐水洗、耐污染、耐磨、粘结强度高等特性,可涂于灰泥、水泥、石棉、砖、木、金属的表面。对宾馆、影院、文化娱乐场所、商店、写字楼等都能起到美化的作用。
实施例2:
本实施例提供一种多彩橘红涂料的配方,与实施例1的不同仅在于:所述配方组份的质量含量稍有不同:
黄珠光粉 0.8%
硝化棉 35%
稀料 18.95%
二丁酯 4%
钼铬红 17%
2029红 1.2%
有机中黄 1%
466助剂 0.05%
树脂 22%。
实施例3:
本实施例提供一种多彩橘红涂料的配方,与实施例1的不同仅在于:所述配方组份的质量含量稍有不同,也是最优选择:
黄珠光粉 0.52%
硝化棉 41.58%
稀料 17.67%
二丁酯 2.81%
钼铬红 14.97%
2029红 0.94%
有机中黄 0.62%
466助剂 0.10%
树脂 20.79%
实施例1-3仅用于解释本发明,其中实施例3作为最优配方选择,并不对本发明的保护范围构成限定。
Claims (3)
1.一种多彩橘红涂料,其特征在于:包括黄珠光粉、硝化棉、稀料、二丁酯、钼铬红、2029红、有机中黄、466助剂、树脂,其中,各组分的质量百分比为:
黄珠光粉 0.4~0.8%
硝化棉 35~45%
稀料 15~20%
二丁酯 2~4%
钼铬红 12~17%
2029红 0.6~1.2%
有机中黄 0.5~1%
466助剂 0.05~0.15%
树脂 18~22%。
2.据权利要求1所述的多彩橘红涂料的配方,其特征在于:各组分的具体质量百分比为:
黄珠光粉 0.52%
硝化棉 41.58%
稀料 17.67%
二丁酯 2.81%
钼铬红 14.97%
2029红 0.94%
有机中黄 0.62%
466助剂 0.10%
树脂 20.79%。
3.根据权利要求1所述的多彩橘红涂料的配方,其特征在于:具体步骤如下:
步骤一:将硝化棉、二丁酯、树脂加入搅拌釜,控制搅拌釜温度为30~40℃,搅拌30~40分钟,得到混合溶液;
步骤二:将钼铬红、2029红、有机中黄颜料添加到步骤一所得的混合溶液中,并用搅拌釜再次搅拌30~40分钟,使其搅拌均匀;
步骤三:将黄珠光粉加入搅拌釜进行搅拌;
步骤四:出釜于高速分散机中,于30~40℃进行强力搅拌,使珠光粉达到涂料所需粒度和浓度;
步骤五:边搅拌,边缓慢加入466助剂;
步骤六:边搅拌,边缓慢加入稀料,使得涂料达到所需粘度;
步骤七:出料分装,测固含量、附着力、柔韧性等物理机械性能,各项指标合格后包装入库。