CN103409097A - 一种装饰板用粘结剂的加工工艺 - Google Patents
一种装饰板用粘结剂的加工工艺 Download PDFInfo
- Publication number
- CN103409097A CN103409097A CN2013102019830A CN201310201983A CN103409097A CN 103409097 A CN103409097 A CN 103409097A CN 2013102019830 A CN2013102019830 A CN 2013102019830A CN 201310201983 A CN201310201983 A CN 201310201983A CN 103409097 A CN103409097 A CN 103409097A
- Authority
- CN
- China
- Prior art keywords
- polyethylene oxide
- binding agent
- nano
- decorative sheet
- decorative sheets
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种装饰板用粘结剂的加工工艺，包括以下步骤：(a)将纳米粒子与聚环氧乙烷按质量比为1∶20-200分散于水中，超生使其分散均匀；(b)在50-80℃下加热逐渐蒸发掉水分。该方法简单、易于操作、适合工业化生产，使用该方法生产的聚环氧乙烷粘结剂固化后其粘结剂涂层强度和耐磨性能得以提高。
Description
技术领域
本发明涉及一种装饰板用粘结剂的加工工艺。
背景技术
粘结剂是磨料和基体之间粘结强度的保证。随着化工工业的发展，各种新型粘结剂进入了涂附磨具领域，提高了涂附磨具的性能，促进了涂附磨具工业的发展。粘结剂除了胶料外，还包括溶剂、固化剂、增韧剂、防腐剂、着色剂、消泡剂等辅助成分。粘结剂除了最常用的动物胶外，还包括合成树脂、橡胶和油漆。
环氧粘结剂是装饰板中常用的粘结剂之一，它在固化后存在应力大、质脆、耐疲劳性/耐冲击性差等缺点，因而环氧粘结剂的增韧改性一直是国内外研究的热点。
发明内容
本发明目的是为了克服现有技术的不足而提供一种装饰板用粘结剂的加工工艺。
为达到上述目的，本发明采用的技术方案是：一种装饰板用粘结剂的加工工艺，包括以下步骤：(a)将纳米粒子与聚环氧乙烷按质量比为1∶20-200分散于水中，超生使其分散均匀；(b)在50-80℃下加热逐渐蒸发掉水分。
优化地，所述的聚环氧乙烷分子量为1万-50万。
优化地，所述的纳米粒子为纳米氧化钙、纳米二氧化硅、纳米有机蒙脱土、纳米粉煤灰、纳米二氧化钛中的一种。
由于上述技术方案运用，本发明与现有技术相比具有下列优点：
(1)、该方法简单、易于操作、适合工业化生产；
(2)、使用该方法生产的聚环氧乙烷粘结剂固化后其粘结剂涂层强度和耐磨性能得以提高。
具体实施方式
下面将对本发明优选实施方案进行详细说明：
实施例1
本例提供一种装饰板用粘结剂的加工工艺，其具体步骤如下：
(a)取1g纳米SiO2，20g分子量为1万的聚环氧乙烷分散于水中，超生使其分散均匀；
(b)在50℃下加热，使该溶液水分缓慢蒸发。
实施例2
本例提供一种装饰板用粘结剂的加工工艺，其具体步骤如下：
(a)取1g纳米CaO，200g分子量为50万的聚环氧乙烷分散于水中，超生使其分散均匀；
(b)在80℃下加热，使该溶液水分缓慢蒸发。
实施例3
本例提供一种装饰板用粘结剂的加工工艺，其具体步骤如下：
(a)取1g纳米纳米有机蒙脱土，200g分子量为50万的聚环氧乙烷分散于水中，超生使其分散均匀；
(b)在80℃下加热，使该溶液水分缓慢蒸发。
实施例4
本例提供一种装饰板用粘结剂的加工工艺，其具体步骤如下：
(a)取1g纳米纳米粉煤灰，200g分子量为50万的聚环氧乙烷分散于水中，超生使其分散均匀；
(b)在80℃下加热，使该溶液水分缓慢蒸发。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围，凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。
Claims (3)
1.一种装饰板用粘结剂的加工工艺，包括以下步骤：
(a)将纳米粒子与聚环氧乙烷按质量比为1∶20-200分散于水中，超生使其分散均匀；
(b)在50-80℃下加热逐渐蒸发掉水分。
2.根据权利要求1所述的装饰板用粘结剂的制作方法，其特征在于：所述的聚环氧乙烷分子量为1万-50万。
3.根据权利要求1所述的装饰板用粘结剂的制作方法，其特征在于：所述的纳米粒子为纳米氧化钙、纳米二氧化硅、纳米有机蒙脱土、纳米粉煤灰、纳米二氧化钛中的一种。