CN103406352A - 一种镍基合金Ni36板的加热和轧制方法 - Google Patents

一种镍基合金Ni36板的加热和轧制方法 Download PDF

Info

Publication number
CN103406352A
CN103406352A CN2013103474522A CN201310347452A CN103406352A CN 103406352 A CN103406352 A CN 103406352A CN 2013103474522 A CN2013103474522 A CN 2013103474522A CN 201310347452 A CN201310347452 A CN 201310347452A CN 103406352 A CN103406352 A CN 103406352A
Authority
CN
China
Prior art keywords
rolling
heating
pass
passage
base alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103474522A
Other languages
English (en)
Other versions
CN103406352B (zh
Inventor
张宝连
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Taigang Stainless Steel Co Ltd
Original Assignee
Shanxi Taigang Stainless Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Taigang Stainless Steel Co Ltd filed Critical Shanxi Taigang Stainless Steel Co Ltd
Priority to CN201310347452.2A priority Critical patent/CN103406352B/zh
Publication of CN103406352A publication Critical patent/CN103406352A/zh
Application granted granted Critical
Publication of CN103406352B publication Critical patent/CN103406352B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种镍基合金Ni36板的加热和轧制方法,属于冶金领域,先电炉加热后再在煤气加热炉加热,电炉加热为钢坯装炉后,以50~80℃/h的加热速度加热,升温至500℃保温2小时出炉;所述煤气加热炉加热为:将温度不低于350℃的钢坯进入煤气加热炉加热,其预热段温度≤900℃,预热段时间为1h,进入加热段和均热段,加热段和均热段的温度控制在1130~1150℃,加热段和均热段的时间为1.5~2h。轧制工序的前三道次的压下量分别是10-12mm、15-17mm、20-22mm。本发明解决了镍基合金Ni36钢板表面轧制裂纹的问题。

Description

一种镍基合金Ni36板的加热和轧制方法
技术领域
本发明属于冶金领域钢板轧制领域,具体涉及一种镍基合金Ni36(4J36)板的加热、轧制方法。 
背景技术: 
 镍基合金Ni36为低膨胀合金钢,加热、轧制是难点,目前该钢种全部依靠进口,轧制板材基本没有。因此,利用煤气炉、电炉结合加热坯料、及采用小道次轧制力,解决Ni36低膨胀合金钢的加热、轧制难度问题。
发明内容
实现镍基合金Ni36中厚板的轧制生产,打破镍基合金Ni36长期以来由国外垄断的局面,实现6-80mm镍基合金Ni36板材低成本生产,减少因表面加热、轧制裂纹造成的废品。 
本发明的技术方案是: 
本发明所述的镍基合金Ni36的化学成分是:C≤0.05,P≤0.02,S≤0.02,Si≤0.30,Mn为0.20~0.60,Ni为35.0~37.0,余量为Fe和不可避免的杂质;
(1)加热方法是:先电炉加热后再在煤气加热炉加热。即先把常温状态下的坯料放入电炉中,开始通电进行加热,升温速度按照≤80℃/h进行操作,待炉温升温至500℃后进行保温,坯料保温2小时后进行出炉,把出炉后的坯料装入煤气加热炉中进行加热,这期间吊运或运输的钢坯温度有所下降,但要保证电炉出炉后装入煤气炉的坯料温度不能低于350℃。目的就是解决该钢种表面氧化铁皮问题及因膨胀系数低、加热易出现裂纹的加热问题。
(2)轧制方法是:第一道次轧制压下量、第二道次轧制压下量、第三道次轧制压下量分别采用小压下量的轧制方式,这三个道次的总压下量之和不超过50mm,并且前三个道次压下量依次按照逐渐增大的趋势进行轧钢,即按照10-12mm、15-17mm、20-22mm的轧制压下量进行轧制,目的是解决轧制裂纹缺陷。 
具体加热步骤如下: 
1、电炉加热:冷钢(即钢坯的温度为室温)装炉后,开始缓慢加热,加热速度为50-80℃/h,升温至500℃保温2小时后,出炉操作。
2、钢坯于电炉出炉后,用吊具或运输辊道装入煤气炉,保证电炉出炉后装入煤气炉的坯料温度不能低于350℃。 
3、煤气加热炉加热:总加热时间控制在2.5-3h。 
(1) 预热段温度≤900℃,钢坯在预热段的时间控制在1h。 
(2)进入加热段和均热段,温度控制在1130-1150℃,总加热时间控制在1.5-2h。 
(3)炉内气氛要求弱氧化气氛控制,加热工做到“三掌握”,即“掌握钢坯在炉内的位置、时间,保证钢坯在加热段、均热段的时间在1.5-2h;掌握炉温控制在1130-1150℃(宁低勿高),掌握钢坯在炉内的运行情况,减少钢坯在烧嘴附近长时间停留。 
具体轧制步骤如下: 
(1)高压水除鳞:轧制前钢坯刚到水嘴下开始冲水,只冲一次水。
      (2)关掉或关小轧机工作辊辊身冷却水,前三道次压下量 
采用小压下量轧制,总压下量之和不超过50mm,即前三个道次压下量依次按照逐渐增大的趋势进行轧钢,即第一道次、第二道次、第三道次的轧制压下量分别是10~12mm、15~17mm、20~-22mm;从第四道次开始,逐渐增大道次压下量,直至完成所需厚度。
注:轧机一般是可逆轧机,以轧辊(轧机牌坊)为中心,分轧辊前和轧辊后两个方向,钢坯轧制从轧辊前到轧辊后为一个轧制道次,也是第一道次;其次钢坯轧制从轧辊后到轧辊前又是一个轧制道次,也称第二道次,依次类推,为第三道次、第四道次….。 
本发明解决了镍基合金Ni36钢坯煤气加热炉直接加热难的问题;采用前三道小压下量轧制,解决了钢板表面轧制裂纹,实现了镍基合金Ni36板材轧制生产,属国内首创;不需投入,效果好,实现了低成本、高利润生产。 
具体实施方式
本实施例在不锈热轧厂的加热、轧制生产。来料为4块钢坯坯料,4块钢坯坯料的冶炼和钢坯的浇注与现有的方法相同。 
镍基合金Ni36的化学成分是:C≤0.05,P≤0.02,S≤0.02,Si≤0.30,Mn为0.20~0.60,Ni为35.0~37.0,余量为Fe和不可避免的杂质。 
4块钢坯坯料规格:165 *1020*1900mm  分别轧制10*1800毛*6000mm上尺、20*1800毛*6000mm、40*1800毛*6000mm、上尺大板,加热和轧制方式如下: 
(一)电炉加热:(1)先把4块坯料165 *1020*1900mm 装入电炉,关闭炉门后,然后通电进行缓慢加热,加热速度为80℃/h,升温至500℃保温2小时,保温完成后,提前1小时通知调度,进行组织出炉操作。
(2)电炉出炉后,由炉前工组织,把钢吊运至炉后辊道上进行装炉,经测量钢坯装炉温度为450℃。 
(3)煤气加热炉加热:总加热时间控制在2.5h。 
① 预热段温度控制≤900℃,钢坯在预热段的时间控制在1h。 
②进入加热段和均热段,温度控制在1130-1150℃(宁低勿高),总加热时间控制在1.5h。 
③炉内气氛要求弱氧化气氛控制,炉气残氧含量控制在5%以下。 
(二)轧制
(1)高压水除鳞:轧制前冲一次水。
(2)二辊轧制: 
①轧制前检查辊面及风管,并关小上工作辊辊身冷却水。
②直接横轧,前三道次采用小压下量轧制,7道次完成二辊轧制,二辊送料厚度为55mm。具体压下分配如下: 
轧制道次 1 2 3 4 5 6 7
道次压下量 10 15 20 30 30 10 5
理论轧制厚度 165 150 130 100 70 60 55
③四辊轧制:厚度公差目标控制为(+0,+0.2mm),以成品厚度10mm为例,6道次完成。具体压下分配如下:
轧制道次 1 2 3 4 5 6
道次压下量 10 10 8 8 5 4
理论轧制厚度 45 35 27 19 14 10

