CN103397222A - 不锈钢拉深模具铜合金及其制备方法 - Google Patents

不锈钢拉深模具铜合金及其制备方法 Download PDF

Info

Publication number
CN103397222A
CN103397222A CN2013102714783A CN201310271478A CN103397222A CN 103397222 A CN103397222 A CN 103397222A CN 2013102714783 A CN2013102714783 A CN 2013102714783A CN 201310271478 A CN201310271478 A CN 201310271478A CN 103397222 A CN103397222 A CN 103397222A
Authority
CN
China
Prior art keywords
stainless steel
copper alloy
hour
drawing mould
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102714783A
Other languages
English (en)
Inventor
何祥炎
黄先功
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Sanlian Pump Industry Co Ltd
Original Assignee
Anhui Sanlian Pump Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Sanlian Pump Industry Co Ltd filed Critical Anhui Sanlian Pump Industry Co Ltd
Priority to CN2013102714783A priority Critical patent/CN103397222A/zh
Publication of CN103397222A publication Critical patent/CN103397222A/zh
Pending legal-status Critical Current

Abstract

不锈钢拉深模具铜合金，其特征在于其中含有如下的重量百分数的化学成分：铝8-9、铁7-8、锰1-2、钴0.3-0.5、In1.2-1.5、As0.05-0.08、Hf0.18-0.22、Bi0.5-0.8、Ni1.1-1.3、W0.24-0.29、余量为铜。本发明摩擦系数低，导热性好，且由于铜和钢铁之间结构差异较大，避免了用钢铁模具拉伸时产生粘结瘤的现象，因此不需要抛光，使用周期长，主要用于制造不锈钢筒形件等的拉深模具。

Description

不锈钢拉深模具铜合金及其制备方法
技术领域
本发明属于合金冶炼技术，具体是一种铜合金及其制备方法。
背景技术
传统的拉深模具材料一般采用Cr12MoV，T10，35CrMo 等合金钢，这些材料作为不锈钢拉深模具时的致命缺点是容易形成粘结瘤，粘结瘤的成因为微观上板料与模具表面都是凹凸不平的粗键面，由于拉深过程中压边力较大，载荷由局部凸起部位承受单位压力很大；又因板料与模具间产生相对运动以及板料的塑性变形产生热能，使得润滑膜粘度下降，采用铜合金制作拉深模具存在强度不高的问题。
发明内容
本发明的目的是提供一种不锈钢拉深模具铜合金及其制备方法，具有较高的强度与导热性。
本发明技术方案如下：
不锈钢拉深模具铜合金，其特征在于其中含有如下的重量百分数的化学成分：铝8-9、铁7-8、锰1-2、钴0.3-0.5、In1.2-1.5、As0.05-0.08、Hf0.18-0.22、Bi0.5-0.8、Ni1.1-1.3、W0.24-0.29、余量为铜。
所述的不锈钢拉深模具铜合金的制备方法，其特征在于：在中频炉加入电解铜，加热至1090-1130℃，待铜料熔化后加入其它合金成分，升温至1150-1180℃，搅拌10-15分钟，扒渣；然后，加入精炼剂，搅拌15-20分钟，然后捞渣；降温至1080-1130℃，进行浇铸，浇铸后以180-210℃/小时速率降温至室温；然后，以130-150℃/小时速率升温至910-920℃，保温2-3小时；再以110-120℃/小时速率降温至260-280℃，保温1-2小时；以150-180℃/小时速率升温至510-520℃，保温2-3小时；再自然冷却至室温。
所述的不锈钢拉深模具铜合金的制备方法，其特征在于：所述的精炼剂由下列重量份原料混合压块而成：氟硅酸钠1-1.2、四硼酸钠2.3-2.6、凹凸棒土3-4、氟化铝钠2.3-.25、SnO21.1-1.3、Bi2O32.1-2.3、二硼化钒1.2-1.4、碳化铌2.0-2.2。
本发明摩擦系数低，导热性好，且由于铜和钢铁之间结构差异较大，避免了用钢铁模具拉伸时产生粘结瘤的现象，因此不需要抛光，使用周期长，主要用于制造不锈钢筒形件等的拉深模具。
具体实施方式
不锈钢拉深模具铜合金，其中含有如下的重量百分数的化学成分：铝8-9、铁7-8、锰1-2、钴0.3-0.5、In1.2-1.5、As0.05-0.08、Hf0.18-0.22、Bi0.5-0.8、Ni1.1-1.3、W0.24-0.29、余量为铜。
所述的不锈钢拉深模具铜合金的制备方法：在中频炉加入电解铜，加热至1090-1130℃，待铜料熔化后加入其它合金成分并检测，升温至1150-1180℃，搅拌10-15分钟，扒渣；然后，加入精炼剂，搅拌15-20分钟，然后捞渣；降温至1080-1130℃，进行浇铸，浇铸后以180-210℃/小时速率降温至室温；然后，以130-150℃/小时速率升温至910-920℃，保温2-3小时；再以110-120℃/小时速率降温至260-280℃，保温1-2小时；以150-180℃/小时速率升温至510-520℃，保温2-3小时；再自然冷却至室温。
精炼剂下列重量份（公斤）原料混合压块而成：氟硅酸钠1、四硼酸钠2.6、凹凸棒土3、氟化铝钠2.3、SnO21.1、Bi2O32.1、二硼化钒1.4、碳化铌2.0。
本发明铜合金机械性能：硬度为HRC36-47，抗拉强度为980 -1340MPa，屈服强度670-830MPa，热导率为34-42W/m.K，伸长率16-24%。

Claims (3)

1.不锈钢拉深模具铜合金，其特征在于其中含有如下的重量百分数的化学成分：铝8-9、铁7-8、锰1-2、钴0.3-0.5、In1.2-1.5、As0.05-0.08、Hf0.18-0.22、Bi0.5-0.8、Ni1.1-1.3、W0.24-0.29、余量为铜。
2.根据权利要求1所述的不锈钢拉深模具铜合金的制备方法，其特征在于：在中频炉加入电解铜，加热至1090-1130℃，待铜料熔化后加入其它合金成分，升温至1150-1180℃，搅拌10-15分钟，扒渣；然后，加入精炼剂，搅拌15-20分钟，然后捞渣；降温至1080-1130℃，进行浇铸，浇铸后以180-210℃/小时速率降温至室温；然后，以130-150℃/小时速率升温至910-920℃，保温2-3小时；再以110-120℃/小时速率降温至260-280℃，保温1-2小时；以150-180℃/小时速率升温至510-520℃，保温2-3小时；再自然冷却至室温。
3.根据权利要求2所述的不锈钢拉深模具铜合金的制备方法，其特征在于：所述的精炼剂由下列重量份原料混合压块而成：氟硅酸钠1-1.2、四硼酸钠2.3-2.6、凹凸棒土3-4、氟化铝钠2.3-.25、SnO21.1-1.3、Bi2O32.1-2.3、二硼化钒1.2-1.4、碳化铌2.0-2.2。
CN2013102714783A 2013-07-01 2013-07-01 不锈钢拉深模具铜合金及其制备方法 Pending CN103397222A (zh)