CN103396559B - 一种室温自干的多功能有机硅树脂及其制备方法 - Google Patents
一种室温自干的多功能有机硅树脂及其制备方法 Download PDFInfo
- Publication number
- CN103396559B CN103396559B CN201310320234.XA CN201310320234A CN103396559B CN 103396559 B CN103396559 B CN 103396559B CN 201310320234 A CN201310320234 A CN 201310320234A CN 103396559 B CN103396559 B CN 103396559B
- Authority
- CN
- China
- Prior art keywords
- dry
- room temperature
- resin
- multifuncitonal
- multifuncitonal organosilicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种室温自干的多功能有机硅树脂及其制备方法，室温自干的多功能有机硅树脂，对下列重量百分比组分的有机硅树脂进行改性：丙烯酸树脂30-50%；聚酯树脂5-20%;有机硅树脂10-30%；溶剂10-20%；催化剂2-4%；助剂？？1-2%；室温自干的多功能有机硅树脂制备方法，包括步骤：（1）在具有加热回流装置的反应釜中依次加入90-100份丙烯酸树？脂及40-50份聚酯树脂；（2）加入20-25份二甲苯，慢慢升温至110度；（3）滴加溶于二甲苯的浓度为50%的有机硅树脂溶液40-50份；（4）滴加3-5份钛酸正丁酯及1-2份氨基硅油；（5）保温若干小时。
Description
技术领域
本发明涉及有机硅树脂，具体涉及一种室温自干的多功能有机硅树脂及其制备方法。
背景技术
有机硅树脂用途广泛，市场迫切需要采用简便的方法合成的多功能有机硅改性树脂。
发明内容
本发明要解决的技术问题是提供一种室温自干的多功能有机硅树脂及其制备方法。
本发明为解决上述技术问题所采用的技术方案为：
对下列重量百分比组分的有机硅树脂进行改性：
根据本发明的实施例，所述溶剂设为二甲苯、丙二醇甲醚醋酸酯、环己酮或者醋酸丁酯。
根据本发明的实施例，所述催化剂设为钛酸正丁酯。
一种室温自干的多功能有机硅树脂制备方法，包括步骤：
(1)在具有加热回流装置的反应釜中依次加入90-100份羟基丙烯
酸树脂及40-50份饱和聚酯树脂；
(2)加入20-25份二甲苯，慢慢升温至110度；
(3)滴加溶于二甲苯的浓度为50％的含甲氧基及苯基硅树脂溶液40-50份；
(4)滴加3-5份钛酸正丁酯及1-2份氨基硅油；
(5)保温若干小时。
根据本发明的实施例，步骤(5)中保温时间为2小时。
根据本发明的实施例，还包括步骤：
(6)检测；
(7)降温；
(8)包装。
本发明的有益效果：本发明可用于玻璃、陶瓷、金属、塑料、石材、玻璃钢等材料上,具有防腐、防潮、酸碱、耐盐雾、耐温、绝缘、耐磨、耐溶剂等优点，可单独使用,也可与其他颜填料、助剂或树脂，如饱和聚酯树脂、醇酸树脂混用，制成油漆、油墨、胶粘剂。
具体实施方式
下面根据实施例对本发明作进一步详细说明:
本发明室温自干的多功能有机硅树脂，按重量百分比包括以下组分：
实施例1：
(1)在具有加热回流装置的反应釜中依次加入90公斤羟基丙烯酸
树脂及40公斤饱和聚酯树脂；
(2)加入20公斤二甲苯，慢慢升温至110度；
(3)滴加溶于二甲苯的浓度为50％的有机硅树脂溶液40公斤；
(4)滴加3公斤钛酸正丁酯及1公斤氨基硅油；
(5)保温2小时；
(6)检测；
(7)降温；
(8)包装。
实施例2:
(1)在具有加热回流装置的反应釜中依次加入100公斤羟基丙烯
酸树脂及50公斤饱和聚酯树脂；
(2)加入25公斤二甲苯，慢慢升温至110度；
(3)滴加溶于二甲苯的浓度为50％的有机硅树脂溶液50公斤；
(4)滴加5公斤钛酸正丁酯及2公斤氨基硅油；
(5)保温2小时；
(6)检测；
(7)降温；
(8)包装。
本领域技术人员不脱离本发明的实质和精神，可以有多种变形方案实现本发明，以上所述仅为本发明较佳可行的实施例而已，并非因此局限本发明的权利范围，凡运用本发明说明书及附图内容所作的等效结构变化，均包含于本发明的权利范围之内。
Claims (6)
1.一种室温自干的多功能有机硅树脂，其特征在于，对下列重量百分比组分的有机硅树脂进行改性：
羟基丙烯酸树脂30-50%
饱和聚酯树脂5-20%
含甲氧基及苯基硅树脂10-30%
溶剂10-20%
催化剂2-4%
氨基硅油1-2%
2.根据权利要求1所述的室温自干的多功能有机硅树脂，其特征在于：所述溶剂设为二甲苯、丙二醇甲醚醋酸酯、环己酮或者醋酸丁酯。
3.根据权利要求1所述的室温自干的多功能有机硅树脂，其特征在于：所述催化剂设为钛酸正丁酯。
4.一种室温自干的多功能有机硅树脂制备方法，其特征在于，包括步骤：
（1）在具有加热回流装置的反应釜中依次加入90-100份羟基丙烯酸树脂及40-50份饱和聚酯树脂；
（2）加入20-25份二甲苯，慢慢升温至110度；
（3）滴加溶于二甲苯的浓度为50%的含甲氧基及苯基硅树脂溶液40-50份；
（4）滴加3-5份钛酸正丁酯及1-2份氨基硅油；
（5）保温若干小时。
5.根据权利要求4所述的室温自干的多功能有机硅树脂制备方法，其特征在于，步骤（5）中保温时间为2小时。
6.根据权利要求5所述的室温自干的多功能有机硅树脂制备方法，其特征在于，还包括步骤：
（6）检测；
（7）降温；
（8）包装。