Claims (2)

1.一种镍基合金Ni36板的加热和轧制方法,所述的镍基合金Ni36的化学成分是:C≤0.05,P≤0.02,S≤0.02,Si≤0.30,Mn为0.20~0.60,Ni为35.0~37.0,余量为Fe和不可避免的杂质;加热方法是先电炉加热后再在煤气加热炉加热,所述电炉加热为钢坯装炉后,以50~80℃/h的加热速度加热,升温至500℃保温2小时出炉;
所述煤气加热炉加热为:将温度不低于350℃的钢坯进入煤气加热炉加热,其预热段温度≤900℃,预热段时间为1h,进入加热段和均热段,加热段和均热段的温度控制在1130~1150℃,加热段和均热段的时间为1.5~2h;
轧制步骤:(1)采用高压水除鳞:轧制前钢坯刚到水嘴下开始冲水,只冲一次水;
      (2)关掉或关小轧机工作辊辊身冷却水,第一道次、第二道次、第三道次的轧制压下量分别是10~12mm、15~17mm、20~22mm,且第一道次、第二道次、第三道次的总压下量之和不超过50mm;从第四道次开始,逐渐增大道次压下量,直至完成所需厚度。
2.根据权利要求1所述的一种镍基合金Ni36板的加热和轧制方法,所述轧制步骤包括二辊轧制和四辊轧制,二辊轧制的产品厚度为55mm;轧制道次的轧制压下量是
轧制道次 1 2 3 4 5 6 7 道次压下量 10 15 20 30 30 10 5
四辊轧制的产品厚度为10mm;轧制道次的轧制压下量是
轧制道次 1 2 3 4 5 6 道次压下量 10 10 8 8 5 4
CN201310347452.2A 2013-08-12 2013-08-12 一种镍基合金Ni36板的加热和轧制方法 Active CN103406352B (zh